The DC electrical conductivity properties of Ge60Se40-xTex alloy with x = 0, 5, 10, 15 and 20). The samples were formed in the form of discs with the thickness of 0.25–0.30 cm and the diameter of 1.5 cm. Samples were pressed under a pressure of 6 tons per cm2 , using a ton hydraulic press. They were prepared after being pressed using a ton hydraulic press using a hydraulic press. Melting point technology use to preper the samples. Continuous electrical conductivity properties were recorded from room temperature to 475 K. Experimental data indicates that glass containing 15% Te has the highest electrical conductivity allowing maximum current through the sample compared to Lu with other samples. Therefore, it is found that the DC co

Wet granulation method was used instead of conventional pan coating  or fluidized –bed coating technique to prepare enteric-coated diclofenac sodium granules, using ethanolic solution of Eudragit^TM L100 as coating, binding and granulating agent .Addition of PEG400 or di-n-butyl phthalate as a plasticizer was found to improve the enteric property of the coat.

Part of the resulted granules was filled in hard gelatin capsules (size 0), while the other part was compressed into tablets with and without disintegrant.

The release profile of these two dosage forms in 0.1N HCl (pH 1.2)for 2 hours, and in phosphate buffer (pH 6.8) for 45 minutes as well as the release kinetic were compared with that of the en

creating unique exercises utilizing a teaching approach that works with the research sample, determining how special exercises affect the development of torso flexibility, and determining how special exercises affect the development of bow ability. Activate the search The results of the pre- and post-tests for the control and experimental research groups show a statistically significant association that is favoring the post-test in the development of bow skill performance Using the experimental technique, the researcher set up one group and gave them two tests (pre and post) based on scientific theories that made sense for the topic at hand. Forty adolescent wrestlers from the Adhamiya Club in the Baghdad Governorate were recognized

In this research, the results of the Integral breadth method were used to analyze the X-ray lines to determine the crystallite size and lattice strain of the zirconium oxide nanoparticles and the value of the crystal size was equal to (8.2nm) and the lattice strain (0.001955), and then the results were compared with three other methods, which are the Scherer and Scherer dynamical diffraction theory and two formulas of the Scherer and Wilson method.the results were as followsScherer crystallite size(7.4nm)and lattice strain(0.011968),Schererdynamic method crystallite size(7.5 nm),Scherrer and Wilson methodcrystallite size( 8.5nm) and lattice strain( 0.001919).And using another formula for Schearer and Wilson methodwe obtain the size of the c

Titanium dioxide nanorods have been prepared by sol-gel template
method. The structural and surface morphology of the TiO₂ nanorods was
investigated by X-ray diffraction (XRD) and atomic force microscopy
(AFM), it was found that the nanorods produced were anatase TiO₂ phase.
The photocatalytic activity of the TiO2 nanorods was evaluated by the
photo degradation of methyl orange (MO). The relatively higher
degradation efficiency for MO (D%=78.2) was obtained after 6h of exposed
to UV irradiation.

A new simultaneous spectrophotometric-kinetic method was developed to determine phenylephrine (PHEN) and tetracycline (TETR) via H-point standard addition method (HPSAM). The proposed procedures rely on the measurements of the difference in the rate of charge-transfer (CT) reaction between each of PHEN and TETR as electron donors with p-Bromanil (p-Br) as an electron acceptor. Different experimental factors which affect the extent of the complex formation were investigated by monitoring the value of absorbance at 446 nm. Time pair of 50 -100 sec was selected and employed, among different examined pairs since it results in the highest accuracy for HPSAM-plot. Linear calibration graphs in the concentration ranges of 10.0-40.0 and 10.0–50.0