Background: Deterioration of maxillofacial silicone properties due to microbial colonization is a common problem and leads to the replacement of the prosthesis. Incorporation of the antimicrobial agent into the silicone could be a solution. The purpose of this study was to evaluate the effect of silver-zinc zeolite addition on some mechanical properties of a maxillofacial silicone (VST-50). Materials and methods: Total 120 specimens were fabricated and divided into 3 groups: 40 specimens for tear strength test, 40 specimens for tensile and percentage of elongation tests and 40 specimens for Shore A hardness and surface roughness. Each group was divided into 4 subgroups according to the amount of zeolite added (0% “control”, 0.5%, 1% and

Zinc Oxide is an indispensable substance in the field of dental treatment. It is used daily and intensively in all governmental and private dental clinics, leading to the disposal of very high concentrations of zinc with waste and eventually in landfill sites as a final destination for solid waste removal. This indicates the urgent need to investigate its behavior upon disposal due to the surrounding conditions. Approximately 4195 g of mixed dental waste samples were collected from (17) healthcare centers in Baghdad Al-Karkh. The leaching behavior of ZnO powder was investigated through batch reactors using makeup dental solid waste samples. The ZnO leaching was tested with 3 conditions; acidic, alkaline, and Ionic Streng

Complexes of the Cr(III), Fe(III), Rh(III), Ru (III), Mo hexagonal valence and Co(II) were prepared using the azo dye 1,1'-(1,3-phenylene bis(diazene-2,1-diyl))bis(2,4,6-trihydroxy-3,1-phenylene))bis(ethan-1-one), which was prepared newly from diazonium salt with 2,4,6-trihydroxyacetophenone, after isolation. The compounds were characterized using proton and carbon nuclear magnetic resonance of the ligand and fine elemental analysis, infrared, ultraviolet-visible, mass measurement, thermogravimetric analysis, differential thermal scanning, metal percentage determination, chlorine content determination, magnetic susceptibility, and molar conductivity. The results showed that the tetra coordinated anionic bond, when linked to metal ions via t

Myrtle plant was washed, dried, and powdered after harvesting to produce a fine powder used in water treatment. An alcoholic extract was created from the myrtle plant using ethanol, which was then analyzed using GC-Mass, Fourier Transform Infrared spectroscopy, and ultraviolet-visible spectroscopy to identify the active components. Zinc nanoparticles were created using alcoholic extract. FT-IR, UV-Vis, SEM, EDX, and TEM were used to characterize zinc nanoparticles. Using a continuous processing procedure, zinc nanoparticles with myrtle extract and powder were employed to clean polluted water containing pesticides and antibiotic. First, 2 g of zinc nanoparticles was mixed with 20 ml of polluted water and the result was (Tetra 44%, Levo 32%),

Zinc oxide (ZnO) nanostructures were synthesized through the hydrothermal method at various conditions growth times (6,7 and 8 hrs.) and a growth temperature (70, 90, and 100 ºC). The prepared ZnO nanostructure samples were described using scanning electron microscopy (SEM) and X-ray diffractometer to distinguish their surface morphologies and crystal structures. The ZnO samples were confirmed to have the same crystal type, with different densities and dimensions (diameter and length). The obtained ZnO nanostructures were used to manufacture gas sensors for NO2 gas detection. Sensing characteristics for the fabricated sensor to NO2 gas were examined at different operating temperatures (180, 200, 220, and 240) ºC with a low gas concentrati