The faujasite type Y zeolite catalyst was prepared from locally available kaolin. For prepared faujasite type NaY zeolite X-ray, FT-IR, BET pore volume and surface area, and silica/ alumina were determined. The Xray and FT-IR show the compatibility of prepared catalyst with the general structure of standard zeolite Y. BET test shows that the surface area and pore volume of prepared catalyst were 360 m2 /g and 0.39 cm3 /g respectively.
The prepared faujasite type NaY zeolite modified by exchanging sodium ion with ammonium ion using ammonium nitrate and then ammonium ion converted to hydrogen ion. The maximum sodium ion exchange with ammonium ion was 53.6%. The catalytic activity of prepared faujasite type NaY, NaNH4Y and NaHY zeolites was investigated by using the experimental laboratory plant scale of fluidized bed reactor. The cracking process was carried out in the temperature range 440 to 500 o C, weight hourly space velocity (WHSV) range 10 to 25 h-1 ,and atmospheric pressure . The catalytic activities of the prepared faujasite type NaY , NaNH4Y and NaHY
zeolites were determined in terms of vacuum gas oil (VGO) conversion, and gasoline yield . The conversion at 500o C and WHSV10 hr-1 by using faujasite type NaY, NaNH4Y and NaHY zeolite were 50.2%, 64.1% and 69.5wt% respectively. The gasoline yield using the same operating conditions were 24.8%, 30.5% and 36.8wt% respectively.
This paper aims to verify the existence of relationships between product innovation and the reputation of the organization. The study problem is that the State Organization for Marketing of Oil (SOMO) system is inflexible in terms of marketing procedures and needs innovative, unconventional methods in innovating its products and improving performance. The reputation of the organization. The importance of the study lies in that it is an attempt to raise the interest of SOMO in its approach to the research variables in order to enhance its competitive position in the future and improve the marketing business environment, which contributes to enhancing the reputation of the organization by product innovation. The study sample
... Show More
(1)
This paper was aimed to study the efficiency of forward osmosis (FO) process as a new application for the treatment of wastewater from textile effluent and the factors affecting the performance of forward osmosis process.
The draw solutions used were magnesium chloride (MgCl2), and aluminum sulphate (Al2 ( SO4)3 .18 H2O), and the feed solutions used were reactive red, and disperse blue dyes.
Experimental work were includes operating the forward osmosis process using thin film composite (TFC) membrane as flat sheet for different draw solutions and feed solutions. The operating parameters studied were : draw solutions concentration (10 – 90 g/l), feed solutions concentration (5 – 30 mg/l), draw solutions flow rate (10 – 50 l/hr
(2)
(3)
(1)
The insurance activity in the various countries of the world are important indicators of the strength of the country's economy, he came to study the stages compensation insurance settlement against fire and the importance of investing time risk in achieving the payment of compensation speed, and the implications for the continuation of the insured to carry out insurance with the insurance company, whether working within the public sector or the private sector. Hence the research problem in how quickly insurance companies to pay compensation as soon as possible and the return of the insured to carry out its work and make up for what he died from loss. Intentional sample was selected from branches and divisions and Their assistants manager
... Show More
The study aimed to prepare a nanocapsules formulation from the acetonic extract of Moringa oleifera leaves, using polymeric capsules, and test its toxicity against the third instar larvae of Culex pipiens mosquitoes. The leaf extract was prepared using acetone as a solvent, and the nano polymeric capsules were prepared using the synthetic polymer polyethylene glycol 4000. The results showed the successful preparation of nano polymeric capsules from the leaf extract, with an average particle size of 259.2 nm, and a nanocapsule diameter of 263.83 nm, as determined by DLS and SEM analysis, respectively. The toxicity results indicated that the nano polymeric capsules of the leaf extract exhibited higher mortality rates, reaching 97.6% a
... Show More
(10)
(11)
Ten blue swimming crabs Portunus segnis (Forskål, 1775) were collected from the north west of the Arabian Gulf off the Iraqi marine waters from October to November 2017 at 29ᵒ 37′ N to 48ᵒ 47′ E.
The barnacle Octolasmis angulata (Aurivillius, 1894) was found on the gills of the present species of crab, the mean incidence of infestation was 30%, while the mean Intensity of infestation was 12.3. The barnacle have a long and slim shaped calcareous plate with the presence of carina and the absence of tergum, in addition to the elongated shape of carina and scutum. The current study represents the first record of the barnacle O. angulata in the Ar
... Show More
(1)
Background: Pain due to muscular cramp during hemodialysis is one of the most common problems experienced by patient undergoing hemodialysis, and is associated with poor outcomes of patients. The main aim of this study was to comparing the effects of lavender oil and olive oil massage on Pain due to muscular cramp during hemodialysis.
Methods: In this random clinical trial, 60 hemodialysis patients were enrolled randomly and allocated to two groups with 30 members in Lordegan and Brojen hospitals, Shahrekord, Iran. The intervention included flora massage on the lower leg muscles so that the first group received olive oil massage (10 drops) and the second group received lavender oil massage (10 dr
... Show More
(5)
(1)
Denture bases are fabricated routinely using Poly(methyl methacrylate) (PMMA) acrylic resin. Yet, it is commonly known for its major drawbacks such as insufficient strength and ductility. The purpose of this study was to improve the performance of PMMA acrylic resin as a denture base material by reinforcement with surface treated lithium disilicate glass ceramic powder. The ceramic powder was prepared by grinding and sieving IPS e.max CAD MT blocks. Then, the powder was surface treated with an organosilane coupling agent (TMSPM) and added to PMMA in amount of 1%, 3%, 5% and 7% by weight. Characterizations of the powder was done by particle size analysis, XRD and FTIR. Transverse strength, Impact strength, Shore D hardness and surface roughn
... Show More
(2)
(2)