Background: acrylic resin denture base consider a common denture base material for its acceptable cost, aesthetic and easy processing but still has disadvantages including easy of fracture and low impact strength. Material and method: The experimental group was prepared by addition of 15% phosphoric acid 2-hydroxyethyl methacrylate ester (PA2HEME) with polymethyl methacrylate monomer; the experimental groups was compared with the control one. The specimens were prepared according to ADA specification No. 12 with dimension 65 mm x 10 mm x2.5 mm (length x width x thickness respectively). The prepared specimens were tested by three-point flexural strength utilizing Instron Universal Testing Machine (WDW, Layree Technology Co.), Shore D hard

Tight reservoirs have attracted the interest of the oil industry in recent years according to its significant impact on the global oil product. Several challenges are present when producing from these reservoirs due to its low to extra low permeability and very narrow pore throat radius. Development strategy selection for these reservoirs such as horizontal well placement, hydraulic fracture design, well completion, and smart production program, wellbore stability all need accurate characterizations of geomechanical parameters for these reservoirs. Geomechanical properties, including uniaxial compressive strength (UCS), static Young’s modulus (Es), and Poisson’s ratio (υs), were measured experimentally using both static and dynamic met

4, 4s (pyridine 2, 6 diylbis (1, 3, 4 oxadiazole 5, 2 diyl)) bisphenol monomer (3) was synthesized from cyclization of Ns2, Ns6 bis (4 hydroxybenzylidene) pyridine 2, 6 dicarbohydrazide (2) in the presence of bromine in glacialacetic acid. Newly five polymers (P1P5) were synthesized from reaction bis 1, 3, 4 oxadiazole bisphenolmonomer with five different di acid chloride. The antibacterial activity of the synthesized polymers was screened against gram positive and gram negative bacteria. Polymers P4 and P5 exhibited significant antibacterial against all microorganisms, as well these polymers showed highest antifungal activity.

In order to understand the effect of the number of piles (N), the history response of dynamic pile load in piled raft system and deflection time history of piled raft under repeated impact load applied on the center of piled raft resting on loose sand, laboratory model tests were conducted on small-scale models. The results of experimental work are found to be dynamic load increase with increase height of drop, the measured repeated dynamic load time history on the center of piled raft was close approximately to three a half sine wave shape with small duration in about (0.015 Sec). The maximum peak of impact loads occurs in pile and deflection time history occur after at the time of the peak repeated impact loads, dynamic pile load

This research focuses on improving the photoelectrochemical performance of binary heterostructure Ag2S/ZnO NRs/ITO by manipulating synthesis conditions, particularly the concentrations of sliver nitrate AgNO3 and thiourea CS(NH2)2. The photoelectrochemical performance of Ag2S/ZnO nanorods on indium tin oxide (ITO) nanocomposite was compared to pristine ZnO NRs/ITO photoanode. The hydrothermal technique, an eco-friendly, low-cost method, was used to successfully produce Ag2S/ZnO NRs at different concentrations of AgNO3 and CS(NH2)2. The obtained thin films were characterized using field emission scanning electron microscopy (FESEM), energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), ultraviolet-visible spectroscopy

compound [1] was formed from the reaction of benzoin and benzaldehyde in the presence of ammonia, which was reacted with sodium hydride in DMF to obtain imidazole salt. This salt was reacted with adipoyl chloride to give compound [2]. Acid hydrazide derivative [3] was obtained from the reaction of compound [2] with hydrazine hydrate. After that Shiff bases [4-9] have been synthesized from the reaction of compound [3] with different aromatic aldehydes. These new formed compounds were diagnosed by 13C-NMR, 1H-NMR for some of them (in Ahl-Albate University in Jordan) and FT-IR spectroscopy (In Baghdad University). All of the prepared products have been studied their biological activities toward two kinds of bacteria. These products show

This effort is related to describe and assess the performance of the Iraqi cement sample planned for oil well-cementing jobs in Iraq. In this paper, major cementing properties which are thickening time, compressive strength, and free water in addition to the rheological properties and filtration of cement slurry underneath definite circumstances are experimentally tested. The consequences point to that the Iraqi cement after special additives encounter the requests of the API standards and can consequently is used in cementing jobs for oil wells. At this research, there is a comparative investigation established on experimental work on the effectiveness of some additives that considered as waste materials which are silica fume, bauxite,