Electrodeposition of metal oxides on graphite electrodes can improve their ability to remove organic substances. In this work, multicomponent oxides of Mn, Co, and Ni were electrochemically deposited on both the anode and cathode of graphite electrodes to enhance their performance in removing phenol. Formation of the deposit was achieved within 2 h in current densities of 20, 25, 30, and 35 mA/cm2 for better composite properties. The deposited layer was characterized by testing the surface structure, morphology, composition, and roughness. X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray (EDX), and Atomic force microscopy (AFM) techniques facilitated these tests. The composite electrodes have synthesized

Abstract : Tin oxide SnO2 films were prepared by atmospheric chemical vapor deposition (APCVD) technique. Our study focus on prepare SnO2 films by using capillary tube as deposition nozzle and the effect of these tubes on the structural properties and optical properties of the prepared samples. X-ray diffraction (XRD) was employed to find the crystallite size. (XRD) studies show that the structure of a thin films changes from polycrystalline to amorphous by increasing the number of capillary tubes used in sample preparation. Maximum transmission can be measured is (95%) at three capillary tube. (AFM) where use to analyze the morphology of the tin oxides surface. Roughness and average grain size for different number of capillary tubes have b

Non-thermal plasmas have become popular as plasma technology has advanced in various fields, including waste management, aerospace technology, and medicinal applications. They can be used to replace combustion fuels in stationary hall motors and need little effort to keep running for longer periods of time. To improve overall system performance, non-reactive gases such as )Xe, Ar, and Kr) are utilized in pure or mixed form to generate plasma. Since DC glow discharge is a fundamental topic of importance, these gases have been researched. The paper concentrates on 2-D modeling and simulation. DC glow-discharge tubes are utilized with argon gas to create plasma and learn about its properties. The magnitude of the electron density, increases wi

In the present study, the effect of Zinc nanoparticles on levels of (T3 , T4 and TSH) hormones was investigated. Zinc nanoparticles were synthesized by Laser induced plasma.The Nd: YAG Nd: YAG laser with a wavelength of 1064 nm was used to generate nanomaterials of the elements (zinc) upon collision with target atoms. Plasma generated by different laser intensity is generated. After confirming the preparation of zinc nanoparticles, XRD, AFM was examined, and the effect of these substances on the thyroid gland (T3, T4, TSH) was observed for two doses of each component (1 ml / kg, 4 ml / kg) after conducting a cytotoxicity examination of the lymphocytes of the rats extracted from Rat spleen was 1.8% less toxic to zinc, and as noted The

The present study was conducted to determine histopathological changes caused by chronic effect of Nitrofurantoin(NFT) in The albino mice Testes. The Study included 40 mice were divided on the five groups: the first group taken distilled water and become control group . the remaining group which are exposure with NFT drug in concentration (100-150-200-250) mg / kg, respectively, Doses were given orally for a period (month and two months). The results of histopathological changes included occurrence of congestion in the blood vessel and degeneration of spermatogonia and aggregation of spermatids in the lumen of semineferous tubules and inhibition of spermatogensis process and decrease of sperm inside the lumen

Reduction of noise and vibration in spur gear experimentally by using asymmetric teeth profiles with tip relief was presented. Both of classical (symmetric) and asymmetric (with and without tip relief) spur gears are used in this work. Gear test rig was constructed to achieve torsional vibration measuring, and two modified cutters are designed and manufactured to achieve tooth profile modifications. First to cut asymmetric gear tooth with pressure angles (14.5^o/25 ^o) without tip relief for loaded and unloaded tooth sides respectively, and second to cut asymmetric gear tooth with pressure angles (14.5^o/25 ^o) for loaded and unloaded tooth sides respectively with tip relief to ach

We have studied the effect of applying an external magnetic field on the characteristics of iron oxide (IO) nanoparticles (NPs) synthesized by pulsed laser ablation in dimethylformamide (DMF). The NPs synthesized with and without applying of magnetic field were characterized by Fourier transformation infrared spectroscopy (FT-IR), UV–Vis absorption, scanning electron microscope (SEM), atomic force microscope (AFM), and X-ray diffraction (XRD). SEM results confirmed that the particle size was decreased after applying magnetic field.

Advancements in horizontal drilling technologies are utilized to develop unconventional resources, where reservoir temperatures and pressures are very high. However, the flocculation of bentonite in traditional fluids at high temperature and high pressure (HTHP) environments can lower cuttings transportation efficiency and even result in problems such as stuck pipe, decreased rate of penetration (ROP), accelerated bit wear, high torque, and drag on the drill string, and formation damage. The major purpose of the present research is to investigate the performance of low bentonite content water-based fluids for the hole cleaning operation in horizontal drilling processes. Low bentonite content water-based drilling fluids were formulated by re

2- amino -5- thiol-1,3,4- thiadiazole (S1) was prepared by cyclic locking of thiosemicarbazide in the presence of anhydrous sodium carbonate and CS2. diazotization of (S1) compound gave diazonium salt (S2) that reacts with different activated aromatic compounds to get the following azo compounds ,2 [(4- aminophenyl) diazenyl ] 1,3,4- thiazdiazole-5- thiol (S3) ,2-[4-amino- 1-naphthyl diazenyl] -1,3,4 – thiazdiazole-5-thiol (S4) , 3-amino-4-[(5- mercapto -1,3,4- thiadiazole -2-yl) diazenyl ] phenol(S5) ,1-[(5-mercapto-1,3,4-thiadiazole-2-yl) diazenyl] -2-naphthol (S6) , 5-{[4-(dimethylamino) phenyl] diazenyl}-1,3,4-thiadiazole-2- thiol(S7) ,5-{[4-(diethylamino) phenyl] diazenyl}-1,3,4- thiadiazole-2- thiol(S8) ,2- amino-5-[(5-mercapto-1,3