In this study we examine variations in the structure of perovskite compounds of LaBa2Cu2O9, LaBa2CaCu3O12 and LaBa2Ca2Cu5O15 synthesized using the solid state reaction method. The samples’ compositions were assessed using X-ray fluorescence (XRF) analysis. The La: Ba: Ca: Cu ratios for samples LaBa2Cu2O9, LaBa2CaCu3O12 and LaBa2Ca2Cu5O15 were found by XRF analysis to be around 1:2:0:2, 1:2:1:3, and 1:2:2:5, respectively. The samples’ well-known structures were then analyzed using X-ray diffraction. The three samples largely consist of phases 1202, 1213, and 1225, with a trace quantity of an unknown secondary phase, based on the intensities and locations of the diffraction peaks. According to the measured parameters a, b, and c, every sa

Sulphated zirconia (SZ) is one of the most important solid acid catalysts was synthesize at different operating conditions, different calcination temperature and sulfonating time has been used. The prepared catalyst was distinguished by X-ray Diffraction (XRD), particle size and morphology of catalyst were checked by atomic force microscopy (AFM) and scanning electron microscopy (SEM) respectively, in addition to analysis by (DTA) Differential thermally and Energy Dispersive X-Ray (EDX). Finally, the N2 adsorption-desorption was used to measure the surface area (BET) and pore volume. High degree of tetragonal crystallinity was obtained 90 %, and surface area of 169 m2/g and pore volume of 0.39 cm3g-1 at 600°C calcination temperature for 3

A progression of Polyaniline (PANI) and Titanium dioxide (TiO₂) nanoparticles (NPs) were prepared by an in-situ polymerization strategy within the sight of TiO₂ NPs. The subsequent nanocomposites were analyzed using Fourier-transform infrared spectra (FTIR), X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), and Energy Dispersive X-Ray Analysis (EDX) taken for the prepared samples. PANI/TiO₂ nanocomposites were prepared by various compound materials (with H₂SO₄ 0.3 M and without it, to compare the outcome of it) by the compound oxidation technique using ammonium persulfate (APS) as oxidant within the sight of ultrafine grade powder of TiO₂ cooled in an ice bath.

Thin films of In2O3-CdO at various CdO contents (0.01, 0.02, 0.03, 0.04 and 0.05) were deposited on transparent substrate which is glass using chemical spray pyrolysis deposition method at substrate temperature 150oC. The structural properties was studied to characterize the prepared materials by XRD analysis. Surface morphology has been illustrated using scanning electron microscopy which proved the nanosize of prepared materials. This materials have been used as gas sensor for toxic gas which is hydrogen sulfide H2S. The sensitivity and response speed have been investigated with addition of CdO nanoparticles. © 2021, S.C. Virtual Company of Phisics S.R.L. All rights reserved.

Suggested in this study the introduction of monomers have the ability to interact with polyester Rzn way confused or Alchapak Vodev polycarbonate first Almiaal acrylate ????? grains and offered models for high temperature and for a period of time of 40 days and absorbance and penetration and after color changes resulting from the storage heat higher using shades where models were extractedthermal storage and take measurements and then returned periodically results were consistent with theoretical expectations and mixing

This study was conducted in a laboratory experiment at the University of Baghdad, College of Science, computing Department, 5 km from the center of Baghdad city, in 2021 to evaluate the sorting method for the tomato crop. The experiments were conducted in a factorial experiment under a complete randomized design with three replications and using SAS analysis, artificial neural network, image processing, the study of external characteristics, and physical features; fruit surface area and fruit circumference were 1334.46 cm2,57.53 cm2 and free diseases. The error value was less than zero, while training with outputs recorded the highest value and which was 5. The neural network's performance between the input and the mean square of th

In this work, zinc oxide nanoparticles (ZnONPs) and sawdust/epoxy composite (20:80) were mixed using a simple molding method with different ZnONPs concentrations of (0.1, 0.3, 0.5, 0.7, and 1.0 %). The samples of the nanocomposites were characterized by the Scanning Electron Microscopy (SEM) technique to demonstrate the homogeneity of the prepared ZnONPs/nanocomposites. The photocatalytic activity of the samples was examined using the methylene blue (MB) dye as a pollutant solution, through evaluation of the efficiency of the prepared compound in the treatment of organic pollutants under illumination by sunlight. The photocatalytic results showed that after 240 minutes of exposure to sunlight, the sample prepared using (0.5 vol.% of ZnON

Lead selenide PbSe thin films of different thicknesses (300, 500, and 700 nm) were deposited under vacuum using thermal evaporation method on glass substrates. X-ray diffraction measurements showed that increasing of thickness lead to well crystallize the prepared samples, such that the crystallite size increases while the dislocation density decreases with thickness increasing. A.C conductivity, dielectric constants, and loss tangent are studied as function to thickness, frequency (10kHz-10MHz) and temperatures (293K-493K). The conductivity measurements confirm confirmed that hopping is the mechanism responsible for the conduction process. Increasing of thickness decreases the thermal activation energy estimated from Arhinus equation is

The effect of Al dust particles on glow discharge regions, discharge
voltage, discharge current, plasma potential, floating potential,
electron density and electron temperature in planar magnetron
sputtering device has been studied experimentally. Four cylindrical
Langmuir probes were employed to measure plasma parameters at
different point on the radial axis of plasma column. The results
shows the present of Al dust causes to increase the discharge voltage
and reduce the discharge current. There are two electron groups in
the present and absent of Al dust particles. The radial profiles of
plasma parameters in the present of dust are non- uniform. The
floating potential of probe becomes more negatively while