Nanocrystalline copper sulphide (Cu2-xS) powders were synthesized by chemical precipitation from their aqueous solutions composed of different molar ratio of copper sulfate dehydrate (CuSO4.5H2O) and thiorea (NH2)2CS as source of Cu+2, S-2 ions respectively, and sodium ethylene diamine tetra acetic acid dehydrate (EDTA) as a complex agent. The compositions, morphological and structural properties of the nanopowders were characterized by energy dispersive spectroscopy (EDS), scanning electron microscope (SEM), and X-ray diffraction (XRD), respectively. The compositional results showed that the copper content was high and the Sulfur content was low for both CuS and Cu2S nanopowders. SEM images shows that all products consist of aggregate o

Activated carbon loading with metals oxides is new adsorbents and catalyst, which seem very promising for desulfurization process. The present study deals with the preparation of three metals oxides loaded on activated carbon (AC). The tri composite of ZnO/NiO/CoO/AC was characterized by X-Ray Diffraction (XRD), X-Ray florescence (XRF), N₂ adsorption for BET surface area, pore volume and Atomic Force Microscopy (AFM). The effect of calcination temperature is investigated. The best calcination temperature is 250^oC based on the presence of phase, low weight loss and keep at high surface area. The surface area and pore volume of prepared tri composite are 932.97m²/g and 0.6031cm³/g respec

Phenol condensed with β-keto esters via Pechmann condensation to form derivatives of Coumarin in various reaction conditions by two ways. Present paper is comparative study of synthesis Coumarin with the yield of product , reaction time and reaction conditions.

This work includes two steps of synthesis, the first one is the synthesis of indole which was prepared according to literature of the reaction of phenyl hydrazine with acetaldehyde in glacial acetic acid afforded phenyl hydrazone of acetaldehyde , this product was fused with zinc chloride to give the indole.Reaction of cyclohexanone with phenyl hydrazine using the same procedure for the preparing giving 1,2,3,4-Tetrahydrocarbazole.Second step involved synthesis of a series of (17) of mannich bases derivatives of indole and 1,2,3,4-Tetrahydrocarbazle. Mannich reaction involves the condensation of aldehyde usually formaldehyde with different secondary amine and with compound containing an activated hydrogen.The reaction illustrated by the fo

A research include of synthesized five member ring, which has been synthesized by condensation of 2-(1-(4- hydroxyphenyl) ethylidene)hydrazine-1-carbothioamide[I] with α-chloro ethylacetate in sodium acetate (fused) to form ethyl 2-(4-(1-((4-oxo-2-thioxopyrrolidin-3-ylidene)hydrazono) ethyl)phenoxy)acetate [II]. After that reacted [II]with hydrazine hydrate to resulting compound [III]. Compound [III] was refluxed with 4-aminobenzoicacid in excess of phosphorus oxy chloride give compound [IV],the later compound [IV] interact with acetyl acetone or ethylacetoacetate give to pyrazole and pyrazoline derivatives[V],[VI]. While when reacted with different aromatic aldehydes and one ketone consistence Schiff base derivatives [VII]a-e . The FTIR a

The work include synthesis of nanocomposites (X / S / Ag) based on blend from Xanthan gum / sodium alginate polymers (X / S) with different loading of synthesized silver nanoparticales (0.01, 0.03 and 0.05 wt%) were added to the blend. The silver nanoparticles were prepared by reduction method and were characterized and analyzed using X-ray diffraction (XRD) and Atomic force microscope (AFM). XRD study showed the presence nanoparticle of silver with crystalline nature and face-centered cubic (FCC) structure and an average size of nanoparticles ranging from 32 to 37 nm. The surface study was performed using AFM which showed a fairly uniform shape to the nanocomposites and a spherical nature for the silver nanoparticles. The nanocomposite exh

The interest in calcium phosphates arises from the fact that bones contain a high percentage of mineralized calcium phosphate . In this study, pure and biocompatible hydroxyapatite (HAP) powder was successfully synthesized using hen’s egg shell as calcium source and phosphoric acid by precipitation method.The precipitate obtained was subjected to ripenning process for 24 hours, filtered, air dried, and calcined at temperatures of 400,800,900,and 1000 ºC.
X-Ray diffraction(XRD) technique was used to investigate the formation of HAP powder, XRD results revealed the HAP formation and also indicate no occurrence of secondary phases. Fourier Transform Infrared(FT-IR) spectrum shows the characterstic peaks for phosphate and hydroxyl grou

This work contain many steps starting from esterification of isophthalic acid to yield diester compound [I] which was converted to their acid hydrazide [II], then the later compound reacted with ethylacetoacetate to yield pyrazol-5-one compound [III]. Afterword added acetyl chloride to give the compound [IV], the reaction of this compound with theiosemicarbazide led to produce a new carbothioamide compound [V], which was reacted with ethyl chloro acetate to yield the thioxoimidazolidin compound [VI]. The condensation reactions of this compound with different substituted aldehyde give new alkene derivatives [VII] ad. The synthesized compounds were characterized by melting points, FT-IR, 1H-NMR and Mass spectroscopy.

Five N-substituted acrylamides were prepared by reaction of substituted aromatic primary amines with acryloyl chloride in the presence of triethyl amine. The synthesized acrylamides were allowed to introduce copolymerization reaction with three vinylic monomers including acrylonitrile, methyl acrylate and methyl methacrylate respectively to obtain eleven new copolymers having different physical properties which may used in different applications.

This work illustrates an enhanced visible light photocatalytic degradation of methyl orange dye (M.O.) by employing BiOI / BiOCl composites prepared under room temperature and without any organic precursors. Various experimental parameters have been studied, namely; composition of the composite, irradiation time and cell material. Composition D which implied 75% BiOI and 25% BiOCl has shown the highest bleaching of M.O. dye. This confirms the optimum photo-sensitization phenomenon for this composition in comparison to others. In the optimum photo-sensitized composite the electron of the conduction band reveals better reducing power and the hole of the valence band exhibits more oxidative power than those of pure BiOI electron and hole. Acco