I've been in this work to prepare some complexes containing mixed Kandat with some transitional elements which new complexes according to the best of our knowledge and to refer to the information from the Internet until I have been studying this diagnosis Aalmakdat

Summary of the research in English:

the research seeks to define the provisions of voluntary charity and some of its contemporary applications, so the research is after the definition of charity and voluntary charity, define the provisions of the Most important thing charity, where the one who is given charity, in the introduction, he talked about the importance of charity in social solidarity,As for the first topic ,it deait with a statement and definition of charity in the Quran,sunnah and comparative juris prudence,whil the second topic was conducted with clarifying the provisions of the ratified, the ratified,while the third topic was concerned with clarifying the application of voluntary charity contemporary investing the Mo

Background Alloys with the addition of zirconium and niobium eliminate the adverse effects of aluminum and vanadium on the nervous system, the possibility of metallosis and the initiation of diseases (including cancers or Alzheimer›s disease). In addition, they have better corrosion resistance, and a Young›s modulus value similar to longitudinal bone tissue. Therefore, only choosing appropriate materials does not guarantee proper functioning of the implants, the surfaces of the implants also have to be suitable to meet the requirements. The laser surface hardening process modifies the surface properties by imparting microstructural changes, whereas surface remelting induces changes in the surface topography, roughness, wettability and w

The structural properties of ternary chalcopyrite AgAlSe2 compound alloys and thin films that prepared by the thermal evaporation method at room temperature on glass substrate with a deposition rate (5±0.1) nm s-1 for different values of thickness (250,500 and 750±20) nm, have been studied, using X-ray diffraction technology. As well as, the optical properties of the prepared films have been investigated. The structural investigated shows that the alloy has polycrystalline structure of tetragonal type with preferential orientation (112), while the films have amorphous structure. Optical measurement shows that AgAlSe2 films have high absorption in the range of wavelength (350-700 nm). The optical energy gap for allowed direct transition we

   The chemicals materials were used to study the effect of citric acid, detergents, sodium carbonate, sodium bicarbonate on the vitality of the third stage of mosquito Culex pipiens molestus. The highest larvicidal efficacy was established from citric acid solution followed by detergents solution, sodium carbonate, sodium bicarbonate with (LC₅₀) values 2096, 2715, 13930, 13960 ppm respectively. The concentration of 1000 ppm of citric acid showed a fatal effect on the third stage larvae of mosquitoes which gave a mortality percent of 100% on the second day of the treatment. It was followed by the concentrations of 750 ppm and 500 ppm respectively which caused the death of all larvae on the fifth and sixth days respe

To achieve sustainability in the field of civil engineering, there has become a great interest in developing reactive powder concrete RPC through the use of environmentally friendly materials to reduce the release of CO₂ gas produced from cement factories as well as contribute to the recycling of industrial wastes that have a great impact on environmental pollution.

In this study, reactive powder concrete was prepared using total binder content of 800 kg/m³, water to binder ratio (0.275), and micro steel fibers  1% by volume of concrete. The experimental program included replacing fly ash with (8, 12, 16) % by cement weight to find the optimal ratio, which achieved the best mechanical proper

Physical adsorption by nitrogen gas was studied on seven commercial platinum reforming catalysts (RG-402, RG-412, RG-432, RG-451, RG 422,RG-482, PS-10), four prepared platinum catalysts (0.1%Pt/alumina, 0.2 %Pt/alumina, 0.45 %Pt/alumina and 0.55% Pt/alumina), and -alumina support. Physical adsorption was carried out by using Accelerated Surface Area and Porosimetry (ASAP 2400 device) at 77 K . The results indicate that the surface area in genaral decreases with increasing platinum percentage, high platinum loaded (0.45% and 0.55%) it was found that the percent increasing in surface area was lower than those obtained for low platinum loaded catalysts , and at very higher platinum loading 0.6 %Pt , some reduction in surface area was

Background: The present study aimed to determine the influence of the different types of mouth wash on discoloration of different orthodontic ceramic, sapphire brackets and adhesives. Materials and methods: The sample composed of 120 ceramic brackets and 120 sapphire brackets, the brackets were divided according to bond material into three groups of 40 brackets include unbounded brackets, chemically cured (no-mix) bonded brackets and Light cured bonded brackets all these groups were further subdivided according to mouth wash type into three groups with 10 brackets each which include; Listerine, cetrimide, chlorhexidine 0.2%, and one control group which immersed in artificial saliva; then Staining measurements were performed with UV-Visibl