This article presents the simultaneous adsorption of bimetal Cu²⁺ and Zn²⁺ from an aqueous solution using activated carbon synthesized from a plum seed precursor by sulfuric acid and microwave activation: plum seeds chemically activated by 45% (w/w) sulfuric acid with 2:1 ratio for 4 h, then carbonized for 2 h at 700 °C and the product obtained activated in a microwave oven for 20 min at 700 W for final of activation. Plum seeds and activated carbon produced were characterized in terms of their physical and chemical composition using Brunauer–Emmett–Teller measurements, field emission scanning electr

Designing high-performance solid polymer electrolytes (SPEs) remains a key challenge, primarily due to their inherently low ionic conductivity, which hampers the advancement of all-solid-state lithium-ion batteries (ASSLiBs). In this work, we address this limitation by developing a green, crosslinked polymer blend comprising carboxymethyl cellulose (CMC) - extracted and functionalized from palm frond fibers - and poly (vinyl alcohol) (PVA). Citric acid (CA) was utilized as a crosslinking agent, while lithium perchlorate (LiClO4) was incorporated as a dopant to enhance ionic conductivity. The SPE membranes were fabricated via solution casting, with the optimized formulation - designated CP-15X-Li25 - containing 15 wt.-% CA and 25 wt.-% LiClO

The integration of nanomaterials in asphalt modification has emerged as a promising approach to enhance the performance of asphalt pavements, particularly under high-temperature conditions. Nanomaterials, due to their unique properties such as high surface area, exceptional mechanical strength, and thermal stability, offer significant improvements in the rheological properties, durability, and resistance to deformation of asphalt binders. This research reviewed the application of various nanomaterials, including nano silica, nano alumina, nano titanium, nano zinc, and carbon nanotubes in asphalt modification. The incorporation of these nanomaterials into asphalt mixtures has shown potential to increase the stiffness and high-tempera

<p>The polyacrylonitrile (PAN)/polysulfone (PSF) blended polymer membranes were modified by decaethylene glycol monododecyl ether (C₁₂EO₁₀) as a non-ionic surfactant. Polymeric solutions containing 17 wt.% of both PAN and PSF with a ratio of 80/20, and C₁₂EO₁₀ with a mass concentration of 6 wt.% and aluminium oxide (Al₂O₃) nanoparticles with varying concentrations (1, 2, and 3 wt.%) were prepared. Adding 6 wt.% of C₁₂EO₁₀ to the casting solution formed a membrane with distinguished hydrophilicity and fouling resistance, higher porosity, appreciable pe

Glass fiber–reinforced polymer (GFRP) reinforcement provides an effective alternative to conventional steel in concrete structures due to its corrosion resistance. Nevertheless, the lower elastic modulus of GFRP necessitates careful consideration of serviceability behavior in GFRP-reinforced concrete members. This study presents a numerical sectional analysis model for predicting the flexural response and ultimate capacity of hybrid reinforced concrete beams incorporating embedded GFRP profiles in combination with either mild steel or GFRP reinforcement bars under monotonic static loading. The proposed model employs realistic nonlinear stress–strain relationships for concrete and steel, together with secant moduli of elasticity

All the prepared metal complexes of Pt (IV), Au(III), Rh (III), Co (II) and V(IV) with new ligand sodium [5-(p-nitro phenyl)-/4-phenyl-1,2,4-triazole-3-dithiocarbamato hydrazide] (TRZ.DTC) have been synthesized and characterized in solid state by using flame atomic absorption, elemental analysis C.H.N.S, FT-IR ,UV-Vis Spectroscopy, conductivity and magnetic susceptibility measurements. The nature of the complexes formed in ethanolic solution has been studied following the molar ratio method also was studied stability constant and found to be stable in molar ratio1:1 of VL (IV) and CoL(II) while Pt(IV), Au(III) and Rh(III) complexes stable in molar ratio 1:2 as well as the molar absorptivity for these complexes were calculated. From the prev