Background: The purpose of this study was to evaluate the effect of in vitro long-term simulation of oral conditions on the bond strength of PEEK CAD/CAM lingual retainers.

Material and methods: The sample consisted of 12 PEEK CAD/CAM retainers each composed of 2 centrally perforated 3x4mm pads joined by a connector. They were treated by 98% sulfuric acid for 1 minute and then conditioned with Single Bond Universal and bonded to the lingual surface of premolar teeth by 3M Transbond TM System. Half of the retainers were artificially aged using a 30-day water storage and 5000 thermocycling protocol before bond strength testing to compare with the non-aged specimens.

Results: The artificially aged retainers showed a marginally

Background : It has been suggested that pretreatment with a statin agent prior to
myocardial infarction limits myocardial
creatine kinase release, and thus may act to
limit myocardial infarct size in humans.
Objective : To examine the effect of very
early statin initiation for acute myocardial
infarction (AMI), to the extent of
myonecrosis as manifested by peak serum
creatine kinase levels.
Methods : Patients with AMI admitted to AlKindy teaching hospital cardiac care unit
from 1st February 2007 to 28th February
2008, who fulfilled the inclusion criteria
cited in the present study, were randomly
assigned into two study groups. The statin
group patients have received a single oral
dose of 40 mg

The experiment was conducted in the old botanical garden belong to Biology Department/ College of Education for Pure Science - Ibn Al-Haitham/Baghdad University for growing season 2015-2016 to study the effect of irrigation with four concentrations of sodium chloride (0, 50, 100, 150) mM.L-1 and spraying with selenium in three concentrations (0, 10, 20) mgL-1 on growth of broad bean plant using clay pots. The experiment was design according to completely randomized design (CRD) with three replications. Results indicated that broad bean plant irrigated with saline water and increasing concentrations of sodium chloride in growth medium caused a significant decreased in the plant growth parameters (plant height, no. of compound leaves. Plant-1

Aim: surface modification of titanium using fiber laser 1064 nm to enhance the bond strength to resin cement. Material and Methods: thirty titanium discs of 0.6 cm x 0.3 cm (diameter and thickness respectively) were categorized after preparation into three groups (n=10) as follows: control group with no surface treatment and two test groups were treated with fiber laser after estimation the appropriate parameters in the pilot study which are 81 ns pulse duration, 30,000 Hz frequency, 50 µm spot size and 10,000 mm/s scanning speed and different average power values (10 W and 20 W) depending on the tested group. Titanium discs surface characterization was performed by scanning electron microscope (SEM), a

The numerical analysis was conducted to studying the influence of length to diameter ratio (L/D) on the behavior of the soil treated with sand columns treated with 8% sodium silicate for both floating and end bearing type by using finite element method (Plaxis 3D Foundation ) for isolated foundation of real dimensions. The analysis’s study indicate that in the floating type the best improvement ratio was achieved at (L/D=8) when using columns with a diameter of (0.5, 0.7), but when using columns with a diameter of 0.3 m, it was noticed that the bearing improvement ratio increases with increasing (L/d). While the results of the analysis for end bearing type show that the higher improvement ratio was achieved at (L/D=4) when using columns w

In this study, composite materials were prepared using unsaturated polyester resin as binder with two types of fillers (sawdust and chopped reeds). The molding method is used to prepare sheets of UPE / sawdust composite and UPE / chopped reeds composite. The mechanical properties were studied including flexural strength and Young's modulus for the samples at normal conditions (N.C). The Commercial wood, UPE and its composite samples were immersed in water for about 30 days to find the weight gain (Mt%) of water for the samples, also to find the effect of water on their flexural strength and Young's modulus. The results showed that the samples of UPE / chopped reeds composite gained highest values of flexural strength (24.