Pyridine-2, 6-dicarbohydrazide comp (2) was synthesized from ethanolic solution of diethyl pyridine-2, 6- dicarboxylate comp (1) with excess of hydrazine hydrate. Newly five polymers (P1-P5) were synthesized from reaction of pyridine-2, 6-dicarbohydrazide comp (2) with five different di carboxylic acid in the presence of poly phosphoric acid (PPA). The antibacterial activity of the synthesized polymers was screened against some gram positive and gram negative bacteria. Antifungal activity of these polymers was evaluated in vitro against some yeast like fungi such as albicans (candida albicans). Polymers P3, P4 and P5 exhibited highest antibacterial and antifungal against all microorganisms under test.

One of the most important , compound which have active hydrogen is the compound possessing (thiol group) Biphenyl-4,4-dithiol is agood example utilized in a wide field for preparation mannich bases , avariety of new acetylenic mannich bases have been Synthesized and all proposed structure were Supported by FTIR , 1H – NMR, 13C-NMR , Elemental analysis and microbial study .

An aromatic ester containing two azo groups namely p-nitro phenyl azo-β-naphthyl-(4'-azobenzoic acid)-4-benzoate was synthesized by esterfiaction of 4,4'-azo dibenzoic acid with p-nitro phenyl azo-β-naphthol. Synthesized ester was characterized by CHN-Elemental analysis, FTIR, 1H NMR and 13C NMR. A modified PVA polymer was obtained by grafting 10 g of PVA-polymer via partial esterification with (2, 3, 4 g) p-nitro phenyl azo-1-naphthyl-4-azobenzoic acid)-4-azo benzoate. Grafting PVA-polymer behaviours was studied, by physical measurements (solubility, swelling), thermal properties (DSC) and tensile.

Activated carbon derived from Ficus Binjamina agro-waste synthesized by pyro carbonic acid microwave method and treated with silicon oxide (SiO2) was used to enhance the adsorption capability of the malachite green (MG) dye. Three factors of concentration of dye, time of mixing, and the amount of activated carbon with four levels were used to investigate their effect on the MG removal efficiency. The results show that 0.4 g/L dosage, 80 mg/L dye concentration, and 40 min adsorption duration were found as an optimum conditions for 99.13% removal efficiency. The results also reveal that Freundlich isotherm and the pseudo-second-order kinetic models were the best models to describe the equilibrium adsorption data.

Samples prepared by using carbon black as a filler material and phenolic resin as a binder. The samples were pressed in a (3) cm diameter cylindrical die to (250)MPa and treated thermally within temperature range of (600-1000)oC for two and three hours. Physical properties tests were performed, like density, porosity, and X-ray tests. Moreover vicker microhardness and electric resistivity tests were done. From the results, it can be concluded that density was increased while porosity was decreased gradually with increasing temperature and treating time. In microhardness test, it found that more temperature and treating time cause more hardness. Finally the resistivity was decreased in steps with temperature and treating time. It can be c

New bidentate dithiocarbamate ligand (NaL) namely [Sodium-2-(((3-methyl -4- “(2,2,2-tri fluoro ethoxy) pyridin-2”-yl) methyl) sulfinyl)-1H-benzoimidazole -1-carbodithioate] was prepared. This free ligand was synthesized from the reaction of a (RS)-2-([3-methyl -4-(2,2,2-tri fluoroethoxy) pyridin-2-yl] methyl sulfinyl)-1H benzoimidazole, CS2 and NaOH in methanol as solvent. From reaction of dithiocarbamate salt (NaL) with metal ions (M); Co(II), Ni(II), Cu(II), Zn(II), Cd(II) and Pd(II)”, have obtained the DTC complexes at general molecular formula [M(L)2(H2O)2] and [Pd(L)2]. To characterize the ligand and its complexes, used different analyses methods such FTIR, UV-Vis, elemental microanalysis, atomic absoreption, magnetic susceptibil