This research paper aimed to quantitively characterize the pore structure of shale reservoirs. Six samples of Silurian shale from the Ahnet basin were selected for nitrogen adsorption-desorption analysis. Experimental findings showed that all the samples are mainly composed of mesopores with slit-like shaped pores, as well as the Barrett-Joyner-Halenda pore volume ranging from 0.014 to 0.046 cm3/ 100 g, where the lowest value has recorded in the AHTT-1 sample, whereas the highest one in AHTT-6, while the rest samples (AHTT-2, AHTT-3, AHTT-4, AHTT-5) have a similar average value of 0.03 cm3/ 100 g. Meanwhile, the surface area and pore size distribution were in the range of 3.8 to 11.1 m2 / g and 1.7 to 40 nm, respectively.

Alginate is one of the natural biopolymers that is widely used for drug formulations, combination of alginate with other polymers, such as gum acacia, pectin, and carrageenan can increase mechanical strength, therefore, can reduce leakage of the encapsulated active pharmaceutical ingredient from the polymer matrix. Interaction of alginate and these polymers can occur via intermolecular hydrogen bonds causing synergism, which is determined from the viscosity of polymer mixture.

Alginate was combined with gum acacia/pectin/carrageenan in different blending ratios (100:0, 75:25, 50:50, 25:75, and 0:100) with and without addition of CaCl₂. The synergism effect is obtained from the design of experimental (DoE), and calculati

Adsorption studies were performed at different initial Tetracycline (TC) and Amoxicillin (AMO) concentration, different biomass dosage and type, contact time, agitation speed, and initial pH.  In the batch mode were investigated. The optimum pH of solutions is 6.5 for TC and 5 for AMO, agitation speed 200 rpm and concentration 50 ppm. The results in FTIR showed that there were -OH and amides (N-H) and other functional groups on the surface of Cladophora and Spirulina algae. The equilibrium isotherm data were modeled with Freundlich, Temkin, and Langmuir isotherm models. The data best fitted with the Langmuir model. The maximal adsorption capacity from the Langmuir model was (9.86, 20. 5 mg/g) for TC and (7.89, 17.4 mg/g) for AMO on

Schiff base N,N'-Bis-(4-dimethylamino-benzylidene)-benzene-1,4-diamine has been synthesized from 4-dimethylaminobenzenaldehyde and benzene-1,4-diamine. The structure of Schiff base was obtained by (C.H.N.) microanalysis, Mass, 1HNMR, FT-IR and UV-Vis spectral methods and thermal analysis. Metal mixed ligand complexes of some metal(II) salts with Schiff base ligand and anthranilic acid were prepared in the molar ratio (1:2:2), (Metal):(SBL)2:(Anthra)2, (SBL)= Schiff base ligand, (Anthra) =anthranilic acid and Metal= Co(II), Ni(II), Cu(II), Zn(II), Cd(II) and Hg(II). The thermal behaviour (TGA) of the complexes was studied. The prepared complexes identified by using mass, thermal analysis, FT.IR and UV-Vis spectrum methods, on otherwise flame

A series of new imides compounds[1-4] were synthesized from reaction of tetrachlorophthalic anhydride or nitro phthalic anhydride or malic anhydride or Succinic anhydride  with  4-amino benzene thiol under fusion conditions. Chloroacetic acid has been added after compounds [1-4] reacted with distilled H2O and Na2CO3, producing compounds [5-8]. In benzene, compounds [5-8] also interacted with the thionyl chloride to produce [9-12]. Poly (vinyl alcohol) was chemically modified by reacting PVA with compounds [9-12] and dimethyl formamide to produce compounds [13-16]. Iron oxide nanoparticles (IONPs) are mixed with modified PVA [13-16] to create nanocomposites [17-20]. Spectral and analytical data from synthesized compounds, such as 1

A series of new imides compounds[1-4] were synthesized from reaction of tetrachlorophthalic anhydride or nitro phthalic anhydride or malic anhydride or Succinic anhydride with 4-amino benzene thiol under fusion conditions. Chloroacetic acid has been added after compounds [1-4] reacted with distilled H2O and Na2CO3, producing compounds [5-8]. In benzene, compounds [5-8] also interacted with the thionyl chloride to produce [9-12]. Poly (vinyl alcohol) was chemically modified by reacting PVA with compounds [9-12] and dimethyl formamide to produce compounds [13-16]. Iron oxide nanoparticles (IONPs) are mixed with modified PVA [13-16] to create nanocomposites [17-20]. Spectral and analytical data from synthesized compounds, such as 1H-NMR, FTI

Diacerein (DCN) is a semi-synthetic anthraquinone derivative of Rhein that is indicated for the management of osteoarthritis. Diacerein exhibits poor dissolution in the GIT fluids and suffers from low bioavailability upon oral administration in addition to the laxative effect of Rhein metabolites. The aim of the present study was to develop novasomal vesicles with optimized entrapment efficiency and size to serve as a carrier for transdermal delivery of diacerein. Novasomal vesicles were prepared by thin film hydration method thin film hydration. The prepared vesicles were optimized utilizing different surfactant to cholesterol molar ration, sonication type, different sonication times and varying fatty acid level. The prepared vesicles were

Nanocomposites of polymer material based on CdS as filler
material and poly methyl methacrylate (PMMA) as host matrix have
been fabricated by chemical spray pyrolysis method on glass
substrate. CdS particles synthesized by co-precipitation route using
cadimium chloride and thioacetamide as starting materials and
ammonium hydroxide as precipitating agent. The structure is
examined by X-ray diffraction (XRD), the resultant film has
amorphous structure. The optical energy gap is found to be (4.5,
4.06) eV before and after CdS addition, respectively. Electrical
activation energy for CdS/PMMA has two regions with values of
0.079 and 0.433 eV.

γ-Al2O3–NPs were synthesized by a green synthesis process based on Boswellia carterii resin extract and aluminum sulphate in an alkaline medium. Boswellia carterii resin extract is a significant reducing and stabilizing agent for synthesizing γ-Al2O3–NPs.Several techniques, including Fourier–transform infrared (FT-IR), UV–visible spectroscopy, x-ray diffraction, electron microscopy (XRD), energy dispersive x-ray (EDX), scanning electron microscopy (SEM), Transmission electron microscopy (TEM), and atomic force microscopy (AFM), were utilized to investigate the final product. XRD and SEM confirmed a plate-like crystalline structure with an average size of 17.5 nm. FT-IR analysis identified aluminum oxide stretching vibrations (655,