The research included preparation of new Schiff base (L) by two steps: preparation of precursor [bis(2-formyl-6-methoxyphenyl) succinate] (P) by reacting (3-methoxy salicyl aldehyde) with (succinoyl dichloride) as first step then react the prepared precursor (P) with (ethanethioamide) to have the new Schiff base [bis(2-((ethane thioyl imino) methyl)-6-methoxy phenyl) succinate] (L) as second step. Characterized compounds based on Mass spectra, 1 H, 13CNMR (for ligand (L)), FT-IR and UV spectrum, melting point, molar conduct, %C, %H, and %N, the percentage of the metal in complexes %M, magnetic susceptibility, while study corrosion inhibition (mild steel) in acid solution by weight loss. These measurements proved that by (Oxygen, Nitrogen, and Sulfur) atoms in the ligand, the metal ions are coordinated in a tetradentate form, and the tetrahedral structure of these complexes is suggested. Based on the measurement of micro elemental analysis (CHNS), the molar ratio appeared (2:1) (M:L). The complexes of [M2(L)Cl2]Cl2 type, where M= Cobalt(ii), Nickel(ii), Copper(ii) and Zinc(ii). These products were determined aligned with two classes of bacterial; bacteria (G+ ) and (G- ). The antibacterial effect of the metal complexes is greater than that of the ligand (free), according to the results of the bacterial activity test for the compounds. Results of corrosion inhibition of (L) and their complexes were determined by method (weight loss) in (0.2M) hydrochloric acid solution for mild steel.
The purpose of the current work was to evaluate the effect of Radiation of Gamma on the superconducting characteristics of the compound PbBr2Ca1.9Sb0.1Cu3O8+δ utilizing a 137Cs source at doses of 10, 15, and 20MRad. Solid state reaction technology was used to prepare the samples. Before and after irradiation, X-ray diffraction (XRD) and superconductor properties were examined. Results indicated that the tetragonal structure of our chemical corresponds to the Pb-1223 phase with an increase in the ratio c/a as a result of gamma irradiation. (Tc (onset) ) and on set temperature Tc (offset)) were also dropping from 113 to the 85.6 K and 129.5 to 97 K, respectively, for a transition temperatu
The aim of this paper is to prove some results for equivalence of moduli of smoothnes in approximation theory , we used a"non uniform" modulus of smoothness and the weighted Ditzian –Totik moduli of smoothness in by spline functions ,several results are obtained .For example , it shown that ,for any the inequality , is satisfied ,finally, similar result for chebyshev partition and weighted Ditzian –Totik moduli of smoothness are also obtained.
During the ongoing economic revolutions of the economic There is a new economic revolution is emboded by upseting the balances of prevailing classic ideas and refusing axioms considered postulates which were not touched including, for example, the theory of ( supply and demand) espoused by (Adam Smith and Marshall and others ) that assumes the existence of a strong relationship between the supply of goods and services and the demand for them, in the light of successive economic developments, considerable technological progress and the information revolution of the complex telecommunication network led to a serious shift of this theory and the emergence of a new theory called (market economies) turned the traditional scales of production,
... Show More
(191)
(171)
A spectrophotometric- reverse flow injection analysis (rFIA) method has been proposed for the determination of Nitrazepam (NIT) in pure and pharmaceutical preparations. The method is based upon the coupling reaction of NIT with a new reagent O-Coumaric acid (OCA) in the presence of sodium periodate in an aqueous solution. The blue color product was measured at 632 nm. The variation (chemical and physical parameters) related with reverse flow system were estimated. The linearity was over the range 15 - 450 µg/mL of NIT with detection limits and limit of quantification of 3.425 and 11.417 µg mL-1 NIT,respectively. The sample throughput of 28 samples
... Show More
(10)
(1)
In this paper Alx Ga1-x As:H films have been prepared by using new deposition method based on combination of flash- thermal evaporation technique. The thickness of our samples was about 300nm. The Al concentration was altered within the 0 x 40.
The results of X- ray diffraction analysis (XRD) confirmed the amorphous structure of all AlXGa1-x As:H films with x 40 and annealing temperature (Ta)<200°C. the temperature dependence of the DC conductivity GDC with various Al content has been measured for AlXGa1-x As:H films.
We have found that the thermal activation energy Ea depends of Al content and Ta, thus the value of Ea were approximately equal to half the value of optical gap.
The present study aimed to identify the extent to which the content of social and national studies courses was included in interactive thinking maps in the educational stages in the Kingdom of Saudi Arabia, and to achieve the goal of the study, the researcher used the descriptive and analytical approach, and the study tool used consisted of a content analysis card; Where it included a list of the types of thinking maps, where the study sample consisted of all social and national studies courses at the elementary and intermediate levels, and it is (12) books for the student in its first and second parts, and after verifying the validity and reliability of the tool, it was applied to the study sample, and the study reached conclusions, inc
... Show MoreThe present research included synthesis of silver nanoparticle from(1*10-3,1*10-4 and1*10-5) M aqueous AgNO3 solution through the extract of M.parviflora reducing agent. In the process of synthesizing silver nanoparticles we detected a rapid reduction of silver ions leading to the formation of stable crystalline silver nanoparticles in the solution.
(15)
(2)
The CIGS/CdS p-n junction thin films were fabricated and deposited at room temperature with rate of deposition 5, and 6 nm secG1 , on ITO glass substrates with 1mm thickness by thermal evaporation technique at high vacuum pressure 2×10G5 mbar, with area of 1 cm2 and Aluminum electrode as back contact. The thickness of absorber layer (CIGS) was 1 µm while the thickness of the window layer CdS film was 300 nm. The X-ray Diffraction results have shown that all thin films were polycrystalline with orientation of 112 and 211 for CIGS thin films and 111 for CdS films. The direct energy gaps for CIGS and CdS thin films were 1.85 and 2.4 eV, respectively. Atomic Force Microscopy measurement proves that both films CIGS and CdS films have nanostru