The pure ZnS and ZnS-Gr nanocomposite have been prepared
successfully by a novel method using chemical co-precipitation. Also
conductive polymer PPy nanotubes and ZnS-PPy nanocomposite
have been synthesized successfully by chemical route. The effect of
graphene on the characterization of ZnS has been investigated. X-ray
diffraction (XRD) study confirmed the formation of cubic and
hexagonal structure of ZnS-Gr. Dc-conductivity proves that ZnS and
ZnS-Gr have semiconductor behavior. The SEM proved that
formation of PPy nanotubes and the Gr nanosheet. The sensing
properties of ZnS-PPy/ZnS-Gr for NO2 gas was investigated as a
function of operating temperature and time under optimal condition.
The sensitivity,

In this paper, fire resistance and residual capacity tests were carried out on encased pultruded glass fiber-reinforced polymer (GFRP) I-beams with high-strength concrete beams. The specimens were loaded concurrently under 25% of the ultimate load and fire exposure (an increase in temperature of 700 °C) for 70 min. Subsequently, the fire-damaged specimens were allowed to cool and then were loaded statically until failure to explore the residual behaviors. The effects of using shear connectors and web stiffeners on the residual behavior were investigated. Finite Element (FE) analysis was developed to simulate the encased pultruded GFRP I-beams under the effect of fire loading. The thermal analyses were performed using the general-pu

Thin-walled members are increasingly used in structural applications, especially in light structures like in constructions and aircraft structures because of their high strength-to-weight ratio. Perforations are often made on these structures for reducing weight and to facilitate the services and maintenance works like in aircraft wing ribs. This type of structures suffers from buckling phenomena due to its dimensions, and this suffering increases with the presence of holes in it. This study investigated experimentally and numerically the buckling behavior of aluminum alloy 6061-O thin-walled lipped channel beam with specific holes subjected to compression load. A nonlinear finite elements analysis was used to obtain the

Under-reamed piles defined by having one or more bulbs have the potential for sizeable major sides over conventional straight-sided piles, most of the studies on under-reamed piles have been conducted on the experimental side, while theoretical studies, such as the finite element method, have been mainly confined to conventional straight-sided piles. On the other hand, although several laboratory and experimental studies have been conducted to study the behavior of under-reamed piles, few numer­ical studies have been carried out to simulate the piles' performance. In addition, there is no research to compare and evaluate the behavior of these piles under dynamic loading. Therefore, this study aimed to numerically investigate bearing capaci

The compounds 3-[4̄-(4˭-methoxybenzoyloxy) benzylideneamino]-2-thioxo-imidazolidine-4-one(3)aand 4-(1-(5-oxo- 2-thioxoimidazolidin-1-ylimino)ethyl)phenyl acetate(3)b were prepared from the reaction of aromatic aldehyde or ketone(1)a,bwith thiosemicarbazide to give aryl thiosemicarbazones(2)a,b ,followed by cyclization with ethylchloroacetate in the presence of fused sodium acetate. Treatment the compounds(3)a,bwith 4- hydroxybenzenediazoniumchloride yielded the correspondings4-((4-((4-hydroxyphenyl)diazenyl)-5-oxo-2- thioxoimidazolidin-1-ylimino)methyl)phenyl 4-methoxybenzoate(4)aand4-(1-(4-((4-hydroxyphenyl)diazenyl)-5-oxo-2- thioxoimidazolidin-1-ylimino)ethyl)phenyl acetate(4)b.The new 2-thioxo-imidazolidin-4-one with esters (5-7)a,b sy

The compounds 3-[4̄-(4˭-methoxybenzoyloxy) benzylideneamino]-2-thioxo-imidazolidine-4-one(3)aand 4-(1-(5-oxo- 2-thioxoimidazolidin-1-ylimino)ethyl)phenyl acetate(3)b were prepared from the reaction of aromatic aldehyde or ketone(1)a,bwith thiosemicarbazide to give aryl thiosemicarbazones(2)a,b ,followed by cyclization with ethylchloroacetate in the presence of fused sodium acetate. Treatment the compounds(3)a,bwith 4- hydroxybenzenediazoniumchloride yielded the correspondings4-((4-((4-hydroxyphenyl)diazenyl)-5-oxo-2- thioxoimidazolidin-1-ylimino)methyl)phenyl 4-methoxybenzoate(4)aand4-(1-(4-((4-hydroxyphenyl)diazenyl)-5-oxo-2- thioxoimidazolidin-1-ylimino)ethyl)phenyl acetate(4)b.The new 2-thioxo-imidazolidin-4-one with esters (5-7)a,b sy

One-third of the total waste generated in the world is construction and demolition waste. Reducing the life cycle of building materials includes increasing their recycling and reuse by using recycled aggregates. By preventing, the need to open new aggregate quarries and reducing the amount of construction waste dumped into landfills, the use of recycled concrete aggregate in drum compacted concrete protects the environment. Four samples of PRCC were prepared for testing (compressive strength, tensile strength, flexural strength, density, water absorption, porosity) as the reference mix and (10, 15, and 20%) of fine recycled concrete aggregate as a partial replacement for fine natural aggregate by volume. The mix is designed according to

         The aim of this investigation is to determine how different weight percentages of alumina nanoparticles, including 0.02, 0.04, and 0.06 percent wt, affect the physical characteristics of Poly Acrylamide (PAAM). Using a hot plate magnetic stirrer, 10 g of poly acrylamide powder was dissolved in 90 g of di-ionized distillate water for 4 hours to produce PAAM with a concentration of 0.11 g/ml. Four sections of the resulting solution, each with a volume of 20 ml, were created. Each solution was added independently with alumina nanoparticles in different ratios 0.0, 0.02, 0.04, and 0.06 to create four nano fluid solutions with different alumina nanoparticle contents based on each weight percent. The hand casting process for n