In this paper some chalcones (C1-C8) are prepared based on the reaction of one mole of substituted acetophenone with one mole of substituted benzaldehydes in the presence of (40%) sodium hydroxide as a base. Pyrazolines (P1–P8) are prepared from the reaction of chalcones (C1-C8) with hydrazine hydrate. Isoxazoline (I1-I8) is prepared from the reaction of chalcones (C1-C8) with hydroxyl amine hydrochloride in the presence of (10%) sodium hydroxide as a base. These compounds are characterized by using various physical and spectral methods. The compounds are screened for their in vitro antibacterial activity using gram-positive bacteria and gram-negative bacteria. Several derivatives of pyrazolines and isoxazolines are produced well to moder

Five N-substituted acrylamides were prepared by reaction of substituted aromatic primary amines with acryloyl chloride in the presence of triethyl amine. The synthesized acrylamides were allowed to introduce copolymerization reaction with three vinylic monomers including acrylonitrile, methyl acrylate and methyl methacrylate respectively to obtain eleven new copolymers having different physical properties which may used in different applications.

Cadmium oxide thin films were prepared by D.C magnetron plasma sputtering using different voltages (700, 800, 900, 1000, 1100 and 1200) Volt. The Cadmium oxide structural properties using XRD analysis for just a voltage of 1200 volt at room temperature after annealing in different temperatures (523 and 623) K were studied .The results show that the films prepared at room temperature have some peaks belong to cadmium element along the directions (002), (100), (102) and (103) while the other peaks along the directions of (111), (200) and (222) belong to cadmium oxide. Annealed samples display only cadmium oxide peaks. Also, the spectroscopic properties of plasma diagnostic for CdO thin films were determined and the results show that the el

New 1,2,4-triazole derivatives of 2-mercaptobenzimidazole (MB) are reported. Ethyl (benzimidazole-2-yl thio) acetate (1) has been prepared by condensing 2-mercaptobenzimidazole with ethylchloroacetate. The ester (1) on reacting with hydrazine hydrate gave the corresponding acetohydrazide(2)which was reacted separately with phenylisocyanate and phenylisothiocyanate, followed by ring closure in an alkaline medium giving 3-[(benzimidazole-2-yl thio) methyl]-4-phenyl-1,2,4-triazole-5-ol and 3-[(benzimidazole-2-yl thio) methyl]-4-phenyl-1,2,4-triazole-5-thiol respectively (6,7). Reaction of acetohydrazide (2) with CS2 and ethanol/KOH, gave dithiocarbazate salt (8). Cyclization of (8) with hydrazine hydrate gave 3-[(benzimi

This new azo dye 3-((2-(1H-indol-3-yl) ethyl) diazenyl) quinoline-2-ol was subsequently used to prepare a series of complexes with the metal ions of Cr+3, Cu+2, VO+2, Mn+2and Mo+6. The compounds identified by 1H and 13C-NMR, FT-IR, UV-Vis, mass spectroscopy, as well as TGA, DSC, and C.H.N., conductivity, magnetic susceptibility, metal and chlorine content. The results showed that the ligand behaves in a bidantate, and that the complexes gave octahedral, excepting for VO+2 square pyramid was given, that all complexes are non-electrolytes. The effectiveness of mention the compounds in inhibiting free radicals was evaluated by the ability to act as an antioxidant was measured using DPPH as a free radical and gallic acid as a standard s

This study involves the synthesis of a new class of silicon polymers, designated as P1-P7, derived from dichlorodimethylsilane (DCDMS) in combination with various organic compounds (Schiff bases prepared from different amines and appropriate aldehydes or ketones) [I-V] through condensation polymerization. The structures of all monomers and polymers were characterization by FTIR and 1HNMR spectroscopy (for some polymers). The results of thermogravimetric analysis (TGA) and differential scanning calorimetry DSC test show stable thermal behaviour. Polymers with a higher concentration of aromatic rings in their repeating structural units exhibited a higher temperature for weight loss, indicating increased thermal stability. Thermal meas

This study involves the synthesis of a new class of silicon polymers, designated as P1-P7, derived from dichlorodimethylsilane (DCDMS) in combination with various organic compounds (Schiff bases prepared from different amines and appropriate aldehydes or ketones) [I-V] through condensation polymerization. The structures of all monomers and polymers were characterization by FTIR and 1HNMR spectroscopy (for some polymers). The results of thermogravimetric analysis (TGA) and differential scanning calorimetry DSC test show stable thermal behaviour. Polymers with a higher concentration of aromatic rings in their repeating structural units exhibited a higher temperature for weight loss, indicating increased thermal stability. Thermal meas