A hierarchically porous structured zeolite composite was synthesized from NaX zeolite supported on carbonaceous porous material produced by thermal treatment for plum stones which is an agro-waste. This kind of inorganic-organic composite has an improved performance because bulky molecules can easily access the micropores due to the short diffusion path to the active sites which means a higher diffusion rate. The composite was prepared using a green synthesis method, including an eco-friendly polymer to attach NaX zeolite on the carbon surface by phase inversion. The synthesized composite was characterized using X-ray diffraction spectrometry, Fourier transforms infrared spectroscopy, field emission scanning electron microscopy, energy d

The influence of pre- shot peening and welding parameters on mechanical and metallurgical properties of dissimilar and similar aluminum alloys AA2024-T3 and AA6061-T6 joints using friction stir welding have been studied. In this work, numbers of plates were equipped from sheet alloys in dimensions (150*50*6) mm then some of them were exposed to shot peening process before friction stir welding using steel ball having diameter 1.25 mm for period of 15 minutes. FSW joints were manufactured from plates at three welding speeds (28, 40, 56 mm/min) and welding speed 40mm/min was chosen at a rotating speed of 1400 rpm for welding the dissimilar pre- shot plates. Tow joints were made at rotational speed of 1000 rpm and welding speed of 40m/min f

The rise of antibiotic-resistant bacteria necessitates the exploration of novel antimicrobial agents. Yttrium oxide nanoparticles (Y₂O₃) have shown potential due to their unique physicochemical properties and antibacterial activities against various pathogens. This study investigates the cytotoxic and antibacterial effects of Y₂O₃ nanoparticles against Serratia fonticuli and Citrobacter koseri, bacteria isolated from cholangitis patients. Bacterial strains were isolated from bile specimens and confirmed using standard microbiological techniques. The methods of X-ray diffraction (XRD), (SEM), and Frequency transform-infrared spectroscopic (FT-IR) were used to characterize YO₃ particles. Using a microdilution technique, the minimum

This study was designed to investigate the hypoglycemic and hypolipidemic activity of aqueous green tea (GT) extract in normal and alloxan-induced diabetic rats. Forty adult male albino rats weighing 180-200 g were divided into four groups of 10 rats each: The first group was served as control; the second group was treated with GT (250 mg/kg b.w); the third group was affected by inducing experimental diabetes by intraperitonial injection of alloxan (150 mg/kg b.w); and the fourth group was affected by inducing diabetes and treated with GT (250 mg/kg b.w). Level of blood glucose and lipid profile [total cholesterol (TC), triglycerides (TG), high-density lipoprotein cholesterol (HDL-C), low density lipoprotein cholesterol (LDL-C) and ve

antimicrobial solutions against Coliforms, E. coli O157: H7, yeasts and molds were evaluated by agar well diffusion method. Chitosan (CH) exhibited best antimicrobial activity against the treated microorganisms at concentration of (5%) with contact time for 6hrs at refrigeration temperature (4ÚC), zones of inhibition for (GA) and (CH) for each solution alone ranging from (0 to 10 mm), chitosan solution (CH) exhibited both antibacterial and antifungal activities, Gum Arabic washing solution showed significant antibacterial activity (P < 0.05) against the microorganisms at concentration (15%), without inhibitory effect against E. coli O157:H7 at concentration (10%), in the current study the results confirmed that (15%) (w/v) of GA and 5%

In this work, an enhanced Photonic Crystal Fiber (PCF) based on Surface Plasmon Resonance (SPR) sensor using a sided polished structure for the detection of toxic ions Arsenic in water was designed and implemented. The SPR curve can be obtained by polishing the side of the PCF after coating the Au film on the side of the polished area, the SPR curve can be obtained. The proposed sensor has a clear SPR effect, according to the findings of the experiments. The estimated signal to Noise Ratio (SNR), sensitivity (S), resolution (R), and Figures of merit (FOM) are approaching; the SNR is 0.0125, S is 11.11 μm/RIU, the resolution is 1.8x〖10〗^(-4), and the FOM is 13.88 for Single-mode Fiber- Photonic Crystal Fiber- single mode Fiber (SMF-P

Phenoxathiin was prepared by the reaction of diphenyl ether with sulfur in the presence of anhydrous aluminum chloride. This work comprised the synthesis of new phenoxathiin derivatives containing heterocyclic moieties. These heterocyclic compounds were synthesized in three groups. The first group was made up of 2-(oxoalken-1-yl) phenoxathiin derivatives (3a-3j) obtained from the reaction of 2-acetylphenoxathiin with different aromatic aldehyde in the presence of sodium hydroxide. The other two groups involved compounds produced from the reaction of (3a-3j) with hydrazine hydrate in acetic acid to get 2-(1-acetyl pyrazolin-3-yl) phenoxathiin derivatives (4a-4j), and phenyl hydrazine in the presence of piperidine to afford 2-(1-phenyl pyrazo