Reducing a structure’s self-weight is the main goal and a major challenge for most civil constructions, especially in tall buildings and earthquake-affected buildings. One of the most adopted techniques to reduce the self-weight of concrete structures is applying voids in certain positions through the structure, just like a voided slab or BubbleDeck slab. This research aims to study, experimentally and theoretically, the structural behavior of BubbleDeck reinforced concrete slabs under the effect of harmonic load. Tow-way BubbleDeck slab of 2500mm×2500m×200mm dimensions and uniformly distributed bubbles of 120mm diameter and 160mm spacing c/c was tested experimentally under the effect of harmonic load. Numerical analysis was als

Background: The study was designed to evaluate the effect of local application of exogenous VEGF/collagen I separately and as a combination in socket healing. Sixty male Albino Wistar rats were subjected for a surgical tooth extraction of upper 1st molar of both sides (right side was considered as experimental site, while left be the control one, treated with 1µL of normal saline). The rats were scarified at 3, 7, 14, 28 days post extraction. Socket healing was histologically examined with immunohistochemistochemical localization of ALP&FGF2. Materials and Method: Sixty male Albino Wistar rats were subjected for a surgical tooth extraction of upper 1stmolar of both sides (right side was considered as experimental site, while left be the

Background: A recent discoveries used for reconstruction in maxillofacial surgery is the composite bone graft materials. The availability of collagen I matrix make our choice to use this material in surgery .It is biomaterials that its structure could be modified by simple techniques. Studies to find a new materials use for bone reconstruction is to overcome the disadvantages of autogenous bone and the synthetic resorbable bone substitutes.

Objectives: This study was done to evaluate the effect of biphasic calcium phosphate collagen composite (ccpc) on healing of bone defects after oral surgical procedures.

Type of the study: A cross sectional study.

Method: It involved 60 patients, 35 male and 25 female, age (15-

This article discusses the function of semiotics in political discourse after the socio-political processes taking place in Iraq since 2003 and its role in the development of textual criticisms of some Iraqi politicians, analyzes the reasons for its functioning in the speech of politicians. The research is mainly focused on finding out to what extent political text studies draw on sign systems that can store and transmit information, the nature of its purpose and the use of available fields for the purpose to be achieved. The chief purpose of the study is to investigate and also clarify the symbols and signs appear within the framework of discursive Iraqi politicians, the nature of the symbols used, and the meanings that are include

     The aim of this paper to study the effect of the implicit factors on the entrepreneurial spirit of the students of the Algerian university. Our structural model was proposed based on the model (Shapiro et Sokol, 1982) and the model (Ajzen, 1991). We tested it on a sample of 163 university students at the University of Algiers 3. The model consists of a set of variables (the intention of contracting as a dependent variable, structural and social educational support as independent variables). The results showed that educational and social support factors affect the entrepreneurial spirit of students more than structural support. The Applied Impacts are the enhancing of knowledge capacities of university stu

   This research studies the rheological properties ( plastic viscosity, yield point and apparent viscosity) of Non-Newtonian fluids under the effect of temperature using different chemical additives, such as (xanthan gum (xc-polymer), carboxyl methyl cellulose ( High and low viscosity ) ,polyacrylamide, polyvinyl alcohol, starch, Quebracho and Chrome Lignosulfonate). The samples were prepared by mixing 22.5g of bentonite with 350 ml of water and adding the additives in four different concentrations (3, 6, 9, 13) g by using Hamilton Beach mixer. The rheological properties of prepared samples were measured by using Fan viscometer model 8-speeds. All the samples were subjected to Bingham plastic model. The temperature range studi

Rapid worldwide urbanization and drastic population growth have increased the demand for new road construction, which will cause a substantial amount of natural resources such as aggregates to be consumed. The use of recycled concrete aggregate could be one of the possible ways to offset the aggregate shortage problem and reduce environmental pollution. This paper reports an experimental study of unbound granular material using recycled concrete aggregate for pavement subbase construction. Five percentages of recycled concrete aggregate obtained from two different sources with an originally designed compressive strength of 20–30 MPa as well as 31–40 MPa at three particle size levels, i.e., coarse, fine, and extra fine, were test

Background: Alginate impression material is the irreversible hydrocolloid material that is widely used in dentistry. The contact time between alginate and gypsum cast could have a detrimental effect on the properties of the gypsum cast. The objective of this study is to evaluate the impact of various contact time intervals of Alginate impressions & type III dental stone on surface properties of stone cast. Materials and Methods: Time intervals tested were 1hour, 6 hours and 9 hours. Surface properties of stone cast evaluated were surface detail reproduction, hardness and roughness. Surface detail reproduction was determined using cylindrical brass test block in accordance with ISO 1563. Surface roughness was measured by profilometer

Polycrystalline Cadmium Oxide (CdO) thin films were prepared
using pulsed laser deposition onto glass substrates at room
temperature with different thicknesses of (300, 350 and 400)nm,
these films were irradiated with cesium-137(Cs-137) radiation. The
thickness and irradiation effects on structural and optical properties
were studied. It is observed by XRD results that films are
polycrystalline before and after irradiation, with cubic structure and
show preferential growth along (111) and (200) directions. The
crystallite sizes increases with increasing of thickness, and decreases
with gamma radiation, which are found to be within the range
(23.84-4.52) nm and (41.44-4.974)nm before and after irradiation for