Carbon nanoparticles are prepared by sonication using carbon black powder. The surface morphology of carbon black (CB) and carbon nanoparticles (CNPs) is investigated using scanning electron microscopy (SEM). The particles size ranges from 100 nm to 400 nm for CB and from 10 nm to 100 nm for CNPs. CNPs and CB are mixed with silicon glue of different ratios of 0.025, 0.2, 0.05, and 0.1 to synthesis films. The optical properties of the prepared films are investigated through reflectance and absorbance analyses. The ratio of 0.05 for CNPs and CB is the best for solar paint because of its higher solar water heater efficiency and is then added to the silicon glue . Temperature of cold water and temperature of hot water in storage tank were ta

In this work, the effect of partial amounts of gases in gas mixture of a CW CO2 laser on the output power was investigated. Also their effect on the condition determining the glow-discharge self-sustaining required for pumping the active medium was studied. Two fit relations were derived to predict the output laser power and the electric field to unit pressure ratio as functions to the partial amounts of gases. Results presented in this work could be used fruitfully to determine some of the optimum operational conditions of glow-discharge low-power CW CO2 lasers.

In this work, varying compositions of SiO₂ micro filler were added
with the Polyvinyl Chloride (PVC) and samples have been prepared
using film casting technique. The results have been analyzed and
compared for PVC samples with (1 wt%, 3 wt%, 5 wt% and 10 wt%)
SiO2 micro filler. Mechanical characteristics such as tensile strength,
elongation at break and Young`s modulus were measured for all the
samples, where the tensile strength was increased from 8.39 Mpa for
purified PVC to 16 Mpa for 3% SiO₂/PVC composite. Also, thermal
conductivity measurement values illustrated that composite materials
have a good thermal insulation at 10 wt. %, thermal conductivity was
decreased from 0.1684 W/m.

The sustainable competitive advantage for organizations is one of the requirements for value creation, which centered on the possession of scarce resources that achieve maximum flows to invest in intellectual capital, if what has been interest in them, measured and employed the way properly and style, so I figured the need for new technologies to enable organizations to measure the intellectual and physical assets and to assess its performance accordingly, so it sheds search light on the measurement of the added value of existing knowledge using the standard value-added factor is the intellectual (value added intellectual coefficient) (VAIC) and to develop a set of assumptions about the extent of the difference between the sample

fication of benzaldehyde (C6H5CHO) and O- amino aniline O-C6H4(NH2)2 in ethanol with 8- Hydroxyquinoline (8HQ) . Formed compounds were acquired of 1:1:2 molar proportion reactions for metal ions and ligands (L) and 2(8HQ) during reaction for MCl2 .nH2O salt products complexes conformable into the forms [M(L)(8HQ)2] ,where M = Mn(II),Co(II) and Ni(II). Whole the compounds were identified during the basis of their; FT-IR and U.V spectrum, melting point, molar conduct, identify of the percentage from the metal at the complexes via flame (AAS), C, H and N content of the Schiff base (L) and metal complexes were analysis and magnetic susceptibility menstruations. A hexagonal coordinated metal complexes were proposed to the separated complexes of

أجريت هذه الدراسة في محافظة النجف بالعراق لتحليل عينات بيولوجية من المدخنين وغير المدخنين. تم استخدام العينات، بما في ذلك مصل الدم والبول والشعر والأظافر، كمؤشرات حيوية لتحديد تركيزات اليورانيوم (UC) ونظائره (238U، 235U، و234U). وباستخدام طريقة التعرض الطبيعي، تم استخدام كاشف المسار النووي (CR-39، المملكة المتحدة) لقياس تركيزات اليورانيوم في العينات. تم جمع خمسة وسبعين عينة من مصل الدم والبول والشعر والأظافر للمد