This mini review provides an overview of methods for manufacturing expanded graphite (EGT) and the use of its composites with metal oxides in the field of photodegradation of dyes. Dyes from textile manufacturing represent a significant environmental pollution problem in waterways worldwide, highlighting the need for environmentally friendly and efficient technologies to remove dyes from industrial and local wastewater. Photodegradation technologies offer a low-cost, sustainable solution with minimal secondary pollution. Carbon-based materials, such as expanded graphite, are advantageous in enhancing catalytic activity. Accordingly, this review will explore the different fabrication techniques of expanded graphite and summarize the recent d

The current research consists of four chapters, the first chapter of which is devoted to presenting the research problem, its importance, purpose and limitations as well as a definition of its terms, as the research was limited to knowing the effect of plant decoration in the Kufic script, while the second chapter included the theoretical framework of the research, which consisted of two topics, one of which is the plant decoration, The second relates to the Kufic script and the stages of its formation, development, and intonation. The third chapter includes the research methodology and mechanisms for analyzing the linear panels. The fourth chapter, during which the most important findings of the researcher were presented, are as follows

Dry gas is considered one of the most environmentally friendly sources of energy. As a result, developing an efficient strategy for storing this gas has become essential. In this work, MOF-199 was synthesized and characterized in order to investigate the MOF-199 in dry gas adsorption using a built-in volumetric system (methane, ethane, and propane from Basrah gas company). The MOF-199 (metal organic framework) was synthesized using the solvothermal method at 373K for 24h, and then it was characterized. The dry gas adsorption on MOF-199 was studied under various conditions (adsorbent dosage, contact time, temperature, and pressure). The isothermal adsorption of the dry gas had been studied on MOF-199 using two types of mo

The sensors based on Nickel oxide doped chromic oxide (NiO: Cr2O3) nanoparticals were fabricated using thick-film screen printing of sol-gel grown powders. The structural, morphological investigations were carried out using XRD, AFM, and FESEM. Furthermore, the gas responsivity were evaluated towards the NH3 and NO2 gas. The NiO0.10: Cr2O3 nanoparticles exhibited excellent response of 95 % at 100oC and better selectivity towards NH3 with low response and recovery time as compared to pure Cr2O3 and can stand as reliable sensor element for NH3 sensor related applications.

Nanostructured photodetectors have garnered great attention due to their enriched electronic and optical properties. In this work, we aim to fabricate a high-performance CeO2/Si photodetector by growing a CeO2 nanostructure film on a silicon substrate using the pulsed laser deposition (PLD) technique at different laser energy densities. The impact of laser energy density and the number of pulses on the morphological, optical, and electrical properties was studied. Field emission scanning electron microscopy (FESEM) results show that the CeO2 film has a spherical grain morphology with an average grain size ranging from 33 to 54 nm, depending on the laser energy density. The film deposited at various numbers of laser pulses also has spherical

The results of research to reach the conditions that prevents the emergence of primary or secondary voids and achieve worker benefit from molded by almost 100%, which was the situation that cast poured in a mold heated and insulated from all sides to achieve freezing directional full starting from the region remote from the casting and ending then. Has also been compared to the microscopic structure of the resulting castings of various molding conditions, as these conditions have achieved the best sound microscopic structures.

Atorvastatin calcium (ATR) is an antihyperlipidemic agent used for lowering blood cholesterol levels. However, it is very slightly soluble in water with poor oral bioavailability, which interferes with its therapeutic action. It is classified as a class II drug according to Biopharmaceutical Classification System (low solubility and high permeability).

Letrozole (LZL) is a non-steroidal competitive aromatase enzyme system inhibitor. The aim of this study is to improve the permeation of LZL through the skin by preparing as nanoemulsion using various numbers of oils, surfactants and co-surfactant with deionized water. Based on solubility studies, mixtures of oleic acid oil and tween 80/ transcutol p as surfactant/co-surfactant (Smix) in different percentages were used to prepare nanoemulsions (NS). Therefore, 9 formulae of (o/w) LZL NS were formulated, then pseudo-ternary phase diagram was used as a useful tool to evaluate the NS domain at Smix ratios: 1:1, 2:1 and 3:1.

The synthesis of zeolite NaX from locally available kaolin has been studied. The operating conditions for zeolite NaX production from kaolin with good crystallinity were as follows; a gel formation step of metakaolin in alkaline medium in presence of additional silica to crystallize the zeolite was achieved at 60 oC for 1 hr,and with stirring. In ageing step of the reactants at room temperature for 5 days and crystallization step at 87±2 oC for 24 hr. The catalytic activity of catalyst prepared from local kaolin was studied by using cumene cracking as a model for catalytic cracking and compared with standard HY zeolite and HX zeolite catalysts. The activity test was carried out in a laboratory continuous flow unit with fixed bed re

In this paper, Activated Carbon was successfully prepared from local Iraqi material namely corns stalks .Zinc chloride ZnCl2 was used as activating agent with different concentrations (20%, 40%, 60%) for 72 hours. followed by carbonization at 450 C for (2) hour. UV-Spectrophotometer used for measuring absorbance of methylene blue solutions before and after adsorption. the maximum amount adsorbed for methylene blue material of the prepared activated Carbon was studied by Langmuir adsorption isotherm. Other characteristics of the resulting activated Carbon also discussed, such as pH, Moisture Content and ash content. Finally Activated carbon prepared in this work has good properties compared to the standard samples in such a way it could be