This study was conducted to evaluate the efficacy of Saccharomyces cerevesiae as a growth promoting agent in tomato. Soaking the seeds in yeast suspension at 5 g/L for 12h increased germination percentage, root length, root fresh and dry weight, plant height, foliage fresh and dry weight, attained 88.5% ; 8.1 cm ; 84.3 mg ; 7.03 mg ; 10.75 cm ; 839 mg and 37.75 mg compared with 80% ; 5.33 cm ; 39 mg ; 4.8 mg ; 7.35 cm ; 608 mg and 25.5 mg in seedlings grown from non treated seeds respectively. Similar results were obtained with seedling from seeds soaked in S. cerevesiae filtrate for 12 hrs. with values of 77.5% ; 6.875 cm ; 91.5 mg ; 7.5 mg ; 9.5 cm ; 777 mg and 40.35 mg compared to 66% ; 5.8 cm ; 57.7 mg ; 5.03 mg ; 5.9 cm ; 493 mg

Ceramic coating compose from a ceramic mixture (MgO, Al₂O₃) and metall (Al-Ni) were produced by Thermal Spray Technique. The mixed ratio of used materials Al:Ni (50%) and 40% of Al₂O₃ and 10% MgO. This mixture was spray on a stainless steel substrate of type (316 L) by using thermal spray with flame method and at spraying distances (8, 12, 16 and 20) cm, then the prepared films were treated by laser and thermal treatment. After that performing a hardness and adhesion tests were eximined. The present study shows that the best value of the thermal treatment is 1000 ℃ for 30 mint; the optimum spray distance is 12 cm and most suitable laser is 500 mJ where the microscopic and mechanical character

CdSe alloy has been prepared successfully from its high purity elements. Thin films of this alloy with different thicknesses (300,700)nm have been grown on glass substrates at room temperature under very low pressure (10-5)Torr with rate of deposition (1.7)nm/sec by thermal evaporation technique, after that these thin films have been heat treated under low pressure (10-2)Torr at (473,673)K for one hour. X-ray patterns showed that both CdSe alloy and thin films are polycrystalline and have the hexagonal structure with preferential orientation in the [100] and [002] direction respectively. The optical measurements indicated that CdSe thin films have allowed direct optical energy band gap, and it increases from (1.77- 1.84) eV and from

Foliar application and seed soaking has been used as a means of supplying supplemental doses of nutrients, plant hormones, stimulants, and organic components. the effects of these applications have included yield increases, and improved drought tolerance, and enhanced crop quality, so A field experiment was carried out during spring seasons in 2019 and 2020 for styding Seed soaking and Foliar Application of Ascorbic acid, Citric acid and Humic acid on Growth, Yield and Active Components IN Maize. Randomized complete block design in split plots arrangement was used with three replicates. Main-plots were for seeds soaking with ascorbic, citric (100 mg l-1) frequently and humic at (1 ml l-1). Sub-plots were for vegetative parts nutrition with

There were many ideas and opinions on the linkage between growth and economic reform  in both developed and developing countries. The relationship is, of course, existed. Therefore, this research comes to analyses it in the Iraqi economy. This study is based on a hypothesis that the economic reformation in Iraq leads to lag level of growth with the of high rates of inflation. However, the study is designed to be included five sections. It found a positive relationship between the economic reformation and slowing of economic growth, in which the specified hypothesis is not fit to the economic reality in Iraq after 2003                  &

In this work, the effect of ceramic coating on performance, exhaust gas temperature and gases emissions of diesel engine operated on diesel fuel and biodiesel blends was investigated. A conventional four stroke, direct injected, single cylinder, diesel engine was tested at constant speed and at different load conditions using diesel fuel and biodiesel blends. The inlet and exhaust valves, the head of piston and cylinder head of the engine were coated by ceramic materials. Ceramic layers were made of (210-240) μm of Al2O3 and (30-60) μm of 4NiCr5Al as a bond coat for inlet and exhaust valves and (350-400) μm of YSZ and (50-100) μm of 4NiCr5Al as a bond coat for head of piston and (280-320) μm of Sic and (40-80) μm of 4NiCr5Al as a b

The Bi2Se3 compound was synthesis by fusing initial compounds consisting of
extra pure elements in stoichiometric ratio from elements compound, charged inside
quartz ampoule. The crystal growth of Bi2Se3 carried out using Brighaman technique
process from melting f (Bi+Se ) at temperature of 810 ºC for about 48 hrs. Single crystal
of Bi2Se3 has been grown in direction (211) after slow cooling on account of heat
gradient to zone furnaces at cooling rate (1-3) C/hr. The structure study of the compound
was determined by x-ray diffraction technique, which it has bismuthinite structure and
orthorhombic unit cell with lattice parameters of a=10.2678 Å, b=11.2392 Å and
c=5.1737 Å

A factorial experiment was applied with four replicates on rosemary plants (Rosmarinus officinalis L.) grown in pots inside the glasshouse of the Department of Biology, College of Science, Salahaddin University, Erbil, Iraq, during April, 2019 to July, 2020, to determine the effects of soil moisture content ( SM1: 100% and SM2: 60% field capacity), nitrogen fertilizer (N1: 100, N2: 200 and N3: 300kg/hectare), and magnesium fertilizer (Mg1: 0.0, Mg2: 30 and Mg3: 60kg/hectare) and their interactions on some growth characteristics  and essential oil content of rosemary plants. Two cuttings were taken from rosemary shoots (on March, 2020 and July, 2020) after 12 and 15 months of planting respectively. Results showed that cutting 1:

The effect of some environmental factors in the loss rate for high weights virgins are full to the screwworm fly of the ancient world and included temperatures 15,20,25,30,35,40 study showed that the rate of loss in weight virgins advanced to full participants at a temperature of 15 C while notgets evolution

The aim of this work is studying the binary system ??'??? Ni?)with two ratios (y=36,80) by using casting method for preparing the samples.Magnetic and Mechanical properties have been studidt different httrea^nttem^rature.All the alloys were found a ferromagnetic behavior and sensitive to the heat treatment. Best properties were found at the heat treatment 1100 C°.A significant different results were found above 1100C° for lower magnetic and mechanical values. This is possibly due to the change on the degree of magnetic moment orders, in which most of the moments are started to remove from coupled ferromagnetically.?