Tin dioxide doped silver oxide thin films with different x content (0, 0.03, 0.05, 0.07) have been prepared by pulse laser deposition technique (PLD) at room temperatures (RT). The effect of doping concentration on the structural and electrical properties of the films were studied. Atomic Force Measurement (AFM) measurements found that the average value of grain size for all films at RT decrease with increasing of AgO content. While an average roughness values increase with increasing x content. The electrical properties of these films were studied with different x content. The D.C conductivity for all films increases with increasing x content. Also, it found that activation energies decrease with increasing of AgO content for all films.

Ag-doped NiO thin films were fabricated by dip coating and subsequently annealed at 373, 473, 573, and 673 K to elucidate the influence of annealing temperature on their structural, morphological, optical, and NO2-sensing characteristics. X-ray diffraction confirmed the formation of polycrystalline Ag/NiO films, with progressively improved crystallinity and larger crystallite size at elevated annealing temperatures. Atomic force microscopy revealed a homogeneous surface morphology with grain growth, with the average grain diameter increasing from 26.40 to 34.2 nm. Optical analysis showed high visible-region transmittance (65–70%) and a gradual reduction in the optical band gap from 2.75 to 2.07 eV with increasing annealing temperature. Ga

Azo derivative ligand[H3L] have been synthesized by the reaction of diazonium salt of p-amino benzoic acid with orcinol in(1:1)mole ratio. The bidente ligand was reacted with the metal ions MnII,FeIIandCrIIIin(2:1)mole ratio via reflux in ethanol using Et3N as a base to give complexes of the general formula: [ M(H2L)2(H2O)x]Cly The synthesized compounds were characterized by spectroscopic methods[ I.R , UV-Vis, A.A and H1 NMR]along with melting point, chloride content and conductivity measurements. The complexes were screend for their in vitro antibacterial activity against one strain of staphylococcus as Gram(+) positive and one strain of pseudomonas as Gram(-) Negative, using the agar diffusion technique.

The 3-aminoacetophenone and 4-aminoantipyrine were used as ‎precursors to prepare new six ligands. The three new ligands (L1,L2 ‎and L3) were synthesis by reacting one mole of 3-aminoacetophenone ‎with one mole of (Acetyl chloride), (benzoyl chloride), (4-‎methoxybenzoyl chloride) and ammonium thiocyanat in acetone as a ‎solvent, they are:-‎ L1 (AAA) =[N-(3-acetylphenylcarbamothioyl)acetamide]‎ L2 (BAA) =[N-(3-acetylphenylcarbamothioyl)benzamide]‎ L3 (MAA) =[N-(3-acetylphenylcarbamothioyl)-4-methoxy benzamide]‎ Also three new derivatives of 4-aminoantipyrine were synthesis by ‎reacting one mole of 4-aminoantipyrine with one mole of (Acetyl ‎chloride), (benzoyl chloride), (4-methoxybenzoyl chloride) and ‎ammonium thio

Zinc Oxide nanoparticles were prepared using pulsed laser ablation process from a pure zinc metal placed inside a liquid environment. The latter is composed of acetyltrimethylammonium bromide (CTAB) of 10−3 molarity and distilled water. A Ti:Sapphire laser of 800 nm wavelength, 1 kHz pulse repetition rate, 130 fs pulse duration is used at three values of pulse energies of 0.05 mJ, 1.11 mJ and 1.15 mJ. The evaluation of the optical properties for the obtained suspension was applied through ultraviolet–visible absorption spectroscopy test (UV/VIS). The result showed peak wavelengths at 210 nm, 211 nm and 213 nm for the three used pulse energies 0.05 mJ, 1.11 mJ and 1.15 mJ respectively. This indicates a blue shift,

The applications of hot plasma are many and numerous applications require high values of the temperature of the electrons within the plasma region. Improving electron temperature values is one of the important processes for using this specification in plasma for being adopted in several modern applications such as nuclear fusion, plating operations and in industrial applications. In this work, theoretical computations were performed to enhance electron temperature under dense homogeneous plasma. The effect of   power and duration time of pulsed Nd:YAG laser   was studied on the heating of   plasmas  by inverse bremsstrahlung  for  several values for the electron density ratio. There results for these ca

Applications of superconductor compounds were considered as modern and important topics, especially these which are exposures to one of the nuclear radiation kinds. So, we gone to investigate the influence of fast neutrons irradiation on electrical and structural characteristics of HgxSb1-xBa2Ca2Cu3O8+δ superconducting compound at (x = 0.7) in ratio. The superconducting specimens were synthesized using solid state technique. Specimens were exposure to the nuclear radiation using fast neutrons with doses (0, 9.06 x1010, 15.3 x 1010 and 18.17 x 1010) n/cm2 respectively. Electrical and X-ray diffraction properties of superconductor specimens before and after irradiation were investigated under standard conditions. Results of X-ray diffraction