Thin films of pure tin mono-sulfide SnS and tin mono-sulfide for (1,2,3,4)% fluorine SnS:F with Thicknesses of (0.85 ±0.05) ?m and (0.45±0.05) ?m respectively were prepared by chemical spray pyrolysis technique. the effect of doping of F on structural and optical properties has been studied. X-Ray diffraction analysis showed that the prepared films were polycrystalline with orthorhombic structure. It was found that doping increased the intensity of diffraction peaks. Optical properties of all samples were studied by recording the absorption and transmission spectrum in range of wave lengths (300-900) nm. The optical energy gap for direct forbidden transi

Quantum dots (QDs) can be defined as nanoparticles (NPs) in which the movement of charge carriers is restricted in all directions. CdTe QDs are one of the most important semiconducting crystals among other various types where it has a direct energy gap of about 1.53 eV. The aim of this study is to exaine the optical and structural properties of the 3MPA capped CdTe QDs. The preparation method was based on the work of Ncapayi et al. for preparing 3MPA CdTe QDs, and hen, the same way was treated as by Ahmed et al. via hydrothermal method by using an autoclave at the same temperature but at a different reaction time. The direct optical energy gap of CdTe QDs is between 2.29 eV and 2.50 eV. The FTIR results confirmed the covalent bonding betwee

The electrical properties of polycrystalline cadmium telluride thin films of different thickness (200,300,400)nm deposited by thermal evaporation onto glass substrates at room temperature and treated at different annealing temperature (373, 423, 473) K are reported. Conductivity measurements have been showed that the conductivity increases from 5.69X10-5 to 0.0011, 0.0001 (?.cm)-1 when the film thickness and annealing temperature increase respectively. This increasing in ?d.c due to increasing the carrier concentration which result from the excess free Te in these films.

BACKGROUND: Acute appendicitis (AA) remains a complex case even for experienced surgeons. Rate of negative appendectomy is 5–40% and delayed intervention result in perforated appendicitis in 5–30% of cases. AIM: The aim of the study was to evaluate NPT as a marker for the diagnosis of AA concerning its severity. And compare the diagnostic value of it with the ALV scoring system. METHODS: One hundred twenty patients presented with signs and symptoms of AA and underwent appendectomy, only 84 patients proved to be AA by histopathological examination, were included in the study. Blood samples for neopterin (NPT) estimation and Alvarado (ALV) score was calculated. Control group consists of 45 healthy individual. RESULTS: NPT levels were s

The Glass Manegerie is a metaphor, which is one of the greatest plays  of great writer Williams. The play talks about  the poor people in society and how try to escape this group of people from the real world to get rid of the hardness of this tuff reality and live in a fantasy world that is much like the glass where the world is very weak this world is acting by Laura, she is  owner of these animals breakable glass where it's weak and unable to defend itself as well as the mother Amanda  is a very selfish never think about her children but only herself.

This research investigates new glasses which are best suitable for design of optical systems
working in the infrared region between 1.01 to 2.3μm. This work is extended to Oliva & Gennari
(1995,1998) research in which they found that the best known achromatic pairs are (BAF2-IRG2; SRF2-
IRG3; BAF2-IRG7; CAF2-IRGN6; BAF2-SF56A and BAF2-SF6). Schott will most probably stop the
production of these very little used and commercially uninteresting IRG glasses. In this work equally
good performances can be obtained by coupling BAF2, SRF2&CAF2 with standard glasses from Schott
or Ohara Company. The best new achromatic pairs found are (SRF2-S-TIH10; CAF2-S-LAL9; CAF2-SLAL13
and CAF2-S-BAH27). These new achromatic pai

In this research, deposition of titanium oxide (TiO₂) and vanadium oxide (V₂O₅) thin film  in different mixing percentage  (0, 25 ,50, 75 and100)%   on the substrate of glass .The coating thickness was ( 50 nm  ).

In this research contact angle was measured and the effect of weather conditions. Results showed that the value of the contact angle of the prepared films reached its highest value at 50% (TiO₂+V₂O₅) was 160º.

The results showed that the optical transmittance of TiO₂ and V₂O₅ thin film decrease with increasing the deposition angle and decrease with increasing V₂O₅ pro

The current research was conducted to report the synthesis of alumina powder from Iraqi kaolin. The kaolin was transformed to metakaolin by calcinations at temperature 800 °C for three hours. Then the calcined kaolin was treated with (1.5 M) from H2SO4 for 6 hours to form Al2(SO4)3.12H2O solution. The precipitate was dried at 80oC for 10 hours and calcinations at different temperatures for two hours. The samples which result was characterized by X–Ray diffraction (XRD) and X–Ray fluorescence (XRF). The results indicate to the crystalline hydrate aluminum sulfate for the sample that be as – synthesis and when calcinations at 600 oC transformed into aluminum sulfate phase. The phases of alumina which we obtain consisted of a gamma a