Pharmaceuticals are widely distributed in different applications and also released into the environment. Adsorption of Ciprofloxacin HCl (CIPH) on Porcelinaite was studied at ambient conditions. The adsorption isotherms can be well described using the Freundlich and Temkin equations. The pH of the solution influences significantly the adsorption capacity of Porcelinaite, the adsorption of CIPH increased from the initial pH 1.3 and then decreased over the pH rang of 3.8-9. The adsorption is sensitive to the change in ionic Strength, which indicate that electrostatic attraction is a significant mechanism for sorption process. The enthalpy change (ΔH) for the adsorption of CIPH onto Porcelinaite signifies an endothermic adsorption. The ΔG va

Abstract Background: Dne of the key component of nasal tipplasty is effecter control of naral tip projection. Several cartilage grafts have been decreased for this purpose each had its own advantage and disadvantage. Aim: To evaluate using of double teostrut graft for controlling of tip projection. Patients and Methods: A total number of 170 patients were subjected to primary and secondary rhino plaster between January 2020 to January 2023. Those patients had double Teostrut banner graft for support of their nasal tip and maintaining tip projection after operation. Results: The follow period was ranging between 6-12 months. The shape of the nose was evaluating by patents vernal analogues scale. The average score for patients satisfaction wa

Background. Material tribology has widely expanded in scope and depth and is extended from the mechanical field to the biomedical field. The present study aimed to characterize the nanocoating of highly pure (99.9%) niobium (Nb), tantalum (Ta), and vanadium (V) deposited on 316L stainless steel (SS) substrates which considered the most widely used alloys in the manufacturing of SS orthodontic components. To date, the coating of SS orthodontic archwires with Nb, Ta, and V using a plasma sputtering method has never been reported. Nanodeposition was performed using a DC plasma sputtering system with three different sputtering times (1, 2, and 3 hours). Results. Structural and elemental analyses were conducted on the deposited coating

Several azo dyes were synthesized through coupling reaetion of some substituted phenols and B.naphthol with diazonium salt of 2- amino-1,3-4- thiadiazol -5- thiol. All the synthesized compounds during this work were characterized using some speetral data (F.TIRand UV)andM.P . 2-[4 --Hydroxy napthyl-azo ] -1,3,4-Thiadiazol -5-Thiol • 2- [2-- hydroxy –4- NO2 – phenyl- azo]- 1,3,4 - Thiadiazol –5-Thiol. • 2- [3--Amino-4-Hydroxy phenyl –azo]-1,3,4 - Thiadiazol –5-Thiol. . • 2-[2--Amino-4-Hydroxy phenyl -azo]-1,3,4 - Thiadiazol –5-Thiol . • 2- [3--Amino-6- Hydroxy phenyl -azo]-1,3,4 - Thiadiazol –5-Thiol. • 2-[2-- Hydroxy- 5 – chloro – Pheny - azo]- 1,3,4 - Thiadiazol –5-Thiol . • 2- [4-- Hydroxy phenyl -azo] -1,

This work included synthesis of several new polymers of polyacryloyl chloride in two steps . The first step the included the reaction of N-( sub. or un sub. benzoyl and sub. or un sub. acetyl ) amidyl sub. 2,6- diamino -4-methyl-1,3,5-triazine (1-5) by condensation of many substituted acid chlorides with 2,6- diamino -4-methyl-1,3,5-triazine . While the second step included the reaction of polyacryloyl chloride with the produced compounds (1-5) in step (1) in the presence amount triethyl amine (Et3N) to obtain new polyimides (6-10). The prepared compounds were characterized by UV. , FT-IR, and some of them by 1H-NMR and 13C- NMR spectroscopy.

The interlaminar fracture toughness of polymer blends reinforced by glass fiber has
been investigated. Epoxy (EP), unsaturated polyester(UPE), polystyrene (PS),
polyurethane (PU) and their blends with different ratios (10%PS/90%EP),
(20%PS/80%EP), (20%PU/80%EP) and (20%PU/80%UPE) were chosen as a matrices A
sheet of composites were prepared using hand lay -up method, these sheet were cut as the
double cantilever beam (DCB) specimen to determine interlaminar fracture toughness of
these composites .Its found that, blending of EP,UPE with 20% of PU will improve the
interlaminar fracture toughness ,but the adding of 10% PS, 20%PS to EP will decrease
the interlaminar toughness of these composites.