Acrylic polymer/cement nanocomposites in dark and light colors have been developed for coating floors and swimming pools. This work aims to emphasize the effect of cement filling on the mechanical parameters, thermal stability, and wettability of acrylic polymer. The preparation was carried out using the casting method from acrylic polymer coating solution, which was added to cement nanoparticles (65 nm) with weight concentrations of (0, 1, 2, 4, and 8 wt%) to achieve high-quality specifications and good adhesion. Maximum impact strength and Hardness shore A were observed at cement ratios of 2 wt% and 4 wt%, respectively. Changing the filling ratio has a significant effect on the strain of the nanocomposites. The contact angle was i

Aim: The current study was aimed to determine the relationship between the orthodontic force applied by monobloc and the salivary level of alkaline phosphatase (ALP) and lactate dehydrogenase (LDH) enzymes, considering the time factor after insertion of the appliance and whether there is a correlation between these enzymes. Materials and methods: A sample of 28 growing patients requiring orthodontic treatment with myofunctional appliance (Monoblock) was taken for the current study with an age range 9 to 12 years,all patients had Angle's class II division 1 malocclusion with no or mild crowding, the sample was selected using simple random sampling. Only 16 subjects (10 males and 6 females) were included who follow certain inclusion criteria.

In this article the conventional "solid-state reaction" method was used to synthesize perovskite Li_0.4Cd_0.6Ba₂Ca₂Cu₃O_10+δ. Four main types of compounds were obtained by physically replacing calcium oxide with cadmium in proportions 0, 0.03, 0.06 and 0.09, the pure Li_0.4Cd_0.6Ba₂Ca₂Cu₃O_10+δ phase, and the phases Li_0.4Cd_0.6Ba₂Ca_1.97Cd_0.03Cu₃O_10+δ

Nutrient agar medium with various concentrations of cefotaxime was used for isolation spontaneous mutants from wild type strain of P.aeruginosa PHA-1. Eighty-two mutants were successfully isolated with the viable count 52×107 , these mutants were confirmed as spontaneous not physiological adaption mutants by reculture on the same medium. Then, wild type PHA-1 and mutants were examined for production pyocyanin; a blue greenish pigment was clearly noticed on King A medium. Remarkably the mutant strain named S300-8 was distinguished in productivity in comparison with wild type strain PHA-1; the amount of pigment was 56.0667mg/l and 74.53mg/l respectively. In addition, pyocyanin produced by mutant strain S300-8 revealed a potent efficacy again

A new tool geometry was used to achieve friction stir spot welding (FSSW) in which the shoulder was designed separately from the rotating pin, and in order to examine weldment strength through the modified tool, a lap joints of AA2024 aluminum alloy plate 1 mm thick were welded successfully by using 6 mm pin diameter and varying process parameters (rotational speeds, tool nose geometry, and depth of tool penetration in the lower welded plate). Experimental tests indicate that the maximum average tensile shear load was 3100 N at the best selected condition. Microstructure examination and micro hardness test along the spot zones were investigated as well as measuring pin penetration load. Visual inspection of the welded spot surface shows a g

Tin dioxide doped silver oxide thin films with different x content (0, 0.03, 0.05, 0.07) have been prepared by pulse laser deposition technique (PLD) at room temperatures (RT). The effect of doping concentration on the structural and electrical properties of the films were studied. Atomic Force Measurement (AFM) measurements found that the average value of grain size for all films at RT decrease with increasing of AgO content. While an average roughness values increase with increasing x content. The electrical properties of these films were studied with different x content. The D.C conductivity for all films increases with increasing x content. Also, it found that activation energies decrease with increasing of AgO content for all films.

Abstract: The aim of this study was to evaluate the effect of bone density value in Hounsfield unit derived from cone beam computed tomography (CBCT), and implant dimensions in relation to implant stability parameters namely the resonance frequency analysis and the insertion torque (IT) value. It included 24 patients who received 42 dental implants (DI). The bone density of the planned implant site was preoperatively measured using cone beam computed tomography. The implant stability was measured using Osstell implant stability quotient (ISQ). The ISQ values were recorded immediately postoperatively and after 16 weeks. The IT value was categorized as 35 N/cm or > 35 N/cm. The mean (standard deviation) primary stability was 79.58 (5.27) ISQ,

In this work, ZnS thin films have been deposited by developed laser deposition technique on glass substrates at room temperature. After deposition process, the films were annealed at different temperatures (200ºC , 300 ºC and 400ºC ) using thermal furnace.The developed technique was used to obtain homogeneous thin films of ZnS depending on vaporization of this semiconductor material by continuous CO2 laser with a simple fan to ensure obtaining homogeneous films. ZnS thin films were annealed at temperature 200ºC, 300 ºC and 400ºC for (20) minute in vacuum environment. Optical properties of ZnS thin film such as absorbance, transmittance, reflectance, optical band gap, refractive index extinction coefficient and absorption coefficien