Lithium–Manganese ferrites having the chemical formula (Li0.5-0.5x Mnx Fe2.5-0.5x O4), (0 ≤ x ≤ 1) were prepared by double sintering powder processing. The density of the ferrite increased with Mn content while the porosity was noticed to decrease. The dielectric constant was found to increase at high frequencies more rapidly than the low ones. The dielectric constant found to decrease with Mn content. The decrease in loss factor with frequency agreed with Deby’s type relaxation process. A maximum of dielectric loss factor was observed when the hopping frequency is equal to the external electric field frequency. Manganese substitution reduced the dielectric loss in ferrite. The variation of tanδ with frequency shows a similar na

The current study was conducted to find out the effect of zinc (Zn) on the liver tissue of adult male white mouse, Mus musculus at concentrations (50 and 100 mg/kg/day) and for (30) days.(30) mice were used, divided into three groups of (10) mice, represented by control group, group of (50) mg/kg/day and (100) mg/kg/day. Histopathological changes appeared in the liver of male mice treated with zinc in concentration (50 and 100 mg/kg/day) for 30 days, including deformation and damage to Glisson's capsule, epithelial separation of capsule, in addition to cellular changes represented by hypertrophy of hepatocytes, as seen a swelling necrosis, hypertrophy of nuclei, thickening and degeneration in some hepatocytes, as well as the observed scatte

A total of 50 fertile human hydatid cases {33(66%) females and (34%) males}, obtained from Al-Ramadi public Hospital during the period from December 2003 to July 2004 were examined to study any bacterial infections. The specimens were obtained from hydatid fluid and then cultured on appropriate culture media to distinguish some species of bacteria which resulted in obtaining: Staphylococcus aureus (18%), Pseudomonas aeruginosa(12%), Escherichia coli(6%) and Streptococcus pneumonia (4%). These bacteria were confirmed by isolation from interacyst fluid and blood culture technique. The possible routs of infection may be through blood, biliary ducts and bronchioles .The selectivity permeable of the cyst wall may be absent and that may allow

Polymers have the ability to extract water after they have been added to the mortar or concrete mixture. They provide the absorbed water during hydration functioning as internal water source. Absorption polymers can absorb up to hundred times of their own weight of pure water.This research deals with the use of water absorption polymer balls in concrete and study the volumetric change of these mixes and compared the results with reference mix (without polymers). Samples were cured both in air and in water for the mixes to compare results which show that samples in air behave for expansion while sample in water acted for shrinkage.

Most of the recent works related to the construction industry in Iraq are focused on investigating the validity of local raw materials as alternatives to the imported materials necessary for some practical applications, especially in thermal and sound insulation. This investigation includes the use of limestone dust as partial substitution of cement in combination with foam agent and silica fume to produce sustainable Lightweight Foam Concrete (LWFC). This study consists of two stages. In the first stage, trial mixes were performed to find the optimum dosage of foam agent. Limestone dust was used as a partial replacement for cement. Chemical analysis and fineness showed great similarity with cement. Many concrete mixes were prepared

This study investigates the possibility of using waste plastic as one of the components of expired lead-acid batteries to produce lightweight concrete. Different percentages of lead-acid battery plastic were used in the production of lightweight concrete. The replacements were (70, 80 and 100%) by volume of the fine and coarse aggregate. Results demonstrated that a reduction of approximately 23.6% to 35% in the wet density was observed when replacement of 70% to 100% of the natural aggregate by lead-acid battery plastic. Also, the compressive strength decreased slightly with the increase in plastic content at different curing ages of 7, 28, 60, 90, 120 days. The lowest value of compressive strength was (20.7 MPa) for (wa

Recycled asphalt concrete mixture are prepared, artificially aged and processed in the laboratory to maintain the homogeneity of recycled asphalt concrete mixture gradation, and bitumen content. The loose asphalt concrete mix was subjected to cycle of accelerated aging, (short –term aging) and the compacted mix was subjected to (long -term aging) as per Super-pave procedure. Twenty four Specimens were constructed at optimum asphalt content according to Marshall Method. Recycled mixture was prepared from aged asphalt concrete using recycling agent (soft asphalt cement blended with silica fumes) by (1.5%) weight of mixture as recycling agent content. The effect of recycling agent on aging after recycling process behavior