In this study, polymeric composites were prepared from unsaturated polyester as a base material with glass powder (fluorescent) in different weight ratios (4, 6, 8, 10,and 11%) as a support material and after comparison before and after reinforcement of the prepared composites, an increase was found. In the values ​​of mechanical properties (hardness, compressive strength), the shock resistance values ​​decreased, but an increase in temperature leads to an increase in the values ​​of shock resistance, as well as the values ​​of compressive strength And it reduces the hardness value.

The aim of this paper is to determine the significant levels of some heavy metals such: lead, chromium, nickel and cadmium, were determined. Sources of pollution and their distribution according to presence of elements in the soils over the whole zone of the province of Maysan in southern of Iraq were investigated 36 soil samples from different zones: residential, industrial, commercial, agricultural and main roads, were collected from the soil surface and a depth of 30 cm and analyzed measuring of concentrations for heavy metals by a device ICP-MS technique. The results were compared with global standard levels of these elements in the soil.

Background: In this study we evaluate the effect of plasma treatment (oxygen and argon) gas in two different exposure times on the surface of heat cure and light cure acrylic resin. Materials and method: 100 specimens of heat cure and light cure acrylic resin were fabricated. The measurements of the samples were (75mm, 25mm and 4.5mm) length, width and depth respectively with stopper of 3mm depth. Two types of gas used oxygen and argon in (5,10) min by using (DC-glow discharge plasma device) then we apply cold cure soft lining material, with the help of Instron machine we test the shear stress value. Results: A highly significant effect after argon and oxygen gases treatment in both 5 and 10 min exposure times on shear bond strength to soft

Abstract

     In this investigation, Al₂O₃ nano material of 50nm particles size were added to the 6061 Al aluminium alloy by using the stir casting technique to fabricate the nanocomposite of 10wt% Al₂O₃. The experimental results observed that the addition of 10wt% Al₂O₃ improved the fatigue life and strength of constant and cumulative fatigue. Comparison between the S-N curves behaviour of metal matrix (AA6061) and the nanocomposite 10wt% Al₂O₃ has been made. The comparison revealed that 12.8% enhancement in fatigue strength at 10⁷cycles due to 10wt% nano reinforcement. Also cumulative fatigue l

Modified unsaturated polyester (MUPE) was blended with Cellulose (Cls) and with ethyl cellulose (ECls) at ambient conditions in the presence of ethyl methyl ketone peroxide (EMKP) as hardener. The blends containing different weight percentages (5-25 %) of Cls or ECls. Mechanical properties (impact strength, hardness, and bending) and dielectric constant were determined. The results observed that Cls increases the impact strength, hardness, and dielectric constant and decreases the bending of the MUPS, while ECls causes an increase in the three mechanical behaviours and a decrease in the dielectric constant of the MU-PS.

The aim of this study was to evaluate the effects of local application of bisphosphonate gel and recombinant human bone morphogenic protein 2 gel, on titanium dental implant stability and marginal bone level. Twenty-seven patients with upper and lower missing posterior tooth/teeth were included in the study with a total of 71 implants that were used for rehabilitation. The implants were randomly divided into 4 groups: 3 study groups and 1 control. Group1; local application of bisphosphonate gel, group 2; local application of recombinant human bone morphogenic protein 2 gel, group 3; local application of a mixed formula of both gels. The gel application was immediately preimplant insertion, group 4; implant insertion without application of a