Calcium-Montmorillonite (bentonite) [Ca-MMT] has been prepared via cation exchange reaction using benzalkonium chloride [quaternary ammonium] as a surfactant to produce organoclay which is used to prepare polymer composites. Functionalization of this filler surface is very important factor for achieving good interaction between filler and polymer matrix. Basal spacing and functional groups identification of this organoclay were characterized using X-Ray Diffraction (XRD) and Fourier Transform Infrared (FTIR) spectroscopy respectively.  The (XRD) results showed that the basal spacing of the treated clay (organoclay) with the benzalkonium chloride increased to 15.17213 ⁰A, this represents an increment of about 77.9% in the

The dielectric constant of most polymers is very low; the addition of TiO2 particles into the polymers provides an attractive and promising way to reach a high dielectric constant. Polymer-based materials with a high dielectric constant show great potential for energy storage applications. Four samples were prepared, one of them was polyurethane (PU) and the other were PU with different weight percent (wt %) of TiO2 (0.1, 0.2, 0.3) powder AFM test was used to distinguish the nanoparticles. The result shows that the most shape of these nanoparticles are spherical and the roughness average is 0.798 nm. The dielectric properties were measured for all samples before and after the exposure to the UV radiation. The result illustrates that the

Sheets of Epoxy (EP) resin with addition of TiO2 of grain size (1.5μm, and 50nm) and weight percentage (1%, 3%, and 5%) were prepared. Discs of 20mm diameter and 3mm thickness were cut for dielectric measurements. Dielectric properties (dielectric constant, dispassion factor and electrical conductivity) over the frequency range 102 -106 Hz were measured.
Comparison was made between the effect of micro and nano particles of TiO2 on the dielectric properties of EP composites with different weight percentage. Epoxy composites with micro sized particles of TiO2 were observed to have the better values of dielectric properties.

Schiff base obtained from the reaction (Trimethoprim) with (sodiumpyruvate ) to produce the ligand [NaL], the reaction was carried out in methanol as a solvent under reflux. The prepared ligand [NaL] was characterized by FT-IR, UV-Vis spectroscopy, 1H,13C-NMR spectra, mass spectra, and melting point.A new mixed ligand complexes have been prepared between ( 8- hydroxyquinolone) and the ligand [NaL] withMn(II).Co(II),Ni(II),Cu(II), (Zn(II) ,(Cd(II)and Pd(II). All the complexes were characterized by spectroscopic methods (FT-IR, UV-Vis spectroscopy), chloride content and melting point ,molar conductance and magnetic susceptibility.These measure- ments showed octahedral geometry around(,Mn2+, Co2+, Ni2+, Cu2+, Zn2+ and Cd2+) ions and square pla

Arrested precipitation methode used to synthesize CuInSe2 (CIS) nanocrystals were added to a hot solvent with organic capping ligands to control nanocrystal formation and growth. CIS thin films deposited onto Soda-Lima Glass (SLG) substrate by spray-coat, then selenized in Ar-atmosphere to form CIS thin films. PVs were made with power conversion efficiencies of 0.631% as-deposited and 0.846% after selenization, for Mo coated, under AM 1.5 illuminations. (XRD) and (EDX) it is evident that CIS have chalcopyrite structure as the major phase with a preferred orientation along (112) direction and Cu:In:Se nanocrystals is nearly 1:1:2 atomic ratio.

In this work preparation of antireflection coating with single layer of MgO using pulsed laser deposition (PLD) method which deposit on glass substrate with different thicknesses (90 and 100) nm annealed at temperature 500 K was done.
The optical and structural properties (X-ray diffraction) have been determined. The optical reflectance was computed with the aid of MATLAB over the visible and near infrared region. Results shows that the best result obtained for optical performance of AR'Cs at 700 shots with thickness 90 nm nanostructure single layer AR'Cs and low reflection at wavelength 550 nm.

The present study aimed to investigate the effects of level pH and the growth phases of Coelastrella saipanensis on Chlorophyll a,b, total, and Carotene. The algae were cultured in BG11 media and grown at different pH levels. We measured chlorophyll a, b, total chlorophyll, growth phases, and carotene concentrations. The results showed that at pH 8.5, the measurements of photosynthetic pigments-chlorophyll a, Chlorophyll b, and the total chlorophyll (0.183, 0.268, and 0.433 mg L-1, respectively). The highest values of chlorophyll a (0.185 mg L-1), and b (0.339 mg L-1), and the total chlorophyll (0.492 mg L-1) were recorded in the stationary phase. In addition, the study found that at pH 8.5 and the beginning of the stationary phase,