This research aims to study the effect of microwave furnace heat on the mechanical properties and fatigue life of aluminum alloy (AA 2024-T3). Four conditions were used inside microwave furnace (specimens subjected to heat as dry for 30 and 60min. and specimens subjected to heat as wet (water) for 30 and 60 min.), and compared all results with original alloy (AA 2024-T3). Tensile, fatigue, hardness and surface roughness tests were used in this investigation. It is found that hardness of dry conditions is higher than wet conditions and it increases with increasing of time duration inside microwave furnace for dry and wet conditions. Also, tensile strength has the same behavior of hardness, but it increases with decreasing

In this research the hard chromium electroplating process, which is one of the common methods of overlay coating was used, by using chromium acid as source of chromium and sulphuric acid as catalyst since the ratio between chromic acid and sulphuric acid is (100 : 1) consequently. Plating process was made by applying current of density (40 Amp / dm²) and the range of solution temperature was (50 – 55^oC) with different time periods (1-5 hr). A  low carbon steel type (Ck₁₅) was used as substrate for hard chromium electroplating. Solid carburization was carried out for hard chromium plating specimen at temperature (925^oC) with time duration (2 hr) to be followed with quenching and tempering

Two new organotin(IV) complexes Me2Snesc (C1) and Bu2Snesc (C2) have been synthesised from the reaction of the corresponding organotin(IV) chloride with the Schiff base ligand 3,4-dihydroxybenzaldehyde-4-ethylsemicarbazone (H2esc). The ligand was prepared in two steps. The first step includes the formation of 4-ethylsemicarbazide, which then reacted with 3,4-dihydroxybenzaldehyde to give the title ligand. Complex formation between the organotin(IV) moiety and the anionic form of 3,4-dihydroxybenzaldehy-4-ethylsemicarbazone occurred through the o-dihydroxy positions. The ligand and its complexes were characterised by elemental analysis, FT-IR and NMR (1H, 13C and 119Sn) spectroscopy. Accordingly, the complexes were proposed to have tetrahedr

China's economic policy and its huge capabilities operate according to an expansion strategy, especially in investing foreign projects, as the past ten years have witnessed a major development in the elements of comprehensive strength, especially in the economic field, in 2014 China launched the largest initiative in the world, represented by the Belt and Road Project (BRI), which links nearly 70 countries, through this project, a very important region has emerged, which is (the port of cadres) in Pakistan, as China has headed towards that region and given the highest importance that is in its interest in the first place regardless of the great Pakistani interest, This is consistent with its future aspirations, especially after breaking

Glass Ionomer Cement (GIC) is one of the important dental temporary filing materials. The aim of this study is to evaluate the effect of adding 3, 5 and 7 wt. % of TiO₂ microparticles to conventional GIC powder (Riva Self Cure) on mechanical properties and its effect on absorption and solubility processes. TiO₂ particles additives improved compressive strength and biaxial flexural strength, where the compressive strength increased with increasing in the added ratio, while the highest value of the biaxial flexural strength was at 3 wt.%. The addition of TiO₂ particles improved the surface Vickers microhardness values, with highest value at 5 wt. %. On other hand TiO₂ addition im

In the present study, MIG welding is carried out on low carbon steel type (AISI 1015) by using electrode ER308L of 1.5mm diameter with direct current straight polarity (DCSP). The joint geometry is of a single V-butt joint with one pass welding stroke for different plate thicknesses of 6, 8, and 10 mm. In welding experiments, AISI 1015 plates with dimensions of 200×100mm and edge angle of 60^o from both sides are utilized. In this work, three main parameters related to MIG welding process are investigated, which are welding current, welding speed, heat input and plate thickness, and to achieve that three groups of plates are employed each one consists of three plates. The results indicate that increasing the weld heat input (t

n each relapse. Objjec tt iiv es :: To sttudy diifffferentt ffacttors whiich miightt be associiatted or lleadiing tto
tthe occurrence off rellapse iin nephrottiic syndrome
Metthods:: A retrospective study of seventy patients with nephrotic syndrome with age range of 1-14 years, who were diagnosed and treated in Child's Central Teaching Hospital over the period of 1st of January and 1st of July 2008.
The patients were divided into three groups; frequent relapses group, infrequent relapses group and undetermined group. We compared between frequent relapses group and infrequent relapses group in regard to age, sex, type of presentation, biochemical findings which include; total serum protein, serum albumin and renal function test,