In this research is to study the influence of the aging heat treatment on the pitting corrosion resistance of martensitic stainless steel (MSS), where a number of specimens from martensitic stainless steel were subjected to solution treatment at 1100 ^oC for one hour followed by water quenching then aging in the temperatures range (500-750) ^oC for different holding times (1,5,10,15&20) hr. Accelerated chemical corrosion test and immersion chemical corrosion test were performed on samples after heat treatment. The results of the research showed that the pitting corrosion resistance is significantly affected by the aging temperature. Where found that the aging samples at a temperature of 500 °C have the highest ra

The ratio of draft tube to reactor diameters is of decisive importance for the operation behavior of air lift loop reactors. The influence of draft tube geometry was investigated with respect to oxygen mass transfer and mixing time. The diameter ratio was varied between 0.33 and 0.80. The measurements were performed in two loop reactors with liquid capacities of 11.775 and 26.49 liters using aqueous with solutions of different coalescence behavior. The results show that there is no single diameter ratio which would produce most favorable conditions for the two process parameters. With respect to the more important requirements of aerobic cultures, i.e high oxygen mass transfer and efficient mixing, a diameter ratio between 0.5 and 0.6 is

Cinnamon plant is considered one of important medicinal plants because it is rich with many active compounds. This research is aimed to study possible effects of extract in culture media of Gardenia jasmenoides. Alcoholic extract was prepared from the bark of cinnamon at different concentrations (0.0, 1.0, 2.0) mg/L, then added to culture media to notice the effect of these concentrations on the growth and development of tissues and organs of Gardenia jasmenoides Ellis in vitro. Results showed the positive effect of increasing callus fresh weight and shoot proliferation from single nodes with presence of plant regulators, 5.0 mg/L Naphthalene acetic acid (NAA) and 3.0 mg/L Benzyl adenine (BA). Results showed that extract has a slight eff

Background/Aim: The timing of a tooth's eruption can be affected by a variety of factors. The nutritional status has an impact on the development of a child's body. The purpose of the study was to analyse the number of children aged 6 to 9 in an Iraqi Arab population who had erupted permanent first molars and to examine how nutritional status affected the timing and level of emergence. Methods: A total of 330 boys and girls, in first grade elementary school, made up the sample. First molars that had erupted were noted, along with the level of the eruption. Each child's nutritional status was evaluated by recording their height and weight and body mass index (BMI) value was compared to the 2007 WHO reference. Results: Girls had highe

Copper Zinc Sulphide (Cu0.5Zn0.5S) alloy and thin films were fabricated in a vacuum. Nano crystallized (CZS) film with thick 450±20 nm was deposit at substrates glasses using thermal evaporation technique below ~ 2 × 10− 5 mbar vacuum to investigated the films structural, morphological and optical properties depended on annealing temperatures ( as-deposited, 423, 523 and 623) K for one hour. The influences annealed temperature on structurally besides morphologically characteristics on these films were investigated using XRD and AFM respectively. XRD confirms the formation a mixed hexagonal phase of CuS-ZnS in (102) direction with polycrystalline in nature having very fine crystallites size varying from (5.5-13.09) nm. AFM analys

In this study, the upgrading of Iraqi heavy crude oil was achieved utilizing the solvent deasphalting approach (SDA) and enhanced solvent deasphalting (e-SDA) by adding Nanosilica (NS). The NS was synthesized from local sand. The XRD result, referred to as the amorphous phase, has a wide peak at 2Θ= (22 - 23º) The inclusion of hydrogen-bonded silanol groups (Si–O–H) and siloxane groups (Si–O–Si) in the FTIR spectra. The SDA process was handled using n-pentane solvent at various solvent to oil ratios (SOR) (4-16/1ml/g), room and reflux temperature, and 0.5 h mixing time. In the e-SDA process, various fractions of the NS (1–7 wt.%) have been utilized with 61 nm particle size and 560.86 m²/g surface area in the presence of 12 m