Positron annihilation lifetime (PAL) technique has been employed to
study the microstructural changes of polyurethane (PU), EUXIT 101
and epoxy risen (EP), EUXIT 60 by Gamma-ray irradiation with the
dose range (95.76 - 957.6) kGy. The size of the free volume hole and
their fraction in PU and EP were determined from ortho-positronium
lifetime component and its intensity in the measured lifetime spectra.
The results show that the irradiation causes significant changes in the
free volume hole size (V_h) and the fractional free volume (F_h), and
thereby the microstructure of PU and EP. The results indicate that
the γ-dose increases the crystallinity in the amorphous regions of PU
and increas

Ten isolates of Klebsiella pneumoniae, seven isolates of Pseudomonas aeruginosa and nine isolates of Staphylococcus aureus, were obtained from 100 urine samples collected from Baghdad hospitals. All isolates were identified biochemically and confirmed by using VITEK 2 and were then tested for their susceptibility towards 6 antibiotics and for phenolic extracts of Thymus vulgaris and Cinnamomum cassia. All bacteria were greatly affected by T. vulgaris, especially K. pneumoniae. Viable count was performed, it was noted that the number of bacterial cells reduced from 1×108 CFU to 1.2× 103, 2×105 and 1.8×106CFU of K. pneumoniae, P. aeruginosa and S. aureus respectively. While C. cassiahad a slight effect on them. K. pneumoniae isola

Abstract: In this research, nanofibers have been prepared by using an electrospinning method. Three types of polymer (PVA, VC, PMMA) have been used with different concentration. The applied voltage and the gap length were changed. It was observed that VC is the best polymer than the other types of polymers.

In this research, nanofibers have been prepared by using an electrospinning method. Three types of polymer (PVA, VC, PMMA) have been used with different concentration. The applied voltage and the gap length were changed. It was observed that VC is the best polymer than the other types of polymers.

This survey investigates the thermal evaporation of Ag2Se on glass substrates at various thermal annealing temperatures (300, 348, 398, and 448) °K. To ascertain the effect of annealing temperature on the structural, surface morphology, and optical properties of Ag2Se films, investigations and research were carried out. The crystal structure of the film was described by Xray diffraction and other methods.The physical structure and characteristics of the Ag2Se thin films were examined using X-ray and atomic force microscopy (AFM) based techniques. The Ag2Se films surface morphology was examined by AFM techniques; the investigation gave average diameter, surface roughness, and grain size mutation values with increasing annealing temperature

Superconducting thin films of Bi1.6Pb0.4Sr2Ca2Cu2.2Zn0.8O10 system were prepared by depositing the film onto silicon (111) substrate by pulsed laser deposition. Annealing treatment and superconducting properties were investigated by XRD and four probe resistivity measurement. The analysis reveals the evolution of the minor phase of the films 2212 phase to 2223 phase, when the film was annealed at 820 °C. Also the films have superconducting behavior with transition temperature ≥90K.

In this article the nanoparticles synthesis of ZnO (Nps) by using the precipitation method at concentrations range (0.5, 0.25, 0.125, 0.0625, 0.03125) mg/mL and then activity was examined against Streptococcus spp that causing dental caries in vitro by well diffusion method, find these concentrations effected in these bacteria and better concentration is 0.03125. ZnO Nps were characterization by EDS to prove this particles are ZnO, and also characterized by atomic force microscope (AFM), X-ray Diffraction (XRD) and TEM, from these technic found that the average size about 30.52 nm and hexagonal shape. The UV-visible result reveals that the large band is observed at 340.8 nm, Zeta potential show that the surface charge is 30.19 mv an

Microwave heating is caused by the ability of the materials to absorb microwave energy and convert it to heat. The aim of this study is to know the difference that will occur when heat treating the high strength aluminum alloys AA7075-T73 in a microwave furnace within different mediums (dry and acidic solution) at different times (30 and 60) minutes, on mechanical properties and fatigue life. The experimental results of microwave furnace heat energy showed that there were variations in the mechanical properties (ultimate stress, yielding stress, fatigue strength, fatigue life and hardness) with the variation in mediums and duration times when compared with samples without treatment. The ultimate stress, yielding stress and fatigue streng

Aim: This study aimed to compare different types of ligation methods to obtain maximum tooth movement with the least undesirable rotation. Methods: Titanium brackets bonded to acrylic canine teeth were ligated to straight stainless steel (SS) archwires using four ligation methods (figure-O and figure-8 elastics, SS ligatures, and Leone Slide ligatures). The teeth with the ligatures in place were stored in a water bath at 37ºC for 1 day, 1 week, 2, 4 or 6 weeks before testing. The teeth were retracted through softened wax along the archwire and the amount of tooth movement and degree of rotation were measured. Results: Slide ligatures showed the highest distance of tooth movement and degree of canine rotation followed by figure-O elastics