In this research, Mn-doped TiO2 thin films were grown on glass, Si and OIT/glass substrates by R.F magnetron sputtering technique with thicknesses (250 nm) using TiO2:Mn target under Ar gas pressure and power of 100 Watt. Through the results of X-ray diffraction, the prepared thin films are of the polycrystallization type after the process of annealing at 600°C for two hour The average crystalline size were 145.32, 280.97 and 261.23 nm for (TiO2:Mn) thin film on glass, Si and OIT/glass substrates respectively, while the measured surface roughness is between 0.981nm and 1.14 nm. The fabricated (TiO2:Mn) thin film on glass sensors have high sensitivity for hydrogen( H2 reducing gas) compared to the sensitivity for hydrogen gas on Si and OIT/

The present research was conducted to reduce the sulfur content of Iraqi heavy naphtha by adsorption using different metals oxides over Y-Zeolite. The Y-Zeolite was synthesized by a sol-gel technique. The average size of zeolite was 92.39 nm, surface area 558 m²/g, and pore volume 0.231 cm³/g. The metals of nickel, zinc, and copper were dispersed by an impregnation method to prepare Ni/HY, Zn/HY, Cu/HY, and Ni + Zn /HY catalysts for desulfurization. The adsorptive desulfurization was carried out in a batch mode at different operating conditions such as mixing time (10,15,30,60, and 600 min) and catalyst dosage (0.2,0.4,0.6,0.8,1, and 1.2 g). The most of the sulfur compounds were removed at 10 min for all catalyst ty

The molluscicidal effects of herbicide 2, 4-D were studied against tow species of freshwater snail Bulinus truncatus and Melanopsis nodosa by short term experiments. Calculated values of lethal concentrations (LC50 and LC100) were maid to two spices for different period of time 24hr, 48hr, 72hr and 96hr. The study had showed that the herbicide 2, 4-D was toxic against the tow species. The toxicity of the herbicide was low or unknown in low concentrations in the first period of exposure 24and 48hr to two spices but it increase gradually with increase period of exposure. The spice of B.truncatus was more tolerant than the M.nodosa. All the individual of M nodosa was death while in B.truncatus the complete death was not appear until finish the

In this research, 5- membered heterocyclic compounds as oxazolidine-5-one J1-J5 derivatives were prepared using primary aromatic amine, aromatic carbonyl compounds and chloroacetic acid. By combining primary aromatic amines and aromatic carbonyl compounds, Schiff's bases were synthesized. Schiff bases are used with the chloroacetic acid compound to prepare oxazolidine-5-one J1-J5 derivatives. The compounds J1-J5 were described using NMR spectroscopy and FT-IR. .The biological efficacy was evaluated according to maximum inhibitory concentrations (MICs) toward Staphyloccoccus aureus and Esherichia coli. The best MIC was 210 μg ml-1 for J4 against the two pathogenic bacteria, while J1, J4, and J1 did not show any inhibitory effect against all

This study aimed to determine the effect of green bismuth oxide (BiO) NPs against multidrug-resistant (MDR) Pseudomonas aeruginosa (P. aeruginosa) from wound infections. Among 450 wound samples collected from patients admitted to the hospital, 200 P. aeruginosa isolates were identified. MDR strains of P. aeruginosa were detected by disc diffusion method. BiO NPs were synthesized using wild Bacillus subtilis (B. subtilis) strain and infrared spectroscopy, X-ray diffraction and scanning electron microscopy techniques. The antibacterial effect of the NPs compared to antibiotics against MDR strains was evaluated using a standard disk diffusion method. BiO NPs were synthesized at 0.005 M concentration of solution. According to the SEM im

         Beryllium Zinc Oxide (Be_xZn_1-xO) ternary nano thin films were deposited using the pulsed laser deposition (PLD) technique under a vacuum condition of 10^-3 torr at room temperature on glass substrates with different films thicknesses, (300, 600 and 900 nm). UV-Vis spectra study found the optical band gap for Be_0.2Zn_0.8O to be  (3.42, 3.51 and 3.65 eV) for the (300, 600 and 900nm) film thicknesses, respectively which is larger than the value of zinc oxide ZnO (3.36eV) and smaller than that of beryllium oxide BeO (10.6eV). While the X-ray diffraction (XRD) pattern analysis of ZnO, BeO and Be _0.2 Zn _0.8 O powder and nano-thin films indicated a hexa

Medicinal plants are a source for a wide variety of natural active compounds and are used for the treatment of diseases throughout the world. Conocarpus erectus L. widely planted all over Iraq and has different secondary metabolites, which has been used in treatment of anemia, cancer, fever and diarrhea. The present study aims to estimate the antibacterial activity of Conocarpus erectus leaves extracts on some microorganisms collected from patients with burn infection. The study began with the collection of Conocarpus erectus leaves in June 2018 from the trees in university of Baghdad. Maceration method was used to prepare aqueous extract, while Soxhelt apparatus was used to prepare methanolic extract. The results of phytochemical test show

The present study envisaged utilizing 4-aminoantipyrine as key intermediate for the synthesis of some new derivatives bearing anti-bacterial and anti-cancer activities moieties viz., antipyrine diazenyl benzaldehydes 2(ad) which were obtained by coupling of diazotized 4-aminoantipyrine (1) with substituted benzaldehydes at 0◦C (iced) temperature. The other antipyrine derivatives where containing bis heterocycles like bis thiazolidinone-antipyrine (4), bis imidazolidinone -antipyrine (5) and bis azetidinone -antipyrine (6).These compounds were prepared through the reaction between 4- aminoantipyrine and terephthaldicarboxaldehyde to get (3) which were reacted with mercaptoacetic acid , glycine or chloroacetyl chloride separately to get com

Coupling reaction of 4-aminoantipyrene with 8-hydroxyqunoline gave the new bidentate azo ligand 5-(4-antipyrene azo)-8-hydroxyqunoline. Treatment of this ligand with the following metals ions (MnII, CoII, NiII, CuII and ZnII) in aqueous ethanol with a 1:2 M:L ratio yielded a series of neutral complexes of the general formula [M(L)2Cl2]. The prepared complexes were characterized using flame atomic absorption, FT.IR, UV-Vis spectroscopic as well as magnetic susceptibility and conductivity measurements. Chloride ion content were also evaluated by (Mohr Method). From above data, the proposed molecular structure for these complexes as octahedral geometry.