A new tool geometry was used to achieve friction stir spot welding (FSSW) in which the shoulder was designed separately from the rotating pin, and in order to examine weldment strength through the modified tool, a lap joints of AA2024 aluminum alloy plate 1 mm thick were welded successfully by using 6 mm pin diameter and varying process parameters (rotational speeds, tool nose geometry, and depth of tool penetration in the lower welded plate). Experimental tests indicate that the maximum average tensile shear load was 3100 N at the best selected condition. Microstructure examination and micro hardness test along the spot zones were investigated as well as measuring pin penetration load. Visual inspection of the welded spot surface shows a g

Background: Glass ionomer restorations are widely employed in the field of pediatric dentistry. There is a constant demand for a durable restoration that remains functional until exfoliation. This study aimed to measure and compare the effect of a novel coating material (EQUIA Forte Coat) on the microleakage of glass hybrid restoration (EQUIA Forte HT) in primary teeth. Material and method: Thirty cavitated (class-II) primary molars were allocated randomly into two groups based on the coat application; uncoated (control) and coated group (experimental). Cavities were prepared by the use of a ceramic bur (CeraBur) and restored with EQUIA Forte HT with or without applying a protective coat (EQUIA Forte Coat). Samples went through the therm

The long healing time of bone after tooth extraction in order to construct artificial teeth is uncomfortable to the patient because of aesthetic or masticatory problems in addition to the daily visit to dental clinic. The objective of this study was to evaluate the effect of 805 nm diode laser with long time intervals on repair of bone and skin incisions in rabbits through biochemical, radiological and histological findings. Eighteen New-Zealand rabbits were undergone surgical operations to make a cavity in the bone of the lower jaw, the rabbits were divided into two groups:- Group A (control group) containing nine rabbits. Group B (lased group) containing nine rabbits in which two cavities were done, one on the right side and the other

The current research aims to identify the effect of the Cornell note-taking strategy on the achievement of chemistry among second-grade female students in government daytime middle schools. Al-Fadhila School was chosen intentionally as its student sample, affiliated with the First Karkh Directorate for the academic year (2024-2025). One of the two classes was then chosen to represent the experimental group, taught according to the Cornell note-taking strategy, and the other class, the control group, was taught according to the traditional method. The equivalence of the two research groups was verified using a set of variables, including chronological age calculated in months, the Raven Intelligence Test, previous achievement in chemistry, a

Recent research has examined the improvement of physical and dielectric properties of BaTiO₃ ceramic material by small addition of excess TiO₂ or BaCO₃. The prepared samples sintered at different temperatures and varying soaking time. The results show that increasing the sintering temperature within 1350°C and soaking time of 10 hrs give better electrical and physical properties, which indicate the reaction is complete at higher temperature and period.

The current research aimed to conducting two experiments to study the effect of coating hatching eggs with nano-titanium dioxide (nano-TiO2) and nano-silica dioxide (nano-SiO2) particles and their mixture with carboxymethyl cellulose (CMC) on the characteristics of hatching percentage, embryo growth inside the egg. The study was conducted in the Department of Animal Production, College of Agriculture, Tikrit University for the period from 19/3/2023 to 17/9/2024. It aimed to evaluate the coating of hatching eggs with Nano-TiO2 and Nano-SiO2 particles and their mixture with carboxymethyl cellulose CMC on the qualities of hatching percentage, embryo growth inside the egg, as well as trying to obtain the best and longest storage method for fert

(Cu1-x,Agx)2ZnSnSe4 alloys have been fabricated with different Ag content(x=0, 0.1, and 0.2) successfully from their elements. Thin films of these alloys have been deposited on coring glass substrate at room temperature by thermal evaporation technique under vacuum of 10-5Torr with thickness of 800nm and deposition rate of 0.53 nm/sec. Later, films have been annealed in vacuum at (373, and 473)K, for one hour. The crystal structure of fabricated alloys and as deposited thin films had been examined by XRD analysis, which confirms the formation of tetragonal phase in [112] direction, and no secondary phases are founded. The shifting of main polycrystalline peak (112) to lower Bragg’s angle as compared to Cu2ZnSnSe4 angle refers to incorpora