The numerical analysis was conducted to studying the influence of length to diameter ratio (L/D) on the behavior of the soil treated with sand columns treated with 8% sodium silicate for both floating and end bearing type by using finite element method (Plaxis 3D Foundation ) for isolated foundation of real dimensions. The analysis’s study indicate that in the floating type the best improvement ratio was achieved at (L/D=8) when using columns with a diameter of (0.5, 0.7), but when using columns with a diameter of 0.3 m, it was noticed that the bearing improvement ratio increases with increasing (L/d). While the results of the analysis for end bearing type show that the higher improvement ratio was achieved at (L/D=4) when using columns w

Many condensed polymers [A1-A7] were prepared via reaction of (Ethylenediaminetetraacetic acid = EDTA), with different prepared imide-diamines by modification [ modification of amino acids and antibiotics (B1- B7)] Imide-diamines were prepared by chlorination of L-amino acids such as [ L-Histidine, L-Alanine, L-Valine, L-Glycine and L-Aspargine ] or selected antibiotics such as [Cephallixine monohydrate and Amoxilline ] with thionyl chloride at 0°C, then reacted with ammonia to obtain imidediamines [B1-B7] . The physical properties of all prepared condensed polymers [A1-A7], new prepared diamines [B1-B7] were studied and characterized by FT -IR spectroscope to certify the structural formulas. The thermal analysis (TGA, DTA) were studied, a

The work includes synthesis and characterization of some new heterocyclic compounds, as flow: The compound (3) (5-(4-chlorophenyl) -2-hydrazinyl-1,3,4-oxadiazole was synthesized by using two methods; the first method includes the direct reaction between hydrazine hydrate 80% and 5-(4-chlorophenyl)-2- (ethylthio) 1,3,4-oxadiazole (1), the second method involves converting 5-(4-chlorophenyl)-1,3,4-oxadiazol-2-amine (2) to diazonium salt then reducing this salt to compound (3) by stannous chloride. Compound (3) was used as starting material for synthesizing several fused heterocyclic compounds. The compound 6-(4- chlorophenyl)[1,2.4] triazolo [3,4,b][1,3,4] oxadiazole-3-(2H) thione (compound 4) was synthesized from the reaction of compo

An experimental program was conducted to determine the residual of composite Steel Beams-Reinforced Concrete (SB-RC) deck floors fabricated from a rolled steel beam topped with a reinforced concrete slab, exposed to high temperatures (fire flame) of 300, 500, and 700ºC for 1 hour, and then allowed to cool down by leaving them in the lab condition to return to the ambient temperature. The burning results showed that, by exposing them to a fire flame of up to 300ºC, no serious permanent deflection occurred. It was also noticed that the specimen recovered 93% of 19.2 mm of the deflection caused by burning. The recovered deflection of burned composite SB-RC deck floor at 500ºC was 40% of 77.9 mm of the deflection caused by burning with a res

Nanofluids are proven to be efficient agents for wettability alteration in subsurface applications including enhanced oil recovery (EOR). Nanofluids can also be used for CO2-storage applications where the CO2-wet rocks can be rendered strongly water-wet, however no attention has been given to this aspect in the past. Thus in this work we presents contact angle (θ) measurements for CO2/brine/calcite system as function of pressure (0.1 MPa, 5 MPa, 10 MPa, 15 MPa, and 20 MPa), temperature (23 °C, 50 °C and 70 °C), and salinity (0, 5, 10, 15, and 20% NaCl) before and after nano-treatment to address the wettability alteration efficiency. Moreover, the effect of treatment pressure and temperature, treatment fluid concentration (SiO2 wt%) and

Background: Polymers are very rarely used in their form. These modifications are carried out in order to improve the properties of polymers.Recently silver have been used successfully as antimicrobial (medical and dental) biomaterials that can prevent caries and infection of implants Purposes: The aim of the present in vitro study is to evaluate the effect of addition of silver nitrate to acrylic resin in different concentrationsthrough several tests part of these are: The effect of this additive on impact strength, transverse strength, and tensile strength of AgNO3 – loaded resin, and to assess any effect of addition of silver nitrate on coloration of acrylic resin. Materials and methods: Different concentrations of silver nitrate