This study is concerned with the effect of Deep Cryogenic Treatment (DCT) at liquid nitrogen temperature (-196 o C) on the mechanical properties and performance of low carbon steel (A858). The tests specimens were divided in to two groups, the first group was subjected to the conventional heat treatment of normalizing, and the second group was also normalized then subjected to (DCT). The results have shown that after (DCT), the Hardness, Tensile properties and the impact energy absorbed were all slightly increased. However the fatigue test showed some positive improvement in fatigue limit by 20(N/mm2 ), and the volume wear rates at different loads were significantly decreased after (DCT). The changes in microstructure due to (DCT) were c

The present work involved synthesis of new thiozolidinone derivatives,These derivatives could be divided into three type of compounds; quinolin-2-one[V]a,b ,Schiff bases[VI]a,b and imide compounds[VII]a-d. The reaction p-Hydroxyacetophenone with thiosemicarbazide led to formation thiosemicarbazon compound [II], the reacted of thiosemicarbazone with chloro acetic acid in CH3CO2Na led to yield 4- thiazelidinone compound[III] in addition, thiosemicarbazide was POCl3 to [III] give [IV] compound used intermediates to synthesis new compounds of reacted with two type of coumarin in glacial acetic acid to give quinolin-2-one[V]a,b, The later compound refluxing with different benzaldehyde in dry benzene and glacial acetic acid give Schiff bases[VI]a

This work comprises the synthesis of new thioxanthone derivatives containing C-substituted thioxanthone. To obtain these derivatives, the o-mercapto benzoic acid was chosen as the starting material, which was reacted with dry benzene in sulfuric acid (98 %) to produce the thioxanthone (1). The 2,7-(disulfonyl phosphine imine) thioxanthone (4-8) were prepared from reaction of compound (1) with chlorosulfonic acid gave 2,7-(disulfonyl chloride) thioxanthone (2). Treatment of (2) with sodium azide to produce 2,7-(disulfonyl azide) thioxanthone (3). Condensation of (3) with phosphorus compounds afforded compounds (4-8). The 2,7-(disulfonamide) thioxanthone (9-21) was obtained when co

Coupling reaction of 2-amino benzoic acid with 8-hydroxy quinoline gave bidentate azo ligand. The prepared ligand has been identified by Microelemental Analysis,1HNMR,FT-IR and UV-Vis spectroscopic techniques. Treatment of the prepared ligand with the following metal ions (ZnII,CdII and HgII) in aqueous ethanol with a 1:2 M:L ratio and at optimum pH, yielded a series of neutral complexes of the general formula [M(L)2]. The prepared complexes have been characterized by using flame atomic absorption, (C.H.N) Analysis, FT-IR and UV-Vis spectroscopic methods as well as conductivity measurements. The nature of the complexes formed were studied following the mole ratio and continuous variation methods, Beer's law obeyed over a concentration ra

Coupling reaction of 2-amino benzoic acid with 8-hydroxy quinoline gave bidentate azo ligand. The prepared ligand has been identified by Microelemental Analysis,1HNMR,FT-IR and UV-Vis spectroscopic techniques. Treatment of the prepared ligand with the following metal ions (ZnII,CdII and HgII) in aqueous ethanol with a 1:2 M:L ratio and at optimum pH, yielded a series of neutral complexes of the general formula [M(L)2]. The prepared complexes have been characterized by using flame atomic absorption, (C.H.N) Analysis, FT-IR and UV-Vis spectroscopic methods as well as conductivity measurements. The nature of the complexes formed were studied following the mole ratio and continuous variation methods, Beer's law obeyed over a concentration range

Coupling reaction of 2-amino benzoic acid with 8-hydroxy quinoline gave bidentate azo ligand. The prepared ligand has been identified by Microelemental Analysis,1HNMR,FT-IR and UV-Vis spectroscopic techniques. Treatment of the prepared ligand with the following metal ions (ZnII,CdII and HgII) in aqueous ethanol with a 1:2 M:L ratio and at optimum pH, yielded a series of neutral complexes of the general formula [M(L)2]. The prepared complexes have been characterized by using flame atomic absorption, (C.H.N) Analysis, FT-IR and UV-Vis spectroscopic methods as well as conductivity measurements. The nature of the complexes formed were studied following the mole ratio and continuous variation methods, Beer's law obeyed over a concentration range

A new Schiff base ligand Bis-1,4-di[N-3-(2-hydroxy-1-amino)- acetophenonylidene] benzylidene [L] and its complexes with (Mn(II) ,Co(II) ,Ni(II and Cu(II)) were synthesized . The ligand was prepared in two steps. In the first step a solution of (terphthalaldehyde) in methanol reacts under reflux with (p-aminoacetophenone) to give an intermediate compound [1-[3-({4-[(3-Acetyl-phenylimino)-methyl]-benzylidene}-amino)-phenyl]- ethanone which reacts in the second step with (2-Amino-phenol) giving the mentioned ligand. The complexes were synthesized by addition the corresponding metal salt solution to the solution of the ligand in methanol under reflux in (1:1) metal to ligand ratio. On the basis of, molar conductance, I.R., UV-Vis, HPLC, chlorid

Activated carbon loading with metals oxides is new adsorbents and catalyst, which seem very promising for desulfurization process. The present study deals with the preparation of three metals oxides loaded on activated carbon (AC). The tri composite of ZnO/NiO/CoO/AC was characterized by X-Ray Diffraction (XRD), X-Ray florescence (XRF), N₂ adsorption for BET surface area, pore volume and Atomic Force Microscopy (AFM). The effect of calcination temperature is investigated. The best calcination temperature is 250^oC based on the presence of phase, low weight loss and keep at high surface area. The surface area and pore volume of prepared tri composite are 932.97m²/g and 0.6031cm³/g respec

The nanostructured Manganese dioxide/Carbon fiber (CF) composite electrode was prepared galvanostatically using a facile method of anodic electrodeposition by varying the reaction time and MnSO4 concentration of the electrochemical solution. The effects of these parameters on the structures and properties of the prepared electrode were evaluated. For determining the crystal characteristics, morphologies, and topographies of the deposited MnO2 films onto the surfaces of carbon fibers, the X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and atomic force microscopy (AFM) techniques were used, respectively. It found that the carbon fibers were coated with γ-MnO2 with a density that increased with increasing the de