Objective: The aim of this study was to evaluate the effect of pumice, burning investment material
and black sand on the surface roughness of heat cure acrylic resin.
Methodology: Sixty specimens were prepared from pink heat cure acrylic resin, the specimens
where grouped into; 20 specimens which polished with pumice and water (control group); 20
specimens which polished with investment material (after burning it) and water; and 20 specimens
which polished with black sand and water. The average surface roughness of specimens after
polishing procedure had been determined by profilometer (surface roughness tester).
Results: Through the application of ANOVA and LSD tests, the result of this study showed that there
wa

The current study designed to determine the effect of Glucosamine sulfate on the liver tissue of Albino mice .the study included (40)mice divided in to 4 groups(control group had distilled water orally ).The other groups treated with(1000,2000,3000)ml/k .respectively for 8 week .the liver have been taken from dissected animal for microscopic preparation to study the histological changes .Frequently histopathologicale changes appeared in the liver tissue of the exposure groups during (4-8)week .This changes depends on (Dose and Time ). The effects were Congestion ,Infiltration ,Swelling ,Vaculation ,Hyalinization , Amyloid and Necrosis.

The current study designed to determine the effect of Glucosamine sulfate on the liver tissue of Albino mice .the study included (40)mice divided in to 4 groups(control group had distilled water orally ).The other groups treated with(1000,2000,3000)ml/k .respectively for 8 week .the liver have been taken from dissected animal for microscopic preparation to study the histological changes .Frequently histopathologicale changes appeared in the liver tissue of the exposure groups during (4-8)week .This changes depends on (Dose and Time ). The effects were Congestion ,Infiltration ,Swelling ,Vaculation ,Hyalinization , Amyloid and Necrosis.

      Self-compacted concrete (SCC) is a highly flowable concrete, with no segregation which can be spread into place by filling the structures framework and permeate the reinforcement without any compaction or mechanical consolidation ACI 237R-14. One of the most important problems faced by concrete industry in Iraq and Gulf Arab land is deterioration due to internal sulfate attack (ISA) that causes damage of concrete and consequently reduces its compressive strength, increases expansion and may lead to its cracking and destruction. The experimental program was focused to study two ordinary Portland cements with different chemical composition with (5, 10 and 15) % percentage of high reactivity metakaoline (HRM)

There are different types of corruptions such as administrative, political, economic and financial corruption. The corruption forms also varied such as bribery, nepotism and extortion. All types and forms of corruption play significant role in the all economic variables generally and on investments in particular, and the corruption used to be an intermediate means in reducing the rate of economic growth.  The corruption contributes in reducing the domestic investments via pay bribery by investors to officials’ persons for supplemental contracts and tenders which finally leads to reduction in the investment efficiency. The corruption also contributes in rise of operational costs for the investment projects.  In additio

In this search, Ep/SiO2 at (3, 6, 9, 12 %) composites is prepared by hand Lay-up method, to measure the change in the thermal conductivity and Impact Strength of epoxy resin before and after immersion in H2SO4 Solution with a 0.3N for 10 days. The results before immersion decreases with the increase of the weight ratios of the reinforcement material (SiO2), It changed from (82.6×10-2 to 38.7×10-2 W/m.°C) with change weight ratios from (3 to 12) % respectively, but after immersion time in the chemical solution where it was (65.6×10-2 W/m.°C) at the weight ratios (6 %) and became (46.6 × 10-2 W/m.°C) after immersion in sulfuric acid. The results of the Impact strength decreased by increasing the percentage weight ratio, it changed f

Through an experimental program of eighteen specimens presented in this paper, the bond strength between reinforcing bar and rubberized concrete was produced by adding waste tire rubber instead of natural aggregate. The fine and coarse aggregate was replaced in 0%, 25%, and 50% with the small pieces of a waste tire. Natural aggregate replacement ratio, rebar size, embedded rebar length, the rebar yield stress of rebar, cover, and concrete compressive strength were studied in this investigation. Ultimate bond stress, bond stress-slip response, and failure modes were presented. The experimental results reported that a reduction of 19% in bond strength was noticed in 50% replaced rubberized concrete compared with convention

This research studies the effect of adding five different percentages of polymer (2, 4, 6, 8, and 10% of cement weight) on cement mortar's fresh and hardened properties, which was cured at laboratory temperature for 7, 14, and 28 days. Workability increases with increasing polymer. The workability value was lowest (25.6 and 29.4) % in mixtures containing 2% and 4% of (SBR). Increasing polymer ratios significantly decreased mechanical properties (compressive and flexural strength). Therefore, the best results were at 2% SBR and 4% SBR at 28 days of age. An inverse relationship was recorded between the increase in SBR ratios and polymer-modified cement mortar's compressive and flexural strength values. In general, the high