Background: The bond strength of the root canal sealers to dentin seems to be a very important property for maintaining the integrity and the seal of root canal filling. The aim of this study was to evaluate the shear bond strength of four different obturation systems using push-out test. Materials and methods: Forty straight palatal roots of the maxillary first molars teeth were used in this study, these roots were instrumented using crown down technique and ProTaper system, instrumentation were done with copious irrigation of 2.5% sodium hypochlorite and 17% buffered solution of EDTA was used as final irrigant followed by distilled water, roots were randomly divided into four groups according to the obturation system (ten teeth for each group): Group I: AH26 sealer and lateral condensation technique, Group II: AH26 sealer and single cone obturation technique, Group III: AH26 sealer and thermafil obturation technique and Group IV: RealSeal SE sealer and lateral condensation technique, the roots then stored in moist environment at 37°C for one week The roots were embedded in clear acrylic resin and each root sectioned into three levels apical, middle and cervical. The measurement of each section was taken to prepare the supporting jig for the sections and the punch used in pushout test, the bond strength was measured using computerized universal testing machine each section fixed in the machine so that the load applied from apical to cervical direction at 0.5mm/min. speed and the computer drew curve to show the higher bond force before dislodgment of the filling material. These forces were divided by the surface area to obtain the bond strength in MPa. Results: Statistical analysis was performed and the result showed avery highly significant differences between the four obturation systems at each level and there were non significant differences between all level apical, middle and cervical within each obturation system except a significant difference found between cervical and apical level in single cone obturation system. Conclusion: This study showed that the shear bond strength of AH26 sealer was higher than RealSeal SE sealer when the same obturation technique was used. The shear bond strength was affected by the obturation technique and lateral condensation technique showed higher bond strength than thermafil and single cone obturation technique when the same type of sealer was used and the bond strength was not or little affected by the tooth level
Premature degradation is the problem of maxillofacial silicones, significantly affected by ultraviolet exposure, contributing to silicones photodegradation. Degradation necessitates frequent replacement of prostheses that increase the total cost of rehabilitation.
This study evaluated the effect of bisoctrizole on the ultraviolet absorption properties of silicone material and the stability of this absorption over time. Also, the bisoctrizole effect on the surface roughness of silicone was evaluated.
(1)
(1)
Background: White spot lesion is the first visible sign of dental caries that is characterized by demineralized lesion underneath an intact surface. Several studies demonstrated that they could be treated using noninvasive techniques like the use of fluoride or casein phospho-peptide and amorphous calcium phosphate. Improvement in aesthetic outcomes by covering the demineralized enamel is one of the advantages of the use of resin infiltration and opal-ustre microabrasion, which are two new techniques that had been used for treatment of white spot lesion. The purpose of this study was to evaluate the impact of resin infiltration and microabrasion in the microhardness of the artificial white spot lesions at various depths. Material and method
... Show More
(17)
(13)
(13)
Background: Propolis has received great interest because of its wide range antimicrobial activity. Propolis also called (bee glue) due to its collection by (Apismellifera) honeybees from various plants resinous substance. The aim of this study was to determine the antibacterial effect of propolis extracts (aqueous and alcoholic) on anaerobic periodontal pathogen namely Aggregatibacteractinomycetemcomitans. Materials and Methods: Strains of Aggregatibacter actinomycetemcomitans wasisolated from pockets of systemically healthy patients aged between 35-55 years old suffering from chronic periodontitis with pocket depths of 5-6 mm, the bacteria cultured on special blood Agar plates solid media. Propolis was extracted by using water and alcohol.
... Show MoreLaser skin wound soldering offers many distinct advantages over conventional closure and laser welding techniques. Objective : to compare the histological effects of human skin wound soldering using 50 % human albumin solder and compound charcoal photosensitiser with 980 nm diode laser acting in various modes of action and parameters. Study Design/Materials and Methods: In this in vitro experimental study , Multiple 3-4 cm long full thickness incisions in a specimen of human skin were soldered using a 4 mm spot diameter beam of 980 nm diode laser(at different laser parameters and modes of action) with 50 % human albumin solder mixed with the compound charcoal at 5 % W/V concentration .After obtaining a successful wound soldering , the wo
... Show More
Background: Calcium hydroxide and calcium-silicate materials used as direct pulp capping materials. The aims of this in vitro study is to compare among these materials in, the calcium ion release and pH change in soaking water after immersion of materials’ specimens in deionized water. Also Solubility and water sorption of materials’ specimens measured after soaking time. Calcium-silicate materials used were Biodentine, TheraCal and MTA Plus. Materials and methods: Four materials used in this study; Urbical lining (as control group), Biodentine, TheraCal and MTA Plus. Ten discs fabricated from each tested material, by using plastic moulds of 9 mm diameter and 1 mm thickness. Each specimen was immersed in 10 ml of d
... Show More
(4)
The rapid growth of cities and their inflation is a big problem, especially in the last years. this growth is accompanied by such problems like population growth, housing need, low level of services, random expansion, traffic congestion as well as pollution of the environment, which leads to a decline in the quality of life in Baghdad, the population are concentration in Baghdad therefore that leads to imbalance of development among cities and productive concentration for service projects in a mega cities, causing migration from other provinces In search of a better life. The main objective of the new cities is to relieve pressure on major cities and guide the growth of cities. Basmaya city it’s a new city project adopted f
... Show More
(9)
(1)
Background This in vitro study compares a self-etch primer (SEP) to an etch-and-rinse (EaR) for bonding sapphire brackets by evaluation of the enamel etch-pattern, shear bond strength, amount of remnant adhesive and enamel surface damage following thermal and fatigue cyclic loading. Material and Methods Ceramic (sapphire) brackets were bonded to 80 extracted human premolars using two enamel etching protocols: conventional EaR using 37% phosphoric acid (PA) gel (control), and a SEP (Transbond Plus). Each group was subdivided into two subgroups (n=20 teeth) according to the time of bracket debonding: after 24 h water storage or following 5000 thermo-cycles plus 5000 cycles fatigue loading, to determine the shear bond strength (SBS), adhesive
... Show More
(21)
(2)
Background: This in vitro study compares a self-etch primer (SEP) to an etch-and-rinse (EaR) for bonding sapphire brackets by evaluation of the enamel etch-pattern, shear bond strength, amount of remnant adhesive and enamel surface damage following thermal and fatigue cyclic loading. Material and Methods: Ceramic (sapphire) brackets were bonded to 80 extracted human premolars using two enamel etching protocols: conventional EaR using 37% phosphoric acid (PA) gel (control), and a SEP (Transbond Plus). Each group was subdivided into two subgroups (n=20 teeth) according to the time of bracket debonding: after 24 h water storage or following 5000 thermo-cycles plus 5000 cycles fatigue loading, to determine the shear bond strength (SBS), adhesiv
... Show More
(21)
(2)