Every so often, a confluence of novel technologies emerges that radically transforms every aspect of the industry, the global economy, and finally, the way we live. These sharp leaps of human ingenuity are known as industrial revolutions, and we are currently in the midst of the fourth such revolution, coined Industry 4.0 by the World Economic Forum. Building on their guideline set of technologies that encompass Industry 4.0, we present a full set of pillar technologies on which Industry 4.0 project portfolio management rests as well as the foundation technologies that support these pillars. A complete model of an Industry 4.0 factory which relies on these pillar technologies is presented. The full set of pillars encompasses cyberph

Twenty five samples out of sixty wound swabs taken from burn patients were identified as P. aeruginosabacteria by conventional methods. Antibiotics susceptibility tests were performed against thirteen antibiotics. P. aeruginosa samples were treated with 0.5 mg/ml of Safranin O solution then irradiated with 532nm Q-switched Nd:YAG laser at four energy densities (0.324, 0.704, 1.380, and 1.831 J/cm2) for different times of 5, 8 and 11 minutes with 5Hz repetition rate. The viability, susceptibility to antibiotic and production of pyocyanin were determined before and after irradiation. The results showed that the number of CFU/ml of P. aeruginosa decreased with increasing the dose of irradiation. Complete killing of cells was observed at 1.8

Background: Thermocycling simulates the temperature dynamics in the oral environment. This in vitro study done to measure and compare the effect of thermocycling on the shear bond strength of stainless steel and sapphire brackets bonded to human enamel teeth using light cured orthodontic adhesive and debonded at various time, and to measure adhesive remnant index after debonding. Materials and Methods: one-hundred-twenty extracted upper first premolars for orthodontic reason were used in this study; depending on weather thermocycled or not, the sample was divided into two main groups, then within each group 30 teeth were used for stainless-steel brackets (Bionic®) and for sapphire brackets (Pure®). Both groups were subdivided into three

The artificial silk (Rayon) was produced from the fronds of date palms which was taken from date palm trees (type Al-Zahdi) from the Iraqi gardens. Two main parts of the frond, namely leaves and stalks were used in this study to produce rayon. The palm fronds were converted into a powder of 90-180 micrometers. Major steps were used to produce rayon; delignification, bleaching and finally dissolution. Modified organosolv method which uses organic solvent method was applied to remove high lignin content. Three variables were studied in the delignification process: temperature, the ratio of ethanol to water and digestion time. The results showed that the best percent of lignin removal was (97%) which occured at; digestion time (80 minutes), te

The 4-(?-bromo acetyl)-4?-toluene sulfonanilide (2) was used as key intermediate to synthesize new heterocyclic compounds. This bromo compound was synthesized via sulfonation of amino group of p-amino acetophenone using Hinsburg method with 4-toluene sulfonyl chloride to form 4-acetyl-4?-toluene sulfonanilide (1) which is used as a starting material in this work. This compound was brominated to yield compound (2) which is used as a precursor to synthesize new five and seven membered heterocyclic compounds such as substituted 1,3-oxazoles (3,4), 1,3-thiazole derivatives (5-7), thiourea compounds (8a,b), 1,3-Thiazoline-2-thione compounds (9a-f) and 1,2,5-triazepine compounds (11a-d). The synthesized compounds were identified depending u

The current research was conducted to report the synthesis of alumina powder from Iraqi kaolin. The kaolin was transformed to metakaolin by calcinations at temperature 800 °C for three hours. Then the calcined kaolin was treated with (1.5 M) from H2SO4 for 6 hours to form Al2(SO4)3.12H2O solution. The precipitate was dried at 80oC for 10 hours and calcinations at different temperatures for two hours. The samples which result was characterized by X–Ray diffraction (XRD) and X–Ray fluorescence (XRF). The results indicate to the crystalline hydrate aluminum sulfate for the sample that be as – synthesis and when calcinations at 600 oC transformed into aluminum sulfate phase. The phases of alumina which we obtain consisted of a gamma a

Background: Appreciation of the crucial role of risk factors in the development of coronary artery disease (CAD) is one of the most significant advances in the understanding of this important disease. Extensive epidemiological research has established cigarette smoking, diabetes, hyperlipidemia, and hypertension as independent risk factors for CADObjective: To determine the prevalence of the 4 conventional risk factors(cigarette smoking, diabetes, hyperlipidemia, and hypertension) among patients with CAD and to determine the correlation of Thrombolysis in Myocardial Infarction (TIMI) risk score with the extent of coronary artery disease (CAD) in patients with unstable angina /non ST elevation myocardial infarction (UA/NSTEMI).Methods: We