In this research tri metal oxides were fabricated by simple chemical spray pyrolysis technique from (Sn(NO₃)₂.20 H₂O, Zn(NO₃)₂.6 H₂O, Cd(NO₃)₂.4 H₂O) salts at concentration 0.1M with mixing weight ratio 50:50 were fabricated on silicon substrate n-type (111). (with & without the presence of grooves by the following diemensions (20μm width, 7.5μm depth) with thickness was about ( 0.1 ±0.05 µm) using water soluble as precursors at a substrate temperature 550 ºC±5, with spray distance (15 cm) and their gas sensing properties toward H₂S gas at different concentrations (10,50,100,500 ppmv) in air were investigated at room te

In this work, electrochemical process was presented to polymerized eugenol on Gr.2 and Gr.5 titanium alloys before and after treated by Micro Arc Oxidation (MAO), where Gr.2 is commercial pure titanium and Gr.5 is Ti-6Al-4V dental alloys. The deposited layers were characterized by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FTIR). The adhesion strength of polymeric thin-film was estimation by using pull-off adhesion test and the result was the adhesion strength of PE was (1.23 MPa) on Gr.2 before MAO and increase to (1.98 MPa) on Gr.2 after MAO treatment. The corrosion behavior of Gr.2 and Gr.5 alloy in artificial saliva environment at

The objective of this study was shed light for cultivation and maintenance of Trichomonas vaginalis parasite growth after isolated it by vaginal swaps from females suffering vaginitis and abnormal vaginal discharges in these media CPLM and TAB media to detect growth curve, morphological changes and viability of parasite in the two culture media, together with effect of sheep and bovine serum on the growth of it. The results of this studies were showed there was abtaine differences between the two types of media , The maximum growth of parasite was in TAB medium after 72 hours incubation with use of bovine serum, while such growth was maximized after 144 hours incubation with the use of sheep serum. In CPLM medium, a maximum gro

Background: Alveolar ridge expansion is proposed when the alveolar crest thickness is ≤5 mm. The screw expansion technique has been utilized for many years to expand narrow alveolar ridges. Recently, the osseodensification technique has been suggested as a reliable technique to expand narrow alveolar ridges with effective width gain and as little surgical operating time as possible. The current study aimed to compare osseodensification and screw expansion in terms of clinical width gain and operating time. Materials and methods: Forty implant osteotomies were performed in deficient horizontal alveolar ridges (3–5 mm). A total of 19 patients aged 21–59 years were randomized into two groups: the screw expansion group, which invo

SAPO-11 is synthesized from silicoaluminophosphate in the presence of di-n-propylamine as a template. The results show that the sample obtained has good crystallinity, 396m2/g BET surface area, and 0.35 cm3/g pore volume. The hydroisomerization activity of (0.25)Pt (1)Zr (0.5)W/SAPO-11 catalyst was determined using n-decane and base oil. All hydroisomerization experiments of n-decane were achieved at a fixed bed plug flow reactor at a temperature range of 200-275°C and  LHSV 0.5-2h-1.  The results show that the n-decane conversion increases with increasing temperature and decreasing LHSV, the maximum conversion of 66.7 % was achieved at temperature 275°C and LHSV of 0.5 h-1. Meanwhile, the same catalyst was used to improve base oil spec

   SAPO-11 is synthesized from silicoaluminophosphate in the presence of di-n-propylamine as a template. The results show that the sample obtained has good crystallinity, 396m²/g BET surface area, and 0.35 cm³/g pore volume. The hydroisomerization activity of (0.25)Pt (1)Zr (0.5)W/SAPO-11 catalyst was determined using n-decane and base oil. All hydroisomerization experiments of n-decane were achieved at a fixed bed plug flow reactor at a temperature range of 200-275°C and  LHSV 0.5-2h^-1.  The results show that the n-decane conversion increases with increasing temperature and decreasing LHSV, the maximum conversion of 66.7 % was achieved at temperature 275°C and LHSV of 0.5 h^-1

The complexes of the 2-hydroxy-4-Nitro phenyl piperonalidene with metal ions Cr(III), Ni(II), Pt(IV) and Zn(II) were prepared in ethanolic solution. These complexes were characterized by spectroscopic methods, conductivity, metal analyses and magnetic moment measurements. The nature of the complexes formed in ethanolic solution was study following the molar ratio method. From the spectral studies, monomer structures proposed for the nickel (II) and Zinc (II) complexes while dimeric structures for the chromium (III) and platinum (IV) were proposed. Octahedral geometry was suggested for all prepared complexes except zinc (II) has tetrahedral geometry, Structural geometries of these compounds were also suggested in gas phase by using

Background: The main objective was to compare the outcome of single layer interrupted extra-mucosal sutures with that of double layer suturing in the closure of colostomies.

Subjects and Methods: Sixty-seven patients with closure colostomy were assigned in a prospective randomized fashion into either single layer extra-mucosal anastomosis (Group A) or double layer anastomosis (Group B). Primary outcome measures included mean time taken for anastomosis, immediate postoperative complications, and mean duration of hospital stay. Secondary outcome measures assessed the postoperative return of bowel function, and the overall mean cost. Chi-square test and student t-test did the statistical analysis..

Resu