The electrospun nanofibers membranes (ENMs) have gained great attention due to their superior performance. However, the low mechanical strength of ENMs, such as the rigidity and low strength, limits their applications in many aspects which need adequate strength, such as water filtration. This work investigates the impact of electrospinning parameters on the properties of ENMs fabricated from polyacrylonitrile (PAN) solved in N, N-Dimethylformamide (DMF). The studied electrospinning parameters were polymer concentration, solution flow rate, collector rotating speed, and the distance between the needle and collector. The fabricated ENMs were characterized using scanning electron microscopy (SEM) to understand the surface morphology and es

Purpose Heavy metals are toxic pollutants released into the environment as a result of different industrial activities. Biosorption of heavy metals from aqueous solutions is a new technology for the treatment of industrial wastewater. The aim of the present research is to highlight the basic biosorption theory to heavy metal removal. Materials and methods Heterogeneous cultures mostly dried anaerobic bacteria, yeast (fungi), and protozoa were used as low-cost material to remove metallic cations Pb(II), Cr(III), and Cd(II) from synthetic wastewater. Competitive biosorption of these metals was studied. Results The main biosorption mechanisms were complexation and physical adsorption onto natural active functional groups. It is observed that

Thin films of Nb2O5 have been successfully deposited using the DC reactive magnetron sputtering technique to manufacture NH3 gas sensors. These films have been annealed at a high temperature of 800°C for one hour. The assessment of the Nb2O5 thin films structural, morphological, and electrical characteristics was carried out using several methods such as X-ray diffraction (XRD), atomic force microscopy (AFM), energy-dispersive X-ray spectroscopy (EDS), Hall effect measurements, and sensitivity assessments. The XRD analysis confirms the polycrystalline composition of the Nb2O5 thin films with a hexagonal crystal structure. Furthermore, the sensitivity, response time, and recovery time of the gas sensor were evaluated for the Nb2O5 thin film

In this work the effect of annealing temperature on the structure and the electrical properties of Bi thin films was studied, the Bi films were deposited on glass substrates at room temperature by thermal evaporation technique with thickness (0.4 µm) and rate of deposition equal to 6.66Å/sec, all samples are annealed in a vacuum for one hour. The X-ray diffraction analysis shows that the prepared samples are polycrystalline and it exhibits hexagonal structure. The electrical properties of these films were studied with different annealing temperatures, the d.c conductivity for films decreases from 16.42 ? 10-2 at 343K to 10.11?10-2 (?.cm)-1 at 363K. The electrical activation energies Ea1 and Ea2 increase from 0.031 to 0.049eV and

Schiff bases (Sh1-Sh3) have been synthesized (p-aminophenol) was condensed with different aromatic aldehyde in ethanol inthe presence of glacial acetic acid as catalyst. These Schiff bases on treatment with monochloroacetyl choride gave 3-chloro-1-(4-hydroxyphenyl)-4-(substituted)azetidin-2-one(Az4-Az6), with αmercaptoacetic acid gave 3-(4-hydroxyphenyl)-2-( substituted)thiazolidin-4-one (Th7-Th9) and with anthranilic acid gave 3-(4-hydroxyphenyl)-2(substituted)-2,3-dihydroquinazolin-4(1H)-one (Qu10-Qu12). The purity of the derivatives was confirmed by TLC. The some compoundsidentify by (FT-IR and1H, 13C-NMR) data. Some of derivatives were evaluated activity against several microbesto determine ability to inhibit bacterial in some h

Samples of Oxytricha falax were collected from Tigris River by 55µ. mesh net. Culturing of O. falax were cultivated in specific conditions (DO 3-5mg/l.; W.Temp. 24±1ºC; pH: 6.8-7.5).The effect of various furfural concentration 0, 20, 40, 80,100 and 124 ppm and toluene concentration 0, 15, 30, 34.2, 34.5 and 35 ppm after two periods of treatment (24 and 48 hr.) on the physiological parameters of O. falax ciliate were observed. This study showed that the lethal concentration of furfural was 124ppm and 80ppm after 24hr. and 48hr. from treatment which killed all the individual community respectively. Furthermore the treatment of O. falax individuals with different concentrations of toluene indicated that 34.5 ppm of it caused disappearance o

The influence of silver doped n-type polycrystalline CdTe film with thickness of 200 nm and rate deposition of 0.3 nm.s -1 prepared under high vacuum using thermal co-evaporation technique on its some structural and electrical properties was reported. The X- ray analysis showed that all samples are polycrystalline and have the cubic zinc blend structure with preferential orientation in the [111] direction. Films doping with impurity percentages (2, 3, and 4) %Ag lead to a significant increase in the carrier concentration, so it is found to change from 23.493 108 cm -3 to 59.297 108 cm -3 for pure and doped CdTe thin films with 4%Ag respectively. But films doping with impurity percentages above lead to a significant decrease in the electrica