The influence of pre- shot peening and welding parameters on mechanical and metallurgical properties of dissimilar and similar aluminum alloys AA2024-T3 and AA6061-T6 joints using friction stir welding have been studied. In this work, numbers of plates were equipped from sheet alloys in dimensions (150*50*6) mm then some of them were exposed to shot peening process before friction stir welding using steel ball having diameter 1.25 mm for period of 15 minutes. FSW joints were manufactured from plates at three welding speeds (28, 40, 56 mm/min) and welding speed 40mm/min was chosen at a rotating speed of 1400 rpm for welding the dissimilar pre- shot plates. Tow joints were made at rotational speed of 1000 rpm and welding speed of 40m/min f

The aim of this work is studying the binary system ??'??? Ni?)with two ratios (y=36,80) by using casting method for preparing the samples.Magnetic and Mechanical properties have been studidt different httrea^nttem^rature.All the alloys were found a ferromagnetic behavior and sensitive to the heat treatment. Best properties were found at the heat treatment 1100 C°.A significant different results were found above 1100C° for lower magnetic and mechanical values. This is possibly due to the change on the degree of magnetic moment orders, in which most of the moments are started to remove from coupled ferromagnetically.?

The evaluation of residual stresses (RS) induced by the friction stir welding (FSW) process is crucial in anticipating the performance of the welded structure. The existence of such residual stresses within a friction stir welded structure may lead to excessive distortion and weakness to afford the applied external loads. To assess quantitatively the effect of these residual stresses generated by FSW process, the current paper implements a Coupled Eulerian–Lagrangian (CEL) finite element simulation to analyze both thermal and subsequent resulted remaining stress environments in dissimilar friction stir welding of AA6061-T6 and AA2024-T3 alloys. The thermal analysis step was conducted first and followed by a mechanical analysis step in whi

Electrochemical Grinding (ECG) process is a mechanically assisted electrochemical process for material processing. The process is able to successfully machine electrically conducting harder materials at faster rate with improved surface finish and dimensional control. This research studies the effect of applied current, electrolyte concentration, spindle speed and the gap between workpiece and tool on hardness and material removal rate during electrochemical grinding for stainless steel 316. The characteristic features of the electrochemical grinding process are explored through Taguchi-design-based experimental studies. The better hardness can be obtained at 10 A of the current, 150 g/l of the electrolyte concentration, 0.3 mm of gap an

The Rate theory of crack growth in PVC pipe has been studied for creep and fatigue crack propagation. Rate theory function parameters, (RTFP), were estimated theoretically from exponential function parameters, (EFP), to experimental data of crack velocity versus stress intensity factor ,(V-K) diagram, to creep crack propagation . Also (RTFP) were estimated theoretically from (EFP) to experimental data of (V-?K) diagram to fatigue crack propagation. Temperature effect with (RTFP) was discussed. Crack velocity function denoted with stress intensity factor and temperature degrees has been determined to fatigue and creep crack propagation theoretically and comparative results this function with experimental data of (V-K or ?K) diagram .

Polyethersulfone (PES) ultrafiltration membrane blending NaX zeolite crystals as a hydrophilic additive was examined for zinc (II) and lead ions Pb (II) removal from aqueous solutions. The effect of NaX zeolite content on the permeation flux and removal efficiency was studied. The results showed that adding zeolite to the polymer matrix enhanced the permeation flux. The permeation flux of all the zeolite/PES matrix membranes was higher than the pristine membrane. No significant improvement was observed in the removal of Zn (II) ions using all prepared membranes as the removal percentage did not raise above 29.2%. However, the removal percentage of Pb (II) ions was enhanced to 97% using a membrane containing 0.9%wt. zeolite. Also, it was

Green synthesis of bimetallic nanoparticles of Fe/Ni (G-Fe/Ni-NPs) and zeolite-5A supported (G-Z-Fe/Ni-NPs) as heterogeneous Fenton-like oxidation for the decolourisation of reactive red 120-dye (RR120) from the aqueous medium using green tea extract as a reducing agent. Zeolite-5A from local kaolin is prepared and characterised using the hydrothermal method and is used as a supporting material for Fe/Ni-NPs. (SEM), (EDX), (AFM), (XRD), (FT-IR), (BET). Its zeta potential were used to characterise G-Fe/Ni-NPs and G-Z-Fe/Ni-NPs. The decolourisation efficiency (Ed) of the RR120-dye using a heterogeneous Fenton-like for G-Fe/Ni-NPs and G-Z-Fe/Ni-NPs is 99.8% and 99.9%, respectively, under the optimum conditions: [H2O2] = 20 and 1 mmol/L

SKF Sami I. Jafar, Mohammad J. Kadhim, Engineering and Technology Journal, 2018 - Cited by 4

The present study investigated Haematological changes in Mesopotamichthys sharpeyi, as well as determination genotoxic effects of cadmium chloride on bunni fish by using 120 fingerlings, fish were distributed randomly into four treatments in addition to control group. Fish in first group treated (T1) with cadmium 0.093mg/L with changing water and added cadmium continuously, fish in the second group treated (T2) with cadmium 0.093mg/L with changing water without adding cadmium, third treatment (T3) with cadmium 0.046mg/L with changing water and adding cadmium continuously, and fourth treatment (T4) with cadmium 0.046mg/L with changing water without adding cadmium. Results of blood picture in T1 and T3 showed a significant reduction in red bl