The compounds 3-[4̄-(4˭-methoxybenzoyloxy) benzylideneamino]-2-thioxo-imidazolidine-4-one(3)aand 4-(1-(5-oxo- 2-thioxoimidazolidin-1-ylimino)ethyl)phenyl acetate(3)b were prepared from the reaction of aromatic aldehyde or ketone(1)a,bwith thiosemicarbazide to give aryl thiosemicarbazones(2)a,b ,followed by cyclization with ethylchloroacetate in the presence of fused sodium acetate. Treatment the compounds(3)a,bwith 4- hydroxybenzenediazoniumchloride yielded the correspondings4-((4-((4-hydroxyphenyl)diazenyl)-5-oxo-2- thioxoimidazolidin-1-ylimino)methyl)phenyl 4-methoxybenzoate(4)aand4-(1-(4-((4-hydroxyphenyl)diazenyl)-5-oxo-2- thioxoimidazolidin-1-ylimino)ethyl)phenyl acetate(4)b.The new 2-thioxo-imidazolidin-4-one with esters (5-7)a,b sy

The compounds 3-[4̄-(4˭-methoxybenzoyloxy) benzylideneamino]-2-thioxo-imidazolidine-4-one(3)aand 4-(1-(5-oxo- 2-thioxoimidazolidin-1-ylimino)ethyl)phenyl acetate(3)b were prepared from the reaction of aromatic aldehyde or ketone(1)a,bwith thiosemicarbazide to give aryl thiosemicarbazones(2)a,b ,followed by cyclization with ethylchloroacetate in the presence of fused sodium acetate. Treatment the compounds(3)a,bwith 4- hydroxybenzenediazoniumchloride yielded the correspondings4-((4-((4-hydroxyphenyl)diazenyl)-5-oxo-2- thioxoimidazolidin-1-ylimino)methyl)phenyl 4-methoxybenzoate(4)aand4-(1-(4-((4-hydroxyphenyl)diazenyl)-5-oxo-2- thioxoimidazolidin-1-ylimino)ethyl)phenyl acetate(4)b.The new 2-thioxo-imidazolidin-4-one with esters (5-7)a,b sy

The effect of micro-and nano silica particles (silica SiO2 (100 μm), Fused silica (12nm)) on some mechanical properties of epoxy resin was investigated (Young's modulus, Flexural strength). The micro-and nano composites were prepared by using three steps process with different volume fraction of micro-and nano particles (1, 2, 3, 4, 5, 7, 10, 15, and 20 vol. %). Flexural strength and Young's modulus of nano composites were increased at low volume fraction (max. enhancement at 4 vol.% ). However at higher volume fraction both Young's modulus and flexural strength decrease. Moreover, above, the mechanical properties are enhanced more than that of neat epoxy resin. The flexural strength decreases with increasing the volume fraction of micr

This study involves the synthesis of a new class of silicon polymers, designated as P1-P7, derived from dichlorodimethylsilane (DCDMS) in combination with various organic compounds (Schiff bases prepared from different amines and appropriate aldehydes or ketones) [I-V] through condensation polymerization. The structures of all monomers and polymers were characterization by FTIR and 1HNMR spectroscopy (for some polymers). The results of thermogravimetric analysis (TGA) and differential scanning calorimetry DSC test show stable thermal behaviour. Polymers with a higher concentration of aromatic rings in their repeating structural units exhibited a higher temperature for weight loss, indicating increased thermal stability. Thermal meas

This study involves the synthesis of a new class of silicon polymers, designated as P1-P7, derived from dichlorodimethylsilane (DCDMS) in combination with various organic compounds (Schiff bases prepared from different amines and appropriate aldehydes or ketones) [I-V] through condensation polymerization. The structures of all monomers and polymers were characterization by FTIR and 1HNMR spectroscopy (for some polymers). The results of thermogravimetric analysis (TGA) and differential scanning calorimetry DSC test show stable thermal behaviour. Polymers with a higher concentration of aromatic rings in their repeating structural units exhibited a higher temperature for weight loss, indicating increased thermal stability. Thermal meas

Thin films were prepared from poly Berrol way Ketrrukemaaih pole of platinum concentrations both Albaarol and salt in the electrolytic Alastontrel using positive effort of 7 volts on the pole and the electrical wiring of the membrane record