Advancing the multi-scale performance of asphalt pavements requires innovative binder modifications that address limitations in rutting resistance, fatigue resistance, and durability across the binder, mixture, and structural levels. This study evaluates the performance of asphalt cement, mixtures, and pavement systems modified with a combination of polyethylene (PE) and carbon nanotubes (CNTs). The binder was modified using 4% PE and varying CNT contents (0.5%, 1%, 1.5%, and 2% by weight of the modified binder). Binder performance was assessed through conventional and rheological tests, including penetration, softening point, viscosity, performance grade (PG) evaluation, and master curve analysis. Mixture-level performance was eval

The research aims to measure the economic efficiency and technological change and the total productivity of resources using the parameter and non-parameter methods, for agricultural companies registered in the Iraqi stock exchange, the number of 6 companies for the period from 2005 to 2017 based on the hypothesis that the  agricultural companies do not achieve economic efficiency and does not control the management of its operations, and It may be technically efficient but the size of its operations is not optimal. From non-parametric methods, the data envelope analysis method was used. Using the DEAP program, the Middle East Company achieved the highest average technical and cost efficiency of 0.62 and 0.58, respectively. The Iraq

The importance of this study stems from the importance of preserving the environment and creating a clean sustainable environment from waste and emissions and all the operations of industrial companies in general and cement companies in particular by activating sustainability accounting standards. The research aims to identify and diagnose deviations in violation of sustainability standards by employing the non-renewable resources standard (NR0401) For the construction industries to create a sustainable audit environment, the deductive approach was followed in the theoretical side and the inductive and descriptive approach to the practical side. The most important results of the research were the possibility of applying sustainab

This paper investigated the fatigue life behavior of two composite materials subjected to different times of shot peening (2, 4 and 6 min).The first material prepared from unsaturated polyester with E-glass reinforcement by 33% volume fraction. While, the second one was prepared from unsaturated polyester with aluminum powder by2.5% volume fraction. The experimental results showed that the improvement in endurance limit was obtained (for the first material) at 2, 4 and 6 min shot peening times where the percentage of maximum improvement was 25% at shot peening time of 6 min. While, the endurance limit of the second material decreased at shot peening times of 2, 4 and 6 min where the percentage of maximum reduction was 29 % at shot peenin

ABSTRACT Background: This study aimed to study the effect of some acidic drinks (Vinegars and fresh Orange juice) and energy drinks (Red bull) on surface roughness of three types of bulkfill composite materials: Filtek posterior bulkfill (3M), Sonicfill (Kerr) and Filtek p60 (3M). Materials and Methods: Total number of 120 samples are prepared by using a mold of (12mm diameter and 3mm height), which were divided into three groups forty samples for each group: Group A: Filtek bulkfill posterior composite (3M), Group B: Sonicfill composite (Kerr), Group C: Filtek P60 (3 M) which then divided into four sub- groups (n=10) (1) samples were kept in distilled water as a control group (2) samples were immersed in Redbull (3) samples were immersed

In this study, composite materials consisting of Activated Carbon (AC) and Zeolite were prepared for application in the removal of methylene blue and lead from an aqueous solution. The optimum synthesis method involves the use of metakaolinization and zeolitization, in the presence of activated carbon from kaolin, to form Zeolite. First, Kaolin was thermally activated into amorphous kaolin (metakaolinization); then the resultant metakaolin was attacked by alkaline, transforming it into crystalline zeolite (zeolitization). Using nitrogen adsorption and SEM techniques, the examination and characterization of composite materials confirmed the presence of a homogenous distribution of Zeolite throughout the activated carbon.

Background: Limited data are available on the dimensional stability and surface roughness of ThermoSens, which is a material used in denture processing. This study aimed to measure the vertical teeth changes and surface roughness of ThermoSens dentures prepared using three different investment materials. Materials and methods: For the dimensional changes test, 30 complete maxillary dentures were prepared using different investment methods: group I, dental stone; group II, silicone putty; and group III, a mixture of dental stone and plaster (ratio, 1:1; n = 10 for each group). Four screws were attached to the dentures: two were attached to the buccal surface of the canine and first molar, and the other two were attached in the flange areas o

The Neutron Fermi Age, t, and the neutron slowing down density,   q (r, t) , have been measured for some materials such as Graphite and Iron by using gamma spectrometry system UCS-30 with NaI (Tl) detector. This technique was applied for Graphite and Iron materials by using Indium foils covered by Cadmium and the measurements done at the Indium resonance of 1.46 eV. These materials are exposed to a plane ²⁴¹Am/Be neutron source with recent activity 38 mCi. The measurements of the Fermi Age were found to be t = 297 ± 21 cm² for Graphite, t = 400 ± 28 cm² for Iron. Neutron slowing down density was also calculated depending on the recent experimental t value and distance.