It is often noted that disordered materials have different chemical properties to their more “ordered” cousins. Quantifying these effects in terms of thermodynamics is challenging in part because disordered materials can be difficult to characterize and are frequently relatively unstable. During the course of our experiments to understand the effects of disorder in catalysts for water oxidation we observed that many disordered manganese and cobalt oxide water oxidation catalysts directly oxidized peroxide in contrast to their more ordered analogues which catalyzed its disproportionation, that is, MnO2+2H+ +H2O2! Mn2+ +2H2O+O2(oxidation) versus H2O2!H2O+1=2 O2(disproportionation). By measuring the efficiency for one reaction over the oth

The research objective was to study the amount of lost fluids, some blood components and mineral salts in volleyball players under hot weather conditions. The sample of the present study was composed of 12 volleyball players of Al-Sinaa Club (Baghdad, Iraq) in the 2022/2023 season. The variables analyzed in this study were: Heart rate before and after exercise, internal and external body temperature before and after exertion, potassium ion, sodium ion, calcium ion, and the amount of fluid lost (the player's weight) before and after the exercise. The tests were conducted at a temperature between 42-47 degrees Celsius. The maximum anaerobic exercise was performed with volleyball. The results showed that to play volleybal

Hydrogen and nanocarbon were produced by the catalytic decomposition of electrocracking gas obtained by the pyrolysis of liquid organic waste via electric arc discharge. The GIAP-16 (NiO-Al2O3) industrial catalyst was used to reduce the maximum decomposition temperature to 700 °C. In a fixed-bed reactor, under atmospheric pressure, reasonable amounts of high-purity hydrogen were produced, accompanied by deposits of nanocarbon by-product. The NiO-Al2O3 catalyst showed excellent catalytic activity. X-ray powder diffraction analysis of the NiO-Al2O3 composite revealed the presence of cubic NiO and rhombohedral Al2O3, which were chemically stable. However, above 500 °C, NiAl2O4 began to appear. The specific surface area of the catalyst was de

The research objective was to study the amount of lost fluids, some blood components and mineral salts in volleyball players under hot weather conditions. The sample of the present study was composed of 12 volleyball players of Al-Sinaa Club (Baghdad, Iraq) in the 2022/2023 season. The variables analyzed in this study were: Heart rate before and after exercise, internal and external body temperature before and after exertion, potassium ion, sodium ion, calcium ion, and the amount of fluid lost (the player's weight) before and after the exercise. The tests were conducted at a temperature between 42-47 degrees Celsius. The maximum anaerobic exercise was performed with volleyball. The results showed that to play volleybal

Alloys of InxSe1-x were prepared by quenching technique with
different In content (x=10, 20, 30, and 40). Thin films of these alloys
were prepared using thermal evaporation technique under vacuum of
10-5 mbar on glass, at room temperature R.T with different
thicknesses (t=300, 500 and 700 nm). The X–ray diffraction
measurement for bulk InxSe1-x showed that all alloys have
polycrystalline structures and the peaks for x=10 identical with Se,
while for x=20, 30 and 40 were identical with the Se and InSe
standard peaks. The diffraction patterns of InxSe1-x thin film show
that with low In content (x=10, and 20) samples have semi
crystalline structure, The increase of indium content to x=30
decreases degree o