The faujasite type Y zeolite catalyst was prepared from locally available kaolin. For prepared faujasite type NaY zeolite X-ray, FT-IR, BET pore volume and surface area, and silica/ alumina were determined. The Xray and FT-IR show the compatibility of prepared catalyst with the general structure of standard zeolite Y. BET test shows that the surface area and pore volume of prepared catalyst were 360 m2 /g and 0.39 cm3 /g respectively.
The prepared faujasite type NaY zeolite modified by exchanging sodium ion with ammonium ion using ammonium nitrate and then ammonium ion converted to hydrogen ion. The maximum sodium ion exchange with ammonium ion was 53.6%. The catalytic activity of prepared faujasite type NaY, NaNH4Y and NaHY zeolites was investigated by using the experimental laboratory plant scale of fluidized bed reactor. The cracking process was carried out in the temperature range 440 to 500 o C, weight hourly space velocity (WHSV) range 10 to 25 h-1 ,and atmospheric pressure . The catalytic activities of the prepared faujasite type NaY , NaNH4Y and NaHY
zeolites were determined in terms of vacuum gas oil (VGO) conversion, and gasoline yield . The conversion at 500o C and WHSV10 hr-1 by using faujasite type NaY, NaNH4Y and NaHY zeolite were 50.2%, 64.1% and 69.5wt% respectively. The gasoline yield using the same operating conditions were 24.8%, 30.5% and 36.8wt% respectively.
Density functional theory (DFT) with B3LYP level and 6-311G[Formula: see text] basis sets for light atoms like N and O and SDD basis sets for heavy atoms like Sn is used to examine the interaction of tin dioxide nanocrystals with nitrogen dioxide as a function of temperature from 273[Formula: see text]K to 373[Formula: see text]K through a Gaussian 09W software program. Gibbs free energy, enthalpy, and entropy of activation and reaction are calculated. The situation of transition of SnO2 clusters toward nitrogen dioxide is investigated. According to the findings, the activation energy of SnO2 clusters with nitrogen dioxide increases as the temperature rises (in negative value). Gauss view 0
... Show More
(1)
(1)
Hollow core photonic bandgap fibers provide a new geometry for the realization and enhancement of many nonlinear optical effects. Such fibers offer novel guidance and dispersion properties that provide an advantage over conventional fibers for various applications. Dispersion, which expresses the variation with wavelength of the guided-mode group velocity, is one of the most important properties of optical fibers. Photonic crystal fibers (PCFs) offer much larger flexibility than conventional fibers with respect to tailoring of the dispersion curve. This is partly due to the large refractive-index contrast available in the silica/air microstructures, and partly due to the possibility of making complex refractive-index structure over the fibe
... Show More
(1)
The study aimed to analyze the relationship between the internal public debt and the public budget deficit in Iraq during the period 2010–2020 using descriptive and analytical approaches to the data of the financial phenomenon. Furthermore, to track the development of public debt and the percentage of its contribution to the public budget of Iraq during the study period. The study showed that the origin of the debt with its benefits consumes a large proportion of oil revenues through what is deducted from these revenues to pay the principal debt with interest, which hinders the development process in the country. It has been shownthat although there was a surplus in some years of study, it was not
... Show More
The research aims at identify the role of the electronic trading system used in the Iraq stock exchange to promote trading activity for the stocks of listed companies in this market.
To prove the hypothesis of research, it was selected the main trading indicators for the market to be a main field in test the research hypothesis.it was selected as the period of time for (9)years span between the years (2005-2013) because they represent the first two articles of equal time periods represent aperiod that preceded the introduction of electronic trading system while the second represents the period of time that followed
The research found a number of conclusions but the mo
... Show More
(1)
Four antimony compounds were used in this inves as additives to retard combustion of unsaturated polyester and epoxy resins, namely: 1. Tetraethyl ammonium tribromoethylantimonates (additive I). 2. Tetraethyl ammonium chlorodibromoethylantimonates (additive II). 3. Tetraethyl ammonium trichloroethylantimonates (additive III). 4. Tetraethyl ammonium bromodichloroethylantimonates (additive IV). The effects of these additives on flammability of unsaturated polyester and epoxy resins have been studied by using sheets of the resins with weight percentages of (0.5,1.0,1.5,2.0,2.5&3.0%) of the additives in dimensions of (150 X150X3)mm .Three standard test methods were used to measure the flame retardation which are: (ASTM:D -2863), (ASTM:D-635
... Show More
in this paper copper oxide (cuO thin films were prepared by the method of vacum thermal evaporation a pressure.
In this paper Alx Ga1-x As:H films have been prepared by using new deposition method based on combination of flash- thermal evaporation technique. The thickness of our samples was about 300nm. The Al concentration was altered within the 0 x 40.
The results of X- ray diffraction analysis (XRD) confirmed the amorphous structure of all AlXGa1-x As:H films with x 40 and annealing temperature (Ta)<200°C. the temperature dependence of the DC conductivity GDC with various Al content has been measured for AlXGa1-x As:H films.
We have found that the thermal activation energy Ea depends of Al content and Ta, thus the value of Ea were approximately equal to half the value of optical gap.
In this research, titanium dioxide nanoparticles (TiO2 NPs) were prepared through the sol-gel process at an acidic medium (pH3).TiO2 nanoparticles were prepared from titanium trichloride (TiCl3) as a precursor with Ammonium hydroxide (NH4OH) with 1:3 ratio at 50 °C. The resulting gel was dried at 70 °C to obtain the Nanocrystalline powder. The powder from the drying process was treated thermally at temperatures 500 °C and 700 °C. The crystalline structure, surface morphology, and particle size were studied by using X-ray diffraction (XRD), Atomic Force Microscopy (AFM), and Scanning Electron Microscope (SEM). The results showed (anatase) phase of titanium dioxide with the average grain size
... Show More
(6)
(3)