Test results of eight reinforced concrete one way slab with lacing reinforcement are reported. The tests were designed to study the effect of the lacing reinforcement on the flexural behavior of one way slabs. The test parameters were the lacing steel ratio, flexural steel ratio and span to the effective depth ratio. One specimen had no lacing reinforcement and the remaining seven had various percentages of lacing and flexural steel ratios. All specimens were cast with normal density concrete of approximately 30 MPa compressive strength. The specimens were tested under two equal line loads applied statically at a thirds part (four point bending test) up to failure. Three percentage of lacing and flexural steel ratios wer

This experiment was performed to investigate the influence of different oils in the diets of laying quail on their egg quality characteristics. One hundred and twenty 7-wk old Japanese quails (Coturnix coturnix japonica) were allocated to four groups with three replicates containing 10 quail each (30 quail per each treatment group). They were fed for 13 weeks (including one week of adaptation period) on diets containing 3% oil from different sources, viz. either sunflower (T1), linseed (T2), maize (T3), or fish oil (T4). Inclusion the diet of laying quail with fish oil (T4) and maize oil (T2) resulted in significant increase with respect to egg weight, yolk weight, albumen weight, yolk diameter, yolk height, albumen diameter, albumen height

This experiment was performed to investigate the influence of different oils in the diets of laying quail on their egg quality characteristics. One hundred and twenty 7-week-old Japanese quails (Coturnix coturnix japonica) were allocated to four groups with three replicates containing 10 quail each (30 quail per treatment group). They were fed for 13 weeks (including one week of adaptation period) on diets containing 3% oil from different sources, viz., sunflower (T1), linseed (T2), maize (T3), or fish oil (T4). Inclusion of the diet of laying quail with fish oil (T4) and maize oil (T2) resulted in a significant increase with respect to egg weight, yolk weight, albumen weight, yolk diameter, yolk height, albumen diameter, albumen height, sh

Objectives: The study objectives were to evaluate customer satisfaction with community pharmacy services and measure the relationships between customer satisfaction and pharmacy/pharmacist characteristics and customer quality of life. Methods: This was a cross-sectional survey of a convenience sample of customers at 20 community pharmacies in 10 different geographical areas in Baghdad city between May and September 2018. We used the satisfaction items which were developed by Paterson and colleagues in 2013. The survey also assessed customer quality of life (QoL) with 12 QoL items. Results: The study recruited 400 pharmacy customers. Overall, customers reported good satisfaction with community pharmacy services. The most

Biaxial hollow slab is a reinforced concrete slab system with a grid of internal spherical voids included to reduce the self-weight. This paper presents an experimental study of behavior of one-way prestressed concrete bubbled slabs. Twelve full-scale one-way concrete slabs of (3000mm) length with rectangular cross-sectional area of (460mm) width and (150mm) depth. Different parameters like type of specimen (solid or bubbled slabs), type of reinforcement (normal or prestress), range of PPR and diameter of plastic spheres (100 or 120mm) are considered. Due to the using of prestressing force in bubbled slabs (with ratio of plastic sphere diameter D to slab thickness H, D/H=0.67), the specimens showed an increase in ultimat

Non-biodegradability of rubber tires contributes to pollution and fire hazards in the natural environment. In this study, the flexural behavior of the Rubberized Reactive Powder Concrete (RRPC) beams that contained various proportions and sizes of scrap tire rubber was investigated and compared to the flexural behavior of the regular RPC. Fresh properties, hardened properties, load-deflection relation, first crack load, ultimate load, and crack width are studied and analyzed. Mixes were made using micro steel fiber of the straight type, and they had an aspect ratio of 65. Thirteen beams were tested under two loading points (Repeated loading) with small-scale beams (1100 mm, 150 mm, 100 mm) size.

The fine aggregate

loaded reinforced concrete circular short columns. An experimental investigation into the behavior
of 24 short reinforced concrete columns with and without steel fibers was carried out. The columns
had a circular section (200 mm diameter and 900 mm long). Test variables include concrete
strength, spacing of spiral reinforcement, and inclusion of steel fibers. The axial stress and axial
strains were obtained and used to evaluate the effects of the presence of steel fibers. It was found
that the addition of steel fibers slightly improves the load carrying capacity of the tested columns
whereas it significantly enhances the ductility of these specimens. Test results also indicated that for
the same confinement parameter

This research presents experimental and theoretical investigation of 15 reinforced concrete spliced and nonspliced girder models. Splices of hooked dowels and cast in place joints, with or without strengthening steel plates were used. Post-tensioning had been used to enhance the splice strength for some spliced girders. The ANSYS computer program was used for analyzing the spliced and non-spliced girders. A nonlinear three dimensional element was used to represent all test girders. The experimental results have shown that for a single span girder using steel plate connectors in the splice zone has given a sufficient continuity to resist flexural stresses in this region. The experimental results have shown that the deflection of hooked do

A nanocrystalline CdS thin film with 100 nm thickness has been prepared by thermal evaporation technique on glass substrate with substrate temperature of about 423 K. The films annealed under vacuum at different annealing temperature 473, 523 and 573 K. The X-ray diffraction studies show that CdS thin films have a hexagonal polycrystalline structure with preferred orientation at (002) direction. Our investigation showed the grain size of thin films increased from 9.1 to 18.9 nm with increasing the annealing temperature. The optical measurements showed that CdS thin films have direct energy band gap, which decreases with increasing the annealing temperature within the range 3.2- 2.85 eV. The absorbance edge is blue shifted. The absorption