The main objectives of this study were investigating the effects of the maximum size of coarse Attapulgite aggregate and micro steel fiber content on fresh and some mechanical properties of steel fibers reinforced lightweight self-compacting concrete (SFLWSCC). Two series of mixes were used depending on maximum aggregate size (12.5 and 19) mm, for each series three different steel fibers content were used (0.5 %, 1%, and 1.5%). To evaluate the fresh properties, tests of slump flow, T500 mm, V funnel time, and J ring were carried out. Tests of compressive strength, splitting tensile strength, flexural tensile strength, and calculated equilibrium density were done to evaluate mechanical properties. For reference mixes, the

Objective: The aim of the research is to prepare skilled mental exercises according to spatial and temporal perceptions and the awareness of the strength of young pole-vaulters, and to recognize the impact of these exercises on improving the indicators of electrical activity of working muscles and some special physical abilities and accomplishing this effectiveness Research methodology: The researcher used the experimental curriculum (one experimental group), and included the sample of research on (5) two joint jumpers in the Iraqi club championship, all from the center of talent in athletics, the sample is trained on the same curriculum prepared by the coach himself but accompanied by a mental training approach that Prepared by the

This study is concerned with the comparison of the results of some tests of passing and dribbling of the basketball of tow different years between teams of chosen young players in Baghdad. Calculative methods were used namely (Arithmetic mean, Value digression and T.test for incompatible specimens). After careful calculative treatments, it has been that there were abstract or no abstract differences in the find results of chestpass, highdribble and cross-over dribble. The clubs were: (Al-Khark, Air defence, Police and Al-Adamiyah) each one separate from the other for the year (2000-2001). After all that many findings were reached such as the lack of objective valuation (periodical tests) between one sport season and the other. In the light

The adhesion strength between Polyethylene (PE) film and Aluminum surface by using the adhesive material (Cyanoacrylate) has been studied. Aluminum (Al) was used as a substrate, and polyethylene (PE) was used as a film adhered to the Al surface. Standard specimens were prepared to use in the peeling test in dry condition, other specimens were immersed in water for 12 days at room temperature. the results for the specimens in the dry condition had shown that high value in the peel force and the peel energy, the peel force was 0.38*103 N/m and the peel energy was 0.605*103 N/m, peeling the film from Al surface leaves a residual of the adhesive material on both adherend, the failure for this specimen were combination of adhesive and cohesive f

المستودع الرقمي العراقي. مركز المعلومات الرقمية التابع لمكتبة العتبة العباسية المقدسة

An inert matrix  that is used to control the release of  (PTX) was prepared using Eudragit RL100 and RSPM types as matrix forming agent . The matrices were prepared by either dry granulation(slugging) , or wet granulation method using chloroform as a solvent evaporation vehichle. The cumulative release was adjusted by using polyvinylpyrollidone (PVP) or ethylcellulose (EC) polymers .The results indicated that   both methods of preparation were valid for incorporation PTX as a sustained release granules .Moreover ,the results revealed that best polymer used  was Eudragit RSPM in 3:20 polymer drug ratio .Besides to that ,   the results indicated that the release profiles were affected by  pH- medium&

Dental implants are considered a unique treatment alternative for the replacement of missing dentition. There is a strive for materials which increase bone formation in bone implant interface and improve osseointegration to offer immediate loading directly after placement with decreased time. The aim of the study was to assess the effect of nano strontium substituted hydroxyapatite and nano fluorapatite mixture coating of screw shaped commercially pure titanium at the bone implant interface by torque removal test and histological assessment in rabbit tibia. Commercially pure titanium was used to prepare 80 screws that were divided into machined surfaces (CpTi), coated with (SrHA), coated with (FA) and coated with mixture 50%SrHA + 50%FA (mi