Two molecular imprinted polymer (MIP) membranes for Levofloxacin (LEV) were prepared based on PVC matrix. The imprinted polymers were prepared by polymerization of styrene (STY) as monomer, N,N methylene di acrylamide as a cross linker ,benzoyl peroxide (BPO) as an initiator and levofloxacin as a template. Di methyl adepate (DMA) and acetophenone (AOPH) were used as plasticizers , the molecular imprinted membranes and the non molecular imprinted membranes were prepared. The slopes and detection limits of the liquid electrodes ranged from -21.96 – -19.38 mV/decade and 2×10-4M- 4×10-4M, and Its response time was around 1 minute, respectively. The liquid electrodes were packed with 0.1 M standard drug solution and its response were stable at pH ranges from 1.0 to 11.0 and with good selectivity for more than several type. The electrodes produced have been successfully applied in preparation of the pharmaceutical sample for the determination of the analyte without any time consuming pretreatment steps.
In this research, two drugs were bonded through amide and ester attachment, using lactic acid as aspacer binder, produced di pro drug such as Procain and Ciprofloxacin. Since Procain has ailocail anesthetic action and Ciprofloxacin as antibacterial drug was reacted with lactic acid produced ester compound (1), then the carboxylic acid of lactic acid could reacted with free Procain oil produced amide attachment, the controlled drug release in different pH values at 37C˚was studied to improve their characteristic and to minimize the side effect of the drug could be used in broad spectrum activity as atherapeutic material.This mutual prodrug was used with another biological active drug instead of single action. The prepared prodrug was charac
... Show MoreThe interest in calcium phosphates arises from the fact that bones contain a high percentage of mineralized calcium phosphate . In this study, pure and biocompatible hydroxyapatite (HAP) powder was successfully synthesized using hen’s egg shell as calcium source and phosphoric acid by precipitation method.The precipitate obtained was subjected to ripenning process for 24 hours, filtered, air dried, and calcined at temperatures of 400,800,900,and 1000 ºC.
X-Ray diffraction(XRD) technique was used to investigate the formation of HAP powder, XRD results revealed the HAP formation and also indicate no occurrence of secondary phases. Fourier Transform Infrared(FT-IR) spectrum shows the characterstic peaks for phosphate and hydroxyl grou
In the present study a series of some four-,five-and seven-membered heterocyclic compounds have been synthesized by the reaetion of Schiff bases (1a,b) with chloroacetyl chloride, sodium azide, thioglycolic acid or various anhydrides to give azetidinone (2a,b), tetrazole (3a,b), thiazolidinone (4a,b) and 1,3-oxazepine derivatives (5-8a,b) respectively. Schiff bases (1a,b)were prepared from the reaction of p-toluidine with aromatic aldehydes. All synthesized compounds were characterized by physical properties and spectral data.
New series of Schiff bases 2(a-j) and corresponding beta-lactam derivatives 3(a-j) were synthesized from cefalexin (1) as starting material. The compound (1) was reacted with different aldehydes and ketones to give Schiff bases derivatives 2(a-j). The synthesized Schiff bases were cyclized by chloroacetyl chloride in the presence of triethylamine to form beta-lactam derivatives 3(a-j). The compounds were characterized by deremination melting point, FT-IR and 1H NMR. The beta-lactam derivatives were screened in vitro antibacterial against some bacterial species
(1)
Activated carbon loading with metals oxides is new adsorbents and catalyst, which seem very promising for desulfurization process. The present study deals with the preparation of three metals oxides loaded on activated carbon (AC). The tri composite of ZnO/NiO/CoO/AC was characterized by X-Ray Diffraction (XRD), X-Ray florescence (XRF), N2 adsorption for BET surface area, pore volume and Atomic Force Microscopy (AFM). The effect of calcination temperature is investigated. The best calcination temperature is 250oC based on the presence of phase, low weight loss and keep at high surface area. The surface area and pore volume of prepared tri composite are 932.97m2/g and 0.6031cm3/g respec
... Show MoreThis work illustrates an enhanced visible light photocatalytic degradation of methyl orange dye (M.O.) by employing BiOI / BiOCl composites prepared under room temperature and without any organic precursors. Various experimental parameters have been studied, namely; composition of the composite, irradiation time and cell material. Composition D which implied 75% BiOI and 25% BiOCl has shown the highest bleaching of M.O. dye. This confirms the optimum photo-sensitization phenomenon for this composition in comparison to others. In the optimum photo-sensitized composite the electron of the conduction band reveals better reducing power and the hole of the valence band exhibits more oxidative power than those of pure BiOI electron and hole. Acco
... Show More
The present work involved synthesis of serval new substituted tetrazole via Schiff bases for trimethoprim drug by two steps. The first step involved direct reaction of different ketones and aldehydes with trimethoprim producing the corresponding Schiff bases (1-10), whereas the second step, involved preparation new tetrazoles derivatives (11-20) through reaction of the ready Schiff bases (in the first step) with sodium azidein in dioxin. The prepared compounds were characterized by UV, FT-IR, and some of them by 13C-NMR, 1H-NMR spectroscopy and physical properties.
Phenol condensed with β-keto esters via Pechmann condensation to form derivatives of Coumarin in various reaction conditions by two ways. Present paper is comparative study of synthesis Coumarin with the yield of product , reaction time and reaction conditions.
The sol-gel route using an agar gel with calcium nitrate and phosphate solution as starting materials for producing hydroxyapatite (HAP). The product formed were needle like, zigzag and straight fibres. The fibrous products on sintering transformed into stoichiometric HAP with a biological Ca/P ratio of 1.67. The influences of pH, temperature, nature of base and phosphate solution on the growth of fibrous HAP were studied. The pH of the solution was found to greatly influence the growth rate and morphology of the resultant product. The optimum gel temperature was found to be 60oC and sintering temperature of 900oC for 1 hour. The crystalline, thermal, functional and morphological characteristics of the fibrous HAP were investigated.
Some esters were prepared from reaction of different molecular weight of PVA with some acid chloride (prepared by reaction of acid with thionyl chloride or phosphorous pentachloride)in the presence of pyridine. The thermal and reological properties were studied. The increasing Of bulky groups decreasing stability of the thermal and reological properties.