The performance of asphalt concrete pavement has affected by many factors, the temperature is the most important environmental one which has a large effect on the structural behavior of flexible pavement materials. The main cause of premature failure of pavement is the rutting, Due to the viscoelastic nature of the asphalt cement, rutting is more pronounced in hot climate areas because the viscosity of the asphalt binder which is
inversely related to rutting is significantly reduced with the increase in temperature resulting in a more rut susceptible paving mixtures. The objective of this study is to determine the effect of temperatures variations on the permanent deformation parameters (permanent strain (p), intercept (a), slope (b), Alpha and Mu) as well as resilient strain (r) and resilient modulus (Mr). To achieve this objective, one aggregate gradation with 12.5mm nominal maximum size, two grades of asphalt cements (40-50 and 60-70) brought form Al- Daurah refinery, limestone dust filler has been used to prepare the asphalt concrete mixtures. 30 Marshall specimens were prepared to determine the optimum asphalt cement content. Thereafter, 30 cylindrical asphalt concrete specimens (102mm in diameter and 203 mm in height) are prepared in optimum asphalt cement and optimum ±0.5 percent. The prepared specimens were used in uniaxial repeated load test to evaluate the permanent deformation parameters of asphalt concrete mixes under the following testing temperature (5, 15, 25, 40 and 60c). The test result analyses appeared that Mr is decrease 51 percent when temperature increased from 5 c to 25 c and then decrease 22 percent with further increase in temperature from 25 c to 60 c. Also, the Alpha value decreases by a factor of 1.25 and 1.13 when temperature increases from 5 c to 25 c and 25 c to 60 c, espectively.
Finally, statistical models were developed to predict the Alpha and Mu parameters of permanent deformation.
The current research aims to measure Generalized Anxiety Disorder among students of the University of Sulaymaniyah / College of Basic Education, and to identify the significance of differences between sex, scientific specialization and age, and for that reason, the research sample of (102) male and female students was chosen in a random manner, and the researcher used the diagnostic criteria for the generalized anxiety disorder contained He mentioned it in the Statistical and Diagnostic Manual of Psychiatry, and the paragraphs of the scale were formulated according to those standards after they verify the conditions of honesty and consistency, and the use of appropriate statistical means. The results of the research indicated that genera
... Show MoreSKF Sami I. Jafar, Mohammad J. Kadhim, Engineering and Technology Journal, 2018 - Cited by 4
(4)
Abstract:
Objectives: To assess nurses' attitude toward end of life phase. To find out relationships between nurses attitude and socio demographic data (age, gender, level of education, years of experience).
Methodology: A descriptive cross-sectional study design is carried out to assess the attitude on nurses concerning patient at the end of life phase at critical care units, from the period of (1nd November 2021) to (1th February 2022). A probability sample random sampling technique used. Then, the number of participants in Baquba Teaching Hospital and general al khalis hospital were determined by using rando
... Show MoreIn this work, the optical properties of Cu2S with different thickness
(1400, 2400, 4400) Ǻ have been prepared by chemical spray pyrolys
is method onto clean glass substrate heated at 283 oC ±2. The effect
of thickness on the optical properties of Cu2S has been studied. It
was found that the optical properties of the electronic transitions on
fundamental absorption edge were direct allowed and the value of the
optical energy gap of Cu2S (Eg) for direct transition decreased from
(2.4-2.1) eV with increasing of the thickness from (1400 - 4400)Ǻ
respectively. Also it was found that the absorption coefficient is
increased with increasing of thicknesses. The optical constants such<
(2)
Recently, several concepts and expressions have emerged that have often preoccupied the world . around the concept of environment and sustainability. This is due to the negative and irresponsible impact of man and his innovations in various industrial and technological fieldsthat have damaged the natural environment. Architecture and cities at the broader level are some of the man made components that caused these negative impacts and in the same time affected by them. What distinguishes architectural and urban projects is the consumption of large . quantities of natural resources and production larger amounts of waste and pollution, along the life of these projects. At the end of the twentieth century and the beginning of the twenty-fir
... Show MoreReceipt date:06/23/2020 accepted date:7/15/2020 Publication date:12/31/2021
This work is licensed under a Creative Commons Attribution 4.0 International License
The executive authority differs from one country to another, as it differs from a federal state to another according to the nature of the applied political systems, so this research focused on federal states according to their political systems, then going into the details of the executive authority and its role In the federal states by referring to the four federal experiments
... Show More
This work was conducted to study the oxidation of phenol in aqueous solution using copper based catalyst with zinc as promoter and different carrier, i.e. γ-Alumina and silica. These catalysts were prepared by impregnation method.
The effect of catalyst composition, pH (5.6-9), phenol to catalyst concentration ratio (2-0.5), air feed rate (30-50) ml/s, stirring speed (400-800) rpm, and temperature (80-100) °C were examined in order to find the best conditions for phenol conversion.
The best operating conditions which lead to maximum phenol conversion (73.1%) are : 7.5 pH, 4/6 phenol to catalyst concentration, 40 ml/s air feed rate, 600 rpm stirring speed, and 100 °C reaction temperature. The reaction involved an induction period
The electrochemical behavior of carbon steel in water sweetening station in Libya has been studied in the range of ( 293–333 oC) using weight loss technique. Measurements were carried out over a range of Reynolds number (5000 – 25000).An apparatus was designed for studying the corrosion process in the turbulent regime, which is of industrial significance. It was found that The corrosion rate of carbon steel in water sweetening station is under diffusion control and increases with increasing Reynolds number. On the other hand the variation of corrosion rate with temperature in the range of (293–333 oC) was found to follow Arrhenius equation and the activation energy approximately the same except at low Reynolds