Nanocrystalline copper sulphide (Cu2-xS) powders were synthesized by chemical precipitation from their aqueous solutions composed of different molar ratio of copper sulfate dehydrate (CuSO4.5H2O) and thiorea (NH2)2CS as source of Cu+2, S-2 ions respectively, and sodium ethylene diamine tetra acetic acid dehydrate (EDTA) as a complex agent. The compositions, morphological and structural properties of the nanopowders were characterized by energy dispersive spectroscopy (EDS), scanning electron microscope (SEM), and X-ray diffraction (XRD), respectively. The compositional results showed that the copper content was high and the Sulfur content was low for both CuS and Cu2S nanopowders. SEM images shows that all products consist of aggregate o

Activated carbon loading with metals oxides is new adsorbents and catalyst, which seem very promising for desulfurization process. The present study deals with the preparation of three metals oxides loaded on activated carbon (AC). The tri composite of ZnO/NiO/CoO/AC was characterized by X-Ray Diffraction (XRD), X-Ray florescence (XRF), N₂ adsorption for BET surface area, pore volume and Atomic Force Microscopy (AFM). The effect of calcination temperature is investigated. The best calcination temperature is 250^oC based on the presence of phase, low weight loss and keep at high surface area. The surface area and pore volume of prepared tri composite are 932.97m²/g and 0.6031cm³/g respec

The work include synthesis of nanocomposites (X / S / Ag) based on blend from Xanthan gum / sodium alginate polymers (X / S) with different loading of synthesized silver nanoparticales (0.01, 0.03 and 0.05 wt%) were added to the blend. The silver nanoparticles were prepared by reduction method and were characterized and analyzed using X-ray diffraction (XRD) and Atomic force microscope (AFM). XRD study showed the presence nanoparticle of silver with crystalline nature and face-centered cubic (FCC) structure and an average size of nanoparticles ranging from 32 to 37 nm. The surface study was performed using AFM which showed a fairly uniform shape to the nanocomposites and a spherical nature for the silver nanoparticles. The nanocomposite exh

Five N-substituted acrylamides were prepared by reaction of substituted aromatic primary amines with acryloyl chloride in the presence of triethyl amine. The synthesized acrylamides were allowed to introduce copolymerization reaction with three vinylic monomers including acrylonitrile, methyl acrylate and methyl methacrylate respectively to obtain eleven new copolymers having different physical properties which may used in different applications.

This work illustrates an enhanced visible light photocatalytic degradation of methyl orange dye (M.O.) by employing BiOI / BiOCl composites prepared under room temperature and without any organic precursors. Various experimental parameters have been studied, namely; composition of the composite, irradiation time and cell material. Composition D which implied 75% BiOI and 25% BiOCl has shown the highest bleaching of M.O. dye. This confirms the optimum photo-sensitization phenomenon for this composition in comparison to others. In the optimum photo-sensitized composite the electron of the conduction band reveals better reducing power and the hole of the valence band exhibits more oxidative power than those of pure BiOI electron and hole. Acco

ZnS nanoparticles were prepared by a simple microwave irradiation method under mild condition. The starting materials for the synthesis of ZnS quantum dots were zinc acetate (R & M Chemical) as zinc source, thioacetamide as a sulfur source and ethylene glycol as a solvent. All chemicals were analytical grade products and used without further purification. The quantum dots of ZnS with cubic structure were characterized by X-ray powder diffraction (XRD), the morphology of the film is seen by scanning electron microscopy (SEM). The particle size is determined by field effect scanning electron microscopy (FESEM), UV-Visible absorption spectroscopy and XRD. UV-Visible absorption spectroscopy analysis shows that the absorption peak of the as-prep

The ligand 4-(2-aminmo-5-nitro-phenylazo)-1,5-dimethyl-2-phenyl-1,2-dihydro-pyrazol-3-one derived from 4-aminoantipyrine and 4-nitroaniline was synthesized. The synthesized ligand was characterized by 1HNMR, FT-IR, UV-Vis spectra and (C.H.N) analysis. Complexes of (YIII and LaIII ) with the ligand were prepared in aqueous ethanol with a 1:2 M:L ratio and at optimum pH. The prepared complexes were characterized by using flame atomic absorption, FT-IR, UV-Vis spectra,(C.H.N) analysis and conductivity measurement. The stoichiometry of complexes was studied by the mole ratio and job methods. A concentration range (1×10-4 - 3×10-4 M) obeyed Beer's law, the complex solutions show high values of molar absorption. On the basis of physicochemical

The ligand 4-(2-aminmo-5-nitro-phenylazo)-1,5-dimethyl-2-phenyl-1,2-dihydro-pyrazol-3-one derived from 4-aminoantipyrine and 4-nitroaniline was synthesized. The synthesized ligand was characterized by 1HNMR, FT-IR, UV-Vis spectra and (C.H.N) analysis. Complexes of (YIII and LaIII ) with the ligand were prepared in aqueous ethanol with a 1:2 M:L ratio and at optimum pH. The prepared complexes were characterized by using flame atomic absorption, FT-IR, UV-Vis spectra,(C.H.N) analysis and conductivity measurement. The stoichiometry of complexes was studied by the mole ratio and job methods. A concentration range (1×10-4 - 3×10-4 M) obeyed Beer's law, the complex solutions show high values of molar absorption. On the basis of physicochemical