The crude enzyme Nattokinase produced by Bacillus subtilis was used in ripening cheddar cheese by adding three concentration of enzyme 80, 160 and 320mg/Kg beside the control treatment without enzyme, the product was checked for three months to determine humidity, protein, fat, non-protein nitrogen, soluble nitrogen and pH, sensory evaluation was conducted, it was noticed that the variety in protein percentages and the soluble nitrogen percentage during second month of ripening for T2, T3 and T4 treatments were (11.2, 15.54 and 18.48) respectively, in comparison with control which was 7.6%, while in the third month it was (17.37, 20.67 and 22.26) respectively, in comparison with control which was only 10%, on the other hand, non-protein

The interest in calcium phosphates arises from the fact that bones contain a high percentage of mineralized calcium phosphate . In this study, pure and biocompatible hydroxyapatite (HAP) powder was successfully synthesized using hen’s egg shell as calcium source and phosphoric acid by precipitation method.The precipitate obtained was subjected to ripenning process for 24 hours, filtered, air dried, and calcined at temperatures of 400,800,900,and 1000 ºC.
X-Ray diffraction(XRD) technique was used to investigate the formation of HAP powder, XRD results revealed the HAP formation and also indicate no occurrence of secondary phases. Fourier Transform Infrared(FT-IR) spectrum shows the characterstic peaks for phosphate and hydroxyl grou

     The nuclear shell model was used to investigate the bulk properties of lithium isotopes (6,7,8,9,11Li), i.e., the ground state density distributions and C0 and C2 components of charge form factors. The theoretical treatment was based on supposing that the Harmonic-oscillator (HO) potential governs the core nucleons while the valence nucleon(s) move through Hulthen potential. Such assumptions were applied for both stable and exotic lithium isotopes. The HO size parameters (  and ), the core radii ( ) and the attenuation parameters (  and ) were fixed to recreate the available empirical size radii for lithium isotopes under study.

A new species of the family Carabidae, subfamily Harpalinae was introdIle7: (1 or a Acupalpus mesopota¬micus on the basis external morphology and male genctalia. The specimens were compared with a world collection of Acupalptis of the British Museum (N. H.) Holotype was kept at the Iraq Natural History Museum. Other 12 specimens were kept in Iraq Natural History Museum.

Used vegetable oil was introduced to transesterfication reaction to produce Biodiesel fuel suitable for diesel engines. Method of production was consisted of filtration, transesterfication, separation and washing. Transesterfication was studied extensively with different operating conditions, temperature range (35-80o C), catalyst concentration (0.5-2 wt. % based on oil), mixing time (30-120 min.) with constant oil/methanol weight ratio 5:1 and mixing speed 1300 rpm. The concentration of Fatty acid methyl esters (Biodiesel) was determined for the transesterficated oil samples, besides of some important physical properties such as specific gravity, viscosity, pour point and flash point. The behavior of methyl esters production and the

Polyvinyl alcohol, (PVA) was prepared using polyvinyl acetate emulsion (manufactured by Al-Jihad factory,
That-Al-Sawary Company) as a local raw material. In this investigation, polyvinyl acetate emulsion was converted to
solid form by coagulation the polymer from its emulsion using sodium sulphate salt as coagulant aid, then alcoholyzed
the solid polyvinyl acetate in methanol using sodium hydroxide as catalyst, polyvinyl alcohol produced by this method is
a dry, white to yellow powder.
Three affecting variables on the degree of hydrolysis of PVA were studied, these variable are Catalyst to
polymer weight ratio in the range of 0.01 – 0.06, reaction time in the range of 20 – 90 min, and reaction temperature in
the

Phosphorus and dye (direct black) removal for small – scale wastewater applications were investigated using oven dried alum sludge (ODS).The use of alum sludge not only provides a low cost technique but also reduces the hazard and the cost related to the disposal of large amount of alum sludge. Phosphorus and dye removal exceeds 90% for all operating conditions applied in the research.
The residuals generated during the treatment of wastewater were further tested to study the possibility of aluminum leaching from oven dried alum sludge during the adsorption of phosphorus and dye. These tests observed a reduction in aluminum leaching indicating a lower risk imposed on land and surface water based on disposal options rather than on al